1 / 31

Thermodynamics and thermophysical properties of liquid Fe-Cr alloys

Rada Novakovic National Research Council (CNR–IENI) Genoa, Italy. Thermodynamics and thermophysical properties of liquid Fe-Cr alloys. Mixing behaviour of liquid binary alloys: energetic & structural factors. Observable indicators: Phase diagrams.

davin
Télécharger la présentation

Thermodynamics and thermophysical properties of liquid Fe-Cr alloys

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Rada Novakovic National Research Council (CNR–IENI) Genoa, Italy Thermodynamics and thermophysical properties of liquid Fe-Cr alloys

  2. Mixing behaviour of liquid binary alloys: energetic & structural factors • Observable indicators: • Phase diagrams. • Empirical factors– physical, chemical & structural properties of alloy constituents (liquid metals), melting points, volume, first shell coordination, radius size, valence difference, electronegativity difference... • Thermodynamic functions– heat capacity, enthalpy, activity, excess Gibbs energy. • Microscopic functions– concentration fluctuations in the long wavelength limit & CSRO (Warren-Cowley short range order) parameter. MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  3. What kind of input data are necessary for modelling? 1.Thermodynamic data on mixing: heat capacity; enthalpy; entropy; Gibbs energies (integral & excess). partial quantities: activities (or chem. potentials). 2. Phase diagram information type of alloy system: segregating or compound forming 3.Thermophysical data: molar volume, surface tension, viscosity of pure components. 4. Structural data: coordination number; neutron diffraction data to be transformed into the microscopic functions 5. Experimental data on Thermo-Physical properties of alloys: for a comparison with theoretical results MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  4. The Fe-Cr system MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  5. Thermodynamic data of the Fe-Cr liquid phase [11Xiong] An improved thermodynamic modeling of the Fe–Cr system down to zero kelvin coupled with key experiments [86Mas] The Fe-Cr phase diagram [76Hul;81AB;82HS;87AS] previous assessments of the p.d. [93BLee] The reassessment of the Fe-Cr phase diagram [93BLee]T=1873K:The optimised term of the excess Gibbs free energy; the enthalpy of mixing [84Bat]; the activities [80Mar;69Fru;69Gil;98Zai]. [06Vre] The presence of interm. - phase [06Ter] The melting, the enthalpy of mixing, thermal diffusivity - by atomic simulations Comment: The Cr-Fe phase diagram can be considered as COMPLETE(although some measurements in the liquid phase are necessary). MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  6. Results of calculations - phase energ. favoured ( AB )  Weak influence on the energetics of the Fe-Cr liquid phase. MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  7. Results of calculations MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  8. SURFACE TENSION • SURFACE TENSION MODELS • Binary systems • Ternary systems • Geometric models • EXAMPLES: Fe-Cr, Al-Nb-Ti

  9. Surface properties of liquid binary alloys: surface segregation & surface tension Butler(1932) published the paper proposing his well known equation: (i = A, B),that gives the relation between the surface tension and thermodynamics of liquids in which the bulk and surface phases are in equilibrium. MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  10. Subtracting Butler’s equ. for both components, and combining with and taking into account the bulk (surface) phase activity coefficients obtained byFowler_Guggenheim methodas and the  and xscan be calculated. The surface tension can be calculated inserting xs into the Butler’s equation. MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  11. * Models based on Butler’s equation - Regular solution - Subregular solution - “Central” atom - Compound Formation Model (CFM) - Self Aggregating Model (SAM) An interface Liquid / Gas : &*Probabilistic Models Singh et al. Monolayer or Multilayers Surface tension calculations of binary systems

  12. * Models based on Butler’s equation - Regular solution - Subregular solution - “Central” Atom - Compound Formation Model (CFM) - Self Aggregating Model (SAM) An interface Liquid / Gas : & *Geometric Models (from thermodynamic calculations of mixing properties in the bulk) SYMMETRIC - Kohler; Colinet; Muggianu ASYMMETRIC - Toop; Bonnier; Hillert; GENERALIZED - Chou Monolayer Surface tension calculations of ternary systems

