Nb 3 Sn Cavity ERL1-4

Nb 3 Sn Cavity ERL1-4. History of ERL1-4 Nb 3 Sn coating, just HPR Test shows relatively flat Q vs E up to quench at ~13 MV/m, Q~1e10 5x HF rinse, HPR November test shows Q-slope 120 K Torture Test shows no degradation Remove coating with BCP Baseline test: good performance up to 20 MV/m

art
Télécharger la présentation

Nb 3 Sn Cavity ERL1-4

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Nb3Sn Cavity ERL1-4 • History of ERL1-4 • Nb3Sn coating, just HPR • Test shows relatively flat Q vs E up to quench at ~13 MV/m, Q~1e10 • 5x HF rinse, HPR • November test shows Q-slope • 120 K Torture • Test shows no degradation • Remove coating with BCP • Baseline test: good performance up to 20 MV/m • Recoat with same parameters • Test shows performance is repeatable

  2. Measuring DC Flux Penetration Field • Nick made a 1760-winding NbTi solenoid • Get cavity to a few MV/m, then apply DC field, watch Pt (or Pr) • When RF field drops, flux from DC field has penetrated to RF surface • Hall probe measures magnetic field

  3. T = 6.3 K Flux penetration

  4. Flux penetration as a function of T2 Lines with x-intercept matching Tc of Nb or Nb3Sn and y-intercepts fitted by eye Approximate Bsh of Nb with correction for field at hall probe

  5. From Nick’s thesis: Ratio of X’s gives magnetic field correction for hall probe