MEMS devices: How do we make them?

MEMS devices: How do we make them?. A mechanism. Gear chain Hinge Gear within a gear. Sandia MEMS. Basic MEMS materials Silicon and its derivatives, mostly. Micro-electronics heritage Si is a good semiconductor, properties can be tuned Si oxide is very robust

brucehopkins
Télécharger la présentation

MEMS devices: How do we make them?

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. MEMS devices: How do we make them? A mechanism Gear chain Hinge Gear within a gear Sandia MEMS

  2. Basic MEMS materials Silicon and its derivatives, mostly • Micro-electronics heritage • Si is a good semiconductor, properties can be tuned • Si oxide is very robust • Si nitride is a good electrical insulator

  3. Materials in MEMS Dominant: SEMICONDUCTORS (Silicon centric) MEMS technology borrows heavily from the Si micro-electronics industry The fabrication of MEMS devices relies on the processing of Silicon and silicon compounds (silicon oxide, nitride …) METALS: used in electrical contacts (Al,Cu), magnetic elements (Ni, NiFe) POLYMERS: used as sacrificial layers, for patterning (photoresist/polyimide)

  4. Making MEMS • Planar technology, • constructing components (MEMS & electronics) on initially flat wafers • > Wafer level processes • > Pattern transfer • Introduction to Micro-machining • - Wet and Dry etching • - Bulk and surface micro-machining • What kinds of materials are used in MEMS? • Semiconductors • Metals • Polymers

  5. Photolithography Light Light MASK MASK Deposit Metal Photoresist Silicon substrate Silicon substrate Positive photoresist Negative photoresist

  6. Deposit and remove materials precisely to • create desired patterns The photo-lithography process Positive Remove deposit and etch J. Judy, Smart Materials & structures, 10, 1115, 2001 Negative

  7. Surface micromachining How a cantilever is made: http://www.darpa.mil/mto/mems

  8. One can make devices as complex as one wishes using deposition and micromachining processes http://mems.sandia.gov/

  9. Any MEMS device is made from the processes of deposition and removal of material e.g. a state-of-the art MEMS electric motor www.cronos.com

  10. The History of MEMS Y.C.Tai, Caltech

  11. Bulk micromachining • Wet Chemical etching: Masking layer Bulk Si Bulk Si Isotropic Anisotropic

  12. Bulk micromachining • Dry etching • Ions: Reactive ion etching (RIE), focused ion beams (FIB) • Laser drilling: using high powered lasers (CO2/YAG) • Electron-beam machining: sequential slow

  13. Wet Etching: Isotropic • atomic layer by atomic layer removal possible • Isotropic etching:Hydrofluoric + nitric + acetic acids (HNA) Bulk Si Chemical reaction: Si + 6 HNO3+6 HF H2SiF6 + HNO2 + H2O + H2 Principle: HNO3 (Nitric acid) oxidizes Si  SiOx HF (Hydrofluoric Acid) dissolves SiOx Acetic acid/water is a diluent

  14. Z Y X Anisotropic etching, due to the Silicon crystal structure - Diamond cubic crystal structure Different planes of atoms in a Silicon crystal have different densities of atoms (111) (100) (110) (111) This implies preferential/anisotropic etching is possible

  15. fiber Applications: Anisotropic Etching Inkjet printers Aligning fibers

  16. Wet etching: Anisotropic Etching (100) (110) (100) (111) Bulk Si Bulk Si Chemical recipes: EDP (Ethylene diamine, pyrocatechol, water) [NH2(CH2)2NH2, C6H4(OH)2] - low SiO2 etch rate, - carcinogenic KOH (Potassium hydroxide), - high <110> / <111> and <100>/ <111> selectivity ( ~ 500) - high SiO2 etching TMAH (Tetra-methyl Ammonium Hydroxide: (CH3)4NOH) - Low SiO2 and SixNy etch rate - smaller <100> / <111> selectivity

  17. Comparison of wet chemical etches Reference: “Etch rates for Micromachining Processing” - K. R. Williams, IEEE Journal of MEMS, vol. 5, page 256, 1996.

  18. Sensors based on (100) preferential etching Honeywell sensor

  19. Micro-fluidic channels based on (110) preferential etching

  20. MEMS Process Sequence Slide courtesy: Al Pisano

  21. Surface micromachining How a cantilever is made: http://www.darpa.mil/mto/mems Sacrificial material: Silicon oxide Structural material: polycrystalline Si (poly-Si) Isolating material (electrical/thermal):Silicon Nitride

  22. MEMS Processing Oxidation of Silicon  Silicon Oxide (Sacrificial material) Dry Oxidation: flowing pure oxygen over Si @ 850 – 1100 oC (thin oxides 1- 100 nm, high quality of oxide) Uses the Deal-Grove Model: xoxide = (BDGt)1/2 Temperature (oC)BDG (mm2/ hour) 920 0.0049 1000 0.0117 1100 0.027

  23. MEMS Processing Oxidation of Silicon  Silicon Oxide (Sacrificial material) Wet Oxidation: uses steam for thicker oxides (100nm – 1.5 mm, lower quality) Temperature (oC)BDG (mm2/ hour) 920 0.203 1000 0.287 1100 0.510 Higher thicknesses of oxide: CVD or high pressure steam oxidation

  24. Silicon oxide deposition SiH4 + O2 LTO: Low Temperature Oxidation process • For deposition at lower temperatures, use • Low Pressure Chemical Vapor Deposition (LPCVD) • SiH4 + O2 SiO2 + 2H2 : 450 oC • Other advantages: • Can dope Silicon oxide to create PSG (phospho-silicate glass) • SiH4 + 7/2 O2 + 2 PH3 SiO2:P + 5 H2O : 700 oC • PSG: higher etch rate, flows easier (better topography) 425-450 oC 0.2-0.4 Torr

  25. Case study: Poly-silicon growth SiH4 Amorphous film 570 oC Crystalline film 620 oC • by Low Pressure Chemical Vapor Deposition • T: 580-650 oC, P: 0.1-0.4 Torr • Effect of temperature • Amorphous  Crystalline: 570 oC • Equi-axed grains: 600 oC • Columnar grains: 625 oC • (110) crystal orientation: 600 – 650 oC • (100) crystal orientation: 650 – 700 oC Kamins,T. 1998 Poly-Si for ICs and diplays, 1998

  26. Poly-silicon growth • Temperature has to be very accurately controlled • as grains grow with temperature, increasing surface • roughness, causing loss of pattern resolution and stresses in • MEMS • Mechanisms of grain growth: • Strain induced growth • - Minimize strain energy due to mechanical deformation, doping … • - Grain growth  time • 2. Grain boundary growth • - To reduce surface energy (and grain boundary area) • - Grain growth  (time)1/2 • 3. Impurity drag • - Can accelerate/prevent grain boundary movement • - Grain growth  (time)1/3

  27. Grains control properties • Mechanical properties • Stress state:Residual compressive stress (500MPa) • - Amorphous/columnar grained structures: Compressive stress • - Equiaxed grained structures: Tensile stress • Thick films have less stress than thinner films • ANNEALING CAN REDUCE STRESSES BY A • FACTOR OF 10-100 • Thermal and electrical properties • Grain boundaries are a barrier for electrons • e.g. thermal conductivity could be 5-10 times lower (0.2 W/cm-K) • Optical properties • Rough surfaces!

  28. Silicon Nitride SiH2Cl2 + NH3 (for electrical and thermal isolation of devices) r: 1016W cm, Ebreakdown: 107 kV/cm • Is also used for encapsulation and packaging • Used as an etch mask, resistant to chemical attack • High mechanical strength (260-330 GPa) for SixNy, provides structural integrity (membranes in pressure sensors) • Deposited by LPCVD or Plasma –enhanced CVD (PECVD) LPCVD: Less defective Silicon Nitride films PECVD: Stress-free Silicon Nitride films x SiH2Cl2 + y NH3 SixNy + HCl + 3 H2 700 - 900 oC 0.2-0.5 Torr

  29. Depositing materialsPVD (Physical vapor deposition) • Sputtering: DC (conducting films: Silicon nitride) RF (Insulating films: Silicon oxide) http://web.kth.se/fakulteter/TFY/cmp/research/sputtering/sputtering.html

  30. Depositing materialsPVD (Physical vapor deposition) • Evaporation (electron-beam/thermal) Commercial electron-beam evaporator (ITL, UCSD)

  31. Electroplating Courtesy: Jack Judy • Issues: • Micro-void formation • Roughness on top surfaces • Uneven deposition speeds • Used extensively for LIGA processing e.g. can be used to form porous Silicon, used for sensors due to the large surface to volume ratio

  32. Depositing materials –contd.- • Spin-on (sol-gel) • e.g. Spin-on-Glass (SOG) used as a sacrificial molding material, processing can be done at low temperatures Dropper Si wafer

  33. Surface micromachining - Technique and issues - Dry etching (DRIE) Other MEMS fabrication techniques - Micro-molding - LIGA Other materials in MEMS - SiC, diamond, piezo-electrics, magnetic materials, shape memory alloys … MEMS foundry processes - How to make a micro-motor

  34. Surface micromachining Carving of layers put down sequentially on the substrate by using selective etching of sacrificial thin films to form free-standing/completely released thin-film microstructures http://www.darpa.mil/mto/mems HF can etch Silicon oxide but does not affect Silicon Release step crucial

  35. Release of MEMS structures • A difficult step, due to surface tension forces: Surface Tension forces are greater than gravitational forces ( L) ( L)3

  36. Cantilever Si substrate Release of MEMS structures • To overcome this problem: • Use of alcohols/ethers, which sublimate, at release step • Surface texturing • Supercritical CO2 drying: avoids the liquid phase 35oC, 1100 psi

  37. A comparison of conventional vs. supercritical drying