  13. Geometric models Kohler Toop Chou

  14. Iso-surface tension lines of liquid Al-Ti-Nb alloys calculated by the Butler equation for the regular solution model at 2073 K. The square symbol represents the composition location of the Ti46Al46Nb8 (at.%) in the Gibbs triangle and the corresponding surface tension calculated value MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  15. Surface tension reference data of Cr MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  16. Surface tension reference data of Fe MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  17. Results of calculations MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  18. Results of calculations MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  19. Results of calculations MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  20. Microscopic functions (B-T) & Thermodynamics For ideal solution the SCC(0) becomes The CSRO parameter and SCC(0) are related to each other by where Z is the coordination number. MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  21. Microscopic functions & local arrangements of atoms in the melt SCC(0)and CSRO parameter indicate chemical order & segregation (phase separation): SCC(0) – the nature of mixing CSRO parameter – thedegree of order Criteria for mixing behaviour 1. SCC(0) < SCC(0, id) presence of chemical order SCC(0) > SCC(0, id) segregation 2. -1 < CSRO < 0 ordering in the melt CSRO =-1complete ordering 0 < CSRO < 1 segregation CSRO =1phase separation MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  22. Results of calculations MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  23. The interdiffusion coefficient (Dm) can be given in terms of the SCC(0)by For “ideal” alloys, SCC(0)= SCC(0,id)= cAcB, then and finally combining the last two eqs. it is obtained, The criteria for mixing behaviour: SCC(0) > SCC (0, id)segregation Dm < Did SCC(0) < SCC (0, id)presence of chem. order Dm > Did MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  24. Results of calculations MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  25. Viscosity Viscosity()of liquid alloys-the atomic level structure and interactions. The composition dependenceofof liquid alloys in respect to the linear low (ideal mixture): a linear variation (simple liquids, e.g.Ag-Au, Sn-Pb, Bi-Pb) positive deviations (compound forming alloys, H <<0) negativedeviations (segregating alloys, H >>0). Sometimes the viscosity of binary liquid alloys exhibits “strange” behaviour (Bi-Ga, Bi-Cu, Ga-Hg..), i.e. the same behaviour as their thermodynamic functions (according to the theory should be opposite!)

  26. In the framework of the QLT the viscosity, , is related to theSCC(0)and diffusionby: For a thermodynamically ideal mixture,SCC(0)=SCC(0,id)=c(1-c) previous equ. becomes: with and for the viscosity of pure components (Stokes-Einstein) Assuming 1 = 2 = =1, it is obtainedthe Stokes-Einstein type relation for diffusion and viscosity:

  27. Recently,we proposed the following viscosity equation: where miand i (i=A,B) are parameters that can be calculated from the experimental data.

  28. Results of calculationsviscosity of some binary systems

  29. Modelling of the interfacial properties of molten Pb / FeCr substrate system: Application of the Phase Field Method • Study of thermodynamics and thermophysical properties of the Fe-Cr, Fe-O, Pb-O, Fe-Cr-Pb, Fe-Cr-Pb-O systems • Model formulation and implementation • Collection of input parameters for the Pb-Fe and Pb-Cr systems • Simulations, analysis of model parameters and validation with experimental micrographs for the Pb-Fe and Pb-Cr systems • Extension of the model and implementation towards ternary system Pb-Fe-Cr • Collection of input parameters for the Pb-Fe-Cr system • Simulations for the interface between molten Pb / FeCr - substrate system • Comparison with experimental micrographs for Pb / Fe-Cr diffusion couples MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy

  30. Thank you for your attention! MATGEN-IV.3 summer school on “Materials for Generation IV reactors: Fundamentals, ongoing research and open questions”,September 19-23, 2011, Lerici (SP), Italy