An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. COMPLEX MULTI-SURFACE COMPOSITE RESTORATIONS DR. PETER WALFORD

  2. EXCESSIVE TIME OPEN/BROKEN CONTACT MATRIX ISSUES GINGIVAL RE-DECAY COMMON PROBLEMS

  3. PULP - SENSITIVITY OR DEATH PITS,VOIDS,BUBBLES UNATTRACTIVE ESTHETICS ISOLATION CHALLENGES INSTRUMENTATION FOR LONG CROWNS PREPARATION DESIGN? MORE PROBLEMS….

  4. WWW.PETERWALFORDDENTISTRY.COM USERNAME cardp2012 PASSWORD halifax

  5. LINKS ON WEBSITE • FOLLOW ((CARDP)) ON HOME PAGE TO FIND APPROPRIATE LINKS WITHIN WEBSITE

  6. HEATED RESINS FAST CURE LIGHTS DELEGATION-the future of the restorative hygienist position BULK FILL?- a flawed concept TIME SAVERS

  7. CALSET COMPOSITE HEATER • BEST SETTING: 54 DEGREES • MULTIPLE DESIGNS FOR COMPULES OR SYRINGES; SYRINGE IS MOST VERSATILE MODEL • DECREASES CURE TIME BY UP TO 75% • INCREASES PHOTOCONVERSION, HARDNESS • THINS OXYGEN-INHIBITED LAYER • FOR EVIDENCE SEE WWW.ADDENT.COM

  8. DETERMINING CURE TIME FOR HEATED RESINS

  9. CHAIRSIDE CURE TESTING • 2MM DISC (DENMAT) • 3.5 MM DISC (HARDWARE TAP WASHER) • DETERMINE CURE BY SCRATCH TEST • CRUDE BUT ONE STEP UP FROM BLIND FAITH • HAVE CDA COMPILE A TABLE- A FEW SURPRISES WILL BE FOUND • DARK SHADES AND FLOWABLES!! TAKE LONGER • SOME VERY LIGHT SHADES MAY ALSO TAKE LONGER DUE TO MISMATCH BETWEEN LIGHT SPECTRUM AND PHOTOINITIATOR

  10. PREVENTING OPEN/BROKEN CONTACT • ANATOMICALLLY CONTOURED CIRCUMFERENTIAL MATRIX • CONTACT FORMERS • CUSTOM WEDGING • RESIN WITH SUITABLE FLEXURAL STRENGTH • ADEQUATE CURING

  11. FLEXURAL STRENGTH

  12. THE IMPORTANCE OF FLEXURAL STRENGTH • THOSE PORTIONS OF THE RESTORATION EXTENDING BEYOND THE ROOT BASE MUST TRANSFER LOADS ON A DIAGONAL PATH TO THE RETORATION • THIS CREATES A TWISTING SHEAR FORCE WITHIN THE RESIN; A “ FLEXURAL LOAD” • BEST PARAMETER TO INDICATE THIS QUALITY IS FLEXURAL STRENGTH • INADEQUATE FLEXURAL STRENGTH WILL LEAD TO BREAKAGE OF MARGINAL RIDGES EVEN IF EVERYTHING ELSE IN THE RESTOATIVE SUITE IS PERFECT • SEE WEBSITE FOR TABLE “COMPOSITE PARAMETER SPREADSHEET”

  13. BEST RESINS FOR LARGE RESTORATIONS: TOP QUARTILE • GRANDIOSO (VOCO) 181 MPa • VENUS DIAMOND (HEREAUS KULZER)169MPa • FILTEK SUPREME ULTRA (3M Espe) 162MPa

  14. VENUSDIAMOND

  15. ENSURING ADEQUATE CURE • UNDERCURED RESIN IS A PREVALENT CAUSE FOR FRACTURED RESTORATIONS • SEE WEBSITE ((CURING COMPOSITES)) • WIDE-SPECTRUM HIGH INTENSITY LIGHTS ARE BEST • BEST RECOMMENDATION: SAPPHIRE PLASMA ARC 5 SEC CURE • VALO LED SEE CLINICIAN’S REPORT OCTOBER 2010

  16. ref

  17. CRAOCTOBER 2010

  18. CURING DEEP BOXES • STUDY CLUB RULE; BEYOND 6MM DEPTH, USE A DUAL CURE SYSTEM UNTIL BOX DEPTH RESTORED TO 6MM • DUAL-CURE ADHESIVE PHOTOBOND OR ALL BOND 3 • DUAL CURE FLOWABLE, STARFILL 2B

  19. STARFILL 2BDANVILLE DENTAL • 141MPa • HYBRID • S/C IN 2.5 MINS • SEVERAL CONVENIENT AUTOMIX TIPS

  20. RECOMMENDED JOURNALS FOR COMPOSITE INFORMATION • REALITY • CLINICIAN’S REPORT • THE DENTAL ADVISOR

  21. ref

  22. RESIDUAL CARIES, BIOFILM CONTAMINATION • CARIES IS A NON-STRUCTURAL SUBSTRATE; DOESN’T BOND, HAS NO RESISTANCE FORM • BIOFILM IS AN INVISIBLE ANDUNIVERALLY PRESENT CONTAMINANT TO ADHESION • BOTH CONTRIBUTE TO PREMATURE FAILURE OF RESINS • CAN BE CONTROLLED WITH THE ROUTINE USE OF CARIES DETECTOR

  23. BENEFITS OF CARIES DETECTOR • CONFIRMS COMPLETE REMOVAL (CARIES IS NOT STRUCTURAL!!) • DISCLOSES PLAQUE • REVEALS FLASH IN FINISHING

  24. DEEP CARIES • ANGELUS MTA 10 MINUTE SET • DOVGAN PLACEMENT INSTRUMENT • FO FULL PROTOCOL SEE CHAPTER IN MODXYZ

  25. ELIMINATING AND REPAIRING PLACEMENT FLAWS • ALCOHOL AS AN INSTRUMENT LUBRICANT IN PLACEMENT • AVOIDS WEAKENING INCREMENT INTERFACES WITH ”PLACEMENT RESIN” • LIGHT SHIELD TO PERMIT UNHURRIED COHESIVE PLACEMENT-NO PREMATURE CURE • Z-PRIME PLUS (BISCO) AS AN EFFECTIVE PRIMER FOR REPAIRS –BONDS TO SILICA 18MPa, ZIRCONIM 22MPa, AND RESIN • HF ETCH OPTIMIZES ADHESION TO SILICA • USE CONVENTIONAL THIN (5-7 MICRON) GEN IV OR V ADHESIVE AFTER Z-PRIME, CURE BOND, RESTORE

  26. PRACTICON

  27. ref

  28. REPAIRING FLAWS IN RESTORATIONS WITH Z-PRIME PLUS • OPEN DEFECT UP INTO A SMALL SAUCER • ETCH WITH PHOSPHORIC ACID IF ENAMEL MARGINS ARE INVOLVED • HF ETCH IF IS A SILICA-BASED FILLER PARTICLE (MOST RESINS ARE) • RINSE, DRY, Z-PRIME (BISCO),BLOW OFF SOLVENT, ADD PHOTOBOND, BLOW OFF EXCESS, CURE • FILL SMALL DEFECTS WITIH MATCHING FLOWABLE WITH AN EXPLORER TIP, CURE • FILL LARGE DEFECTS WITH RESTORING RESIN, CURE • FINISH WITH 7902,POLISH WITH WET SHOFU FG BROWNIE POINT, SLOW RPMS.

  29. WEBSITE LINK ON REPAIRS • http://www.peterwalforddentistry.com/tiki/tiki-index.php?page=Repairing%20Bubbles%2CVoids%2C%20and%20Flaws