In situ TEM Study of Ni-InGaAs Solid-State Reactions

In situ TEM Study of Ni-InGaAs Solid-State Reactions. Renjie Chen. Introduction. As conventional Si CMOS scaling approaches the end of the roadmap, III-V based MOSFETs are seriously being considered as an alternative technology to continue Moore’s law . [1]

merrill
Télécharger la présentation

In situ TEM Study of Ni-InGaAs Solid-State Reactions

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. In situ TEM Study of Ni-InGaAs Solid-StateReactions Renjie Chen

  2. Introduction • As conventional Si CMOS scaling approaches the end of the roadmap, III-V based MOSFETs are seriously being considered as an alternative technology to continue Moore’s law.[1] • To realized high-performance III-V MOSFETs, reliable contact metalsfor S/D with low contact resistance is essential,especiallyinhighlyscalesdevices. • An atomic level understanding of the metal-semiconductorsolid-statereactioncancan shed light on material-electronic property interactions at nano-scale,especiallywhentheintentionalorunintentionaldefectsarepresent. [1] Takagi, S.; Takenaka, M. In High mobility material channel CMOS technologies based on heterogeneous integration, Junction Technology (IWJT), 2011 11th International Workshop on, IEEE: 2011; pp 1-6

  3. Content • Introduction • Ni – III-V solid state reaction • In-situ TEM & Our group’s work • MyPreliminaryresults • ProcessdesigntofabricatechannelsonTEMmembrane • Recipemodification

  4. Ni-InGaAsSolid-StateReaction Self-aligned S/DContact Technology Ivana; Pan, J. etc. Applied Physics Letters 2011,99 (1), 012105-3 Kim, S. etc.Electron Devices Meeting (IEDM), pp26.6. 1-26.6. 4 Subramanian, S.; etc. Journal of The Electrochemical Society 2011,159 (1), H16-H21

  5. CrystallographicStudyofNi-GaAs GaAs Zinc Blende (a = 5.654 Å) Ni2GaAs hexagonal (a = 3.83 Å,c=5.04 Å) NiAshexagonal (a = 3.602 Å, c= 5.009 Å) β-NiGacesium chloride (a = 2.887 Å) Lahav, A.; Eizenberg, M.; Komem, Y., Interfacial reactions between Ni films and GaAs. Journal of Applied Physics 1986, 60 (3), 991-1001.

  6. Ni-InAsinNanoscaleChannels Diffusion Modal with Constant Source: Diffusion length: X = (Dt)1/2 Chueh, Y.-L., et al. (2008). "Formation and Characterization of NixInAs/InAs Nanowire Heterostructures by Solid Source Reaction." Nano Letters 8(12): 4528-4533

  7. In-situTEMTechnique Frances M Ross 2010 Rep. Prog. Phys. 73 114501 MRS BULLETIN • VOLUME 33 • FEBRUARY 2008 • www.mrs.org/bulletin

  8. PreviousWorkinOurGroup Heterogeneous Reactions in SiNanowires Tang, W.; Dayeh, S. A.; Picraux, S. T.; Huang, J. Y.; Tu, K.-N., Ultrashort Channel Silicon Nanowire Transistors with Nickel Silicide Source/Drain Contacts. Nano Letters 2012,12 (8), 3979-3985 Heterogeneous Reactions in Ge/Si Core/Shell Nanowires Dr.Minh’swork,submitted

  9. Heterogeneous Reactions withpresenceofTB: NucleationModeling: Heterogeneous Reactions withpresenceofTBandGB: Tang, W.; Picraux, S. T.; Huang, J. Y.; Gusak, A. M.; Tu, K.-N.; Dayeh, S. A., Nucleation and Atomic Layer Reaction in Nickel Silicide for Defect-Engineered Si Nanochannels. Nano Letters 2013,13 (6), 2748-2753

  10. Transfer InGaAs Membrane onto TEM Aperture TEM membrane TEM membrane InGaAs [100] Ni Ni InGaAs [110] Ni Ni Standard cubic stereographic projections for the [001] oriented crystal

  11. Approach 1: Ni-silicide Bonding Multiple Dielectric layers Deposition Bonding with Si TEM aperture Remove InP • HfO2 is used for HF resist layer (10 nm) • Al2O3 acts as block layer for F-etch (6 nm) • SiO2 prevents electronic leakage (200 nm) • Ni is used for Nickel Silicide bonding (Ti 25 nm, Ni 100 nm)

  12. Approach 2: Ni-InGaAs Bonding Bonding with Ni-InGaAs InP Removal • No need to remove SiNx layer • The broken window provides natural hollow square for Ni film evaporation • Ni for Ni-InGaAs bonding (Ti 5 nm, Ni 20 nm)

  13. Approach 1: Ni-silicide Bonding Approach 2: Ni-InGaAs Bonding Decrease Ni film thickness TEM aperture with 1 window (500um x 500um)

  14. TEMaperturewithmultiplewindowsincreases the chance for unbroken window: TEM aperture with 9 windows (100um x 100um)

  15. Fabricate InGaAs Diffusion Channels on Membrane Window • 1st EBL step: Write global/chip marks, followed by evaporation of Ni/Au/Ni • 2nd EBL step: Write Parallel lines on each window, evaporate Ni as both the reaction reservoir and the supporting lines • 2nd EBL step: Write Fin structure in between the Ni lines with different orientation

  16. MMA/PMMA double layers improve the lift-off process:

  17. Modified HSQ recipe for Fin writing: WithoutsurroundingNilines WithsurroundingNilines DenseNilines MF 319 Low T developing process 25% HDMS High T developing process

  18. Summary • In situ TEM observation is powerful to investigate the Ni-InGaAs solid state reaction . • Diffusion rate, alloy frontier interface, and crystallographic relationship can be studied during in situ TEM observation. • Currently, theInGaAsmembranewassuccessfullytransferredwithmodifiedbondingprocess,andseveralproblemsassociatedwithEBLwritinghasbeensolved. • FurtherexperimentsneedtobedoneinordertopreparethesamplereadyforTEMstudy.

  19. Thanks Q&A