Tribology

Tribology. Friction and Wear of Silicon Nitride Exposed to Moisture at High Temperatures. Andy Lin Engr 540x Tribology. Introduction. What’s the purpose of this study? We know that... Si 3 N 4 + 3O 2 = 3SiO 2 + 2N 2 SiO 2 interacts with water

Télécharger la présentation

Tribology

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Tribology Friction and Wear of Silicon Nitride Exposed to Moisture at High Temperatures Andy Lin Engr 540x Tribology

  2. Introduction • What’s the purpose of this study? We know that... • Si3N4 + 3O2 = 3SiO2 + 2N2 • SiO2 interacts with water • The goal is to determine the effects of water on Silicon Nitride -For coefficient of friction and wear rate

  3. Purpose • Why is this Relevant? Applications… • Silicon nitride automobile applications exposed to water vapor • Bearing/components of gas turbine engines • Ceramic coating on metallic components

  4. Experimental Procedure • Used sliding ball-on-flat apparatus in different environments containing water vapor at elevated temperature • Silicon nitride flats and isostatically pressed balls • 10,000 strokes (equivalent to 218 meters sliding distance) • Environments include: Argon, Air, 2% H20, 8% H20, 34% H20

  5. Friction coefficient vs Temperature • µ for Argon and air • about 0.65 from room • temperature to 1273K • µ for 8% H20 about • 0.3 from 573-973K • Higher µ after critical • temperature at 973K • 34% H20 has higher • critical temperature • Critical temperature • depends on partial • pressure of H20

  6. Wear Rate vs Temperature • Increased wear rate is • correlated with increased in µ • Transition to higher wear rate at 8% H20 also seen at 973K • Wear rate is lower in • presence of water as • compared with argon and air

  7. Wear Grooves and Rolls • Optical micrograph of wear groove with 8% H2O vapor at 973K • Cylindrical rolls oriented perpendicular to sliding direction • Geometry of rolls dependent on temperature and water vapor content • Rolls provide mechanical support between surfaces and reduce actual surface area contact

  8. SEM of “Rolls” • SEM of “rolls” with 34% H2O vapor at 873K • Rolls develop perpendicular to the sliding direction • Rolls are formed from smaller wear particles that adhere and form the cylinders (ie Playdoh)

  9. SEM of “Rolls” • SEM of “rolls” with 34% H2O vapor at 873K • Surface shows delamination and resulting debris particles • Debris particles are flattened and curled into a roll • Many layers of debris can be seen on rolls

  10. TEM “Rolls” • Image of fractured roll with small debris particles

  11. TEM “Rolls” • TEM of midsection and end • Surface non-homogenous • Smaller pieces are constituents of roll

  12. Friction and Wear vs Temperature • 2 transition temperatures for friction and wear • At the lower transition temperature, for H2O trials, µ reduces to about 1/2 the coefficient of friction at room temperature.

  13. Friction and Wear vs Temperature • At the higher transition temperature, for H2O trials, the µ increases to level of air and argon • This higher transition temperature is dependent on the partial pressure of water.

  14. Lower Transition Temperature • What going on at the lower transition temperature? • Formation of Oxide • Si3N4 + 3O2 = 3SiO2 + 2N2 • The increase in temperature allows: • significant oxide formation to reduce µ and wear • H20 vapor to modify SiO2 and lower it’s viscosity to form rolls • No rolls if SiO2 is too hard and brittle

  15. Higher Transition Temperature • What going on at the higher transition temperature? • Rolls begin to break down • Bigger and thicker rolls last longer • Produced by higher H2O vapor pressure • SiO2 layer breaks down • Becomes too soft • Displaced and squeezed out of contact surface • Therefore wear increases

  16. Conclusion • Formation of rolls is a big factor in reducing µ and wear • Formation of rolls are dependent on H20 vapor pressure and temperature • Therefore µ and wear rates of silicon nitride are dependent on temperature and humidity