This study explores the optimization of parameters for the Future Circular Collider (FCC) quadrupole magnets to enhance their performance. The focus is on achieving the highest gradient