Ethox Chemical, LLC

Ethox Chemical, LLC. Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3). Product Assurance Services, Inc. PAS Job# 7195. JUN 2008. Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3) Hall Apparent Density and Flow Rate.

cianna
Télécharger la présentation

Ethox Chemical, LLC

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Ethox Chemical, LLC Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3) Product Assurance Services, Inc. PAS Job# 7195 JUN 2008

  2. Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3) Hall Apparent Density and Flow Rate

  3. Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3)Green Properties

  4. Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3)Green Properties

  5. Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3)Sintered Properties Sintered @ 2050 F 95%N2/5% H2 3.5 in./min.

  6. Evaluation of Ethox Blended Lubes versus Standard EBS in MPIF F-0000 (Test #3)Conclusions • Samples 8-1, 8-4, 8-6, 8-8, 8-10 had comparable properties to EBS. • 8-1 and 8-4 were unacceptable for sintering because of Low TRS strength. • 8-6, 8-8, 8-10 showed similar hardness and density, but had higher sintered Dimensional Change, Lower TRS, and some evidence of residue on the surface. Based on the similarity of results between these three samples, they appear to be similar in composition. • I think we should focus on these three samples, and try to figure out where the delubing issue is coming from. We may solve the other problems once we determine why we are having residue.