An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. A COMMON R&D ON THE HIGH GRADIENT Nb CAVITIES Fabien Éozénou WORKSHOP FJPPL 2007 May 10th 2007 - Fabien Eozénou -

  2. OUTLINE • CONTEXT: ILC Why are Electropolishing and Baking crucial. • MAJOR ISSUES • LAST RESULTS PRESENTED AT TTC by KEK • LAST RESULTS PRESENTED AT TTC by SACLAY • COMMON R&D PROGRAM - Fabien Eozénou -

  3. CONTEXT - Fabien Eozénou -

  4. R&D NECESSARY FOR ILC • International Linear Collider 16000 Superconductive Nb cavities > 35 MV/m • Surface treatments crucial for high gradients • R&D necessary (Ex GDE S0 program for reproducible gradients) ‘Standard preparation’ : Barrel Polishing + EP + Anneal + Final EP + HPR + Rinse + Baking EP = Electro-Polishing HPR = High Pressure Rinsing - Fabien Eozénou -

  5. R&D CRUCIAL ON TWO DIFFERENT TOPICS • Electropolishing • Baking Electropolishing was a breakthrough to achieve high gradients By H.Padamsee Baking: Cavity is baked under vacuum to remove high field Q-Slope whose origin remains mysterious ‘Standard’ parameters: 120°C: 48h - Fabien Eozénou -

  6. WHAT IS ELECTROPOLISHING? (EP) • Process - Nb polished internally with an electrolyte (concentrated H2SO4 - HF mixture) under voltage - Cavity = Anode & Cathode is an Al pipe inside the cavity • Chemical reactions - Anode: Niobium oxidation 2 Nb + 5 H2O  Nb2O5 + 10 H+ + 10 e- - Cathode: H2 generation 2 H+ + 2 e- H2 (Teflon net to prevent H contamination) - HF: dissolution of oxide Nb2O5 layer - H2SO4: forming of a viscous layer - Fabien Eozénou -

  7. MACROPOLISHING + MICROPOLISHING ELECTROLYTE Micropolishing smoothens irregularities < 1 µm Better RF performances due to smoother surface? - Fabien Eozénou -

  8. ELECTROPOLISHING AND BAKING SET-UP Single Cell Ichiro Cavity EP At KEK/ Nomura Plating Single Cell EP at Saclay Infra Red cavity baking in Clean Room at Saclay 9-Cell EP For STF at NP - Fabien Eozénou -

  9. MAJOR ISSUES • Achieve a better reproducibility for high gradients • Reduce impurities • Choose better rinsing procedures • Improve baking parameters • Better knowledge of acid quality - Fabien Eozénou -

  10. LAST RESULTS FROM KEK ON SINGLE CELL PRESENTED AT TTC MEETING - Fabien Eozénou -

  11. SINGLE CELL STUDY - Fabien Eozénou -

  12. EFFICIENT RECIPE FOR LOW SCATTER - Fabien Eozénou -

  13. ACID QUALITY CONTROL BY ICE F- and SO42- in EP acid measured by Ion Capillary Electrophoresis (ICE) HF losses due to degassing during acid preparation and EP are huge! - Fabien Eozénou -

  14. LAST RESULTS FROM SACLAY ON SINGLE CELL PRESENTED AT TTC MEETING - Fabien Eozénou -

  15. LAST RESULTS FOR NEW BAKING PARAMETERS B. Visentin - Fabien Eozénou -

  16. [F-] at time 1 000s SINGLE CELL EP + MODELING Single cell Electro-polishing: First Results. EP at constant voltage Baking and RF Test @ DESY 42.73 MV/m @1.8K after baking +7MV/m / last treatment Modeling: Influence of fluid circulation/cathode shape COMSOL Software Convection and diffusion + Chemical Reaction By M. Bruchon - Fabien Eozénou -

  17. SEARCH FOR BEST EP PARAMETERS • Voltage • New Voltage has been investigated. 5 Volt with standard mixture • Oscillation region → very shiny surface. • (Cavity 1C21 waiting for test). • Concerning the study for different HF-H2SO4-H2O mixtures • Standard mixture works well. • Water addition (Ex 1-9-1 mixture) undesirable • (lower removal rate and deteriorated surface). • High HF concentrations promising on samples → 3 - 6.72 - 0.28 mixture to be tested on single cell (low T, low voltage). • Diluted mixtures tested but Hydrogen contamination Intensity Voltage - Fabien Eozénou -

  18. COMMON R&D PROGRAM: CROSS PROCESSING AND TESTING OF CAVITIES - Fabien Eozénou -

  19. BAKING RESISTANT CAVITIES Some cavity tested at Saclay are not cured by baking! Polluted Niobium? Would heavy material removal by Barrel Polishing at KEK cure this batch of cavity? - Fabien Eozénou -

  20. ELECTROPOLISHING AND MODELING LL comparative studies between TTF, RE, LL, IS shapes 1500 s 13 000 to 30 000 s (mol.m-3) DIFFERENT CATHODE SHAPES INVESTIGATED BY MODELING → comparative RF measurements between TTF and IS shapes - Fabien Eozénou -

  21. « 1 - HOUR » BAKING & TUNER TESTS After positive result with “Fast Argon Baking” 145 °C / 3 hours … New apparatus under fabrication at Saclay for “1-Hour Baking” at 160°C (UHV or Argon) RF Test on 1-cell LL Ichiro cavity With a cavity from KEK Performances Comparison between “standard UHV baking” and “ 1-hour Argon baking” Tests at KEK with Saclay tuners for Lorenz forces detuning at high gradients on 9-cells Ichiro cavities at 77K - Fabien Eozénou -

  22. BETTER UNDERSTANDING OF BATH AGING At Saclay, we use a simple (but not precise) way to evaluate degassed acid. Scrubber for EP Set-Up: Sodium hydroxide + BTB C27H28Br2O5S When the mixture becomes acidic, it turns yellow. + Ionic chromatography tested on sample electropolishing ARE INVESTIGATIONS AT KEK AND SACLAY IN ACCORDANCE? - Fabien Eozénou -

  23. Thank you!!! - Fabien Eozénou -