An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Hydrothermal synthesis of ZSM-5 membranes By MeilingJi

  2. Outlinecontent 1. In situ growth 2. Secondary growth 3. Work plan

  3. 1. In situ growth

  4. 165℃，4 h crystallization conditions Time & Temperature 165℃，12 h 185℃，4 h 165℃，24 h 185℃，24 h

  5. substrate 165℃，12 h 165℃，12 h 165℃，24 h 165℃，24 h

  6. Concentration nucleation C1 crystal growth t1 t2 t4 t3 24 h Crystallization Time

  7. surface roughness 020

  8. 2. Secondary growth

  9. Reproducity of secondary growth 332/051 Random orientation good intergrowth 101 151/303 Random orientation Random orientation 200/020 133 Random orientation Thickness ~1.8μm

  10. Preparation of seed 0.36TPAOH:1TEOS:58H2O:4EtOH aging Ultrasonication 15 min Crystallization 98℃，48 h Centrifugation 10000 r/min for 10 min weighing • The amount of seed can be easily controlled. • The obtained seed can be stored in a desiccator for later use.

  11. Impact of seed concentration 0mg/mL 2mg/mL 5mg/mL

  12. Seed coated Random orientation 25SiO2：9TPAOH：1450H2O: 100EtOH 100 ℃ ，48 h seed obtained after centrifugation 5 mg/mL in EtOH A gel layer formed Discrete zeolite particles PH = 12.49 PH = 6.16

  13. JH Koegler, H Bekkum, et al., Zeolites,1997,19(4): 262-269. • Effect of Al • It facilitate the formation of the gel layer on the support. • It retard zeolitization in this gel layer. Re Lai, Yushan Yan, George R. Gavalas, Micropor Mesopor Mater, 2000,37(1-2):9-19

  14. agglomerate unstable Adv. Funct. Mater. 2008, 18, 952–958 stable good Zeta potential(mv) Si/Al Figure1. Zeta potential vs. PH for zeolite silicalite-1 crystals in aqueous suspension.

  15. 5mg/mL 2mg/mL 100%（101） 21.9%（051） 0mg/mL 100%（101） 56.8%（051） 100%（101） 59.0%（051） PDF：#44-0003 ZSM-5:Al2O354SiO2

  16. CPO definition Characteristic planes and growing axis for MFI type zeolite I:intensity of a peak P:powder reference S:film sample I:intensity of a peak P:powder reference S:film sample [1] Microporous and Mesoporous Materials, 1999. 28(1): 185-194 [2] Journal of Materials Chemistry, 1998, 8(10): 2217-2221. [3]Microporous and Mesoporous Materials, 2009,123(1-3):113-112 [4]Microporous and Mesoporous Materials, 2008, 115(1-2): 113-122. Fig.1. Typical shape of MFI-typ zeolite crystals

  17. 5mg/mL 2mg/mL 100%（101） 21.9%（051） 0mg/mL 100%（101） 56.8%（051） 100%（101） 59.0%（051） PDF：#44-0003 ZSM-5:Al2O354SiO2

  18. 3. Work plan

  19. Work plan +++++++ +++++++ +++++++

  20. Q&A Thanks for your time！