Paul M. Grant Visiting Scholar, Stanford (2005-2008) IBM Research Staff Member Emeritus

Does the Hold the Key to Room Temperature Superconductivity?. http://www.w2agz.com/rtsc07.htm. The Third International Conference on Quantum, Nano and Micro Technologies ICQNM 2009 February 1-7, 2009 - Cancun, Mexico. Quasiperiodic Quasi-One-Dimensional Metallic Nano-Structures.

fuller-head
Télécharger la présentation

Paul M. Grant Visiting Scholar, Stanford (2005-2008) IBM Research Staff Member Emeritus

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Does the Hold the Key to Room Temperature Superconductivity? http://www.w2agz.com/rtsc07.htm The Third International Conference on Quantum, Nano and Micro Technologies ICQNM 2009 February 1-7, 2009 - Cancun, Mexico Quasiperiodic Quasi-One-Dimensional Metallic Nano-Structures Paul M. Grant Visiting Scholar, Stanford (2005-2008) IBM Research Staff Member Emeritus EPRI Science Fellow (Retired) Principal, W2AGZ Technologies

  2. NanoConcept What novel atomic/molecular arrangement might give rise to higher temperature superconductivity >> 165 K?

  3. NanoBlueprint • Model its expected physical properties using Density Functional Theory. • DFT is a widely used tool in the pharmaceutical, semiconductor, metallurgical and chemical industries. • Gives very reliable results for ground state properties for a wide variety of materials, including strongly correlated, and the low lying quasiparticle spectrum for many as well. • This approach opens a new method for the prediction and discovery of novel materials through numerical analysis of “proxy structures.”

  4. NanoConstruct “Eigler Derricks”

  5. Models of Electrical Conductivity1900 One Idea: ( ( ( R ( ( ( Just Goes to Zero! ( ( ( • • e- ( ( e- ( T

  6. Models of Electrical Conductivity1910 The Most Popular: e- R Freezes Out! T

  7. 1911: A Big Surprise! Thus the mercury at 4.2 K has entered a new state, which, owing to its particular electrical properties, can be called the state of superconductivity H. Kamerlingh-Onnes (1911)

  8. Physics of Superconductivity(Carriers Pair Off) • + + e- + + • e-

  9. “Bardeen-Cooper-Schrieffer” • Where • = Debye Temperature (~ 275 K) • = Electron-Phonon Coupling (~ 0.28) * = Electron-Electron Repulsion (~ 0.1) a = “Gap Parameter, ~ 1-3” Tc = Critical Temperature ( 9.5 K “Nb”)

  10. Electron-Phonon Coupling a la Migdal-Eliashberg-McMillan(plus Allen & Dynes) First compute this via DFT… Then this… Quantum-Espresso (Democritos-ISSA-CNR) http://www.pwscf.org Grazie!

  11. “3-D”AluminumTC = 1.15 K

  12. 1986: Another Big Surprise! 164 K Hg-1223 High-TC La-214 Bednorz and Mueller IBM Zuerich, 1986 200 150 Temperature, TC (K) 100 50 Low-TC Hg V3Si 0 1900 1920 1940 1960 1980 2000 Year

  13. - - + + - - + + - - + + Diethyl-cyanine iodide Little, 1963

  14. “Bill Little’s BCS” • Where • = Exciton Characteristic Temperature (~ 22,000 K) • = Fermion-Boson Coupling Constant (~ 0.2) * = Fermion-Fermion Repulsion (?) a = “Gap Parameter, ~ 1-3” Tc = Critical Temperature, ~ 300 K

  15. μ* Allender-Bray-Bardeen (1973)

  16. Davis – Gutfreund – Little (1975)

  17. Al Chain Supercell:c* = c, a*, b* ~ 3 x c*

  18. Al Chain Supercell:c* = c, a*, b* = >10 x a • Periodic Al chain unstable – dimerizes! • Fermi surface is totally gapped! • However… …could still give a BCS HTSC if hω >>  !

  19. “Not So Famous Danish Kid Brother” Harald Bohr Silver Medal, Danish Football Team, 1908 Olympic Games

  20. Almost Periodic Functions “Electronic Structure of Disordered Solids and Almost Periodic Functions,” P. M. Grant, BAPS 18, 333 (1973, San Diego)

  21. APF “Band Structure” “Electronic Structure of Disordered Solids and Almost Periodic Functions,” P. M. Grant, BAPS 18, 333 (1973, San Diego)

  22. Fibonacci Chains “Monte-Carlo Simulation of Fermions on Quasiperiodic Chains,” P. M. Grant, BAPS March Meeting (1992, Indianapolis)

  23. Al Fibonacci Chain Supercell:c* = G3(2.862|4.058), a*, b* ~ 2 x c*

  24. 64 = 65

  25. Fast Forward: 2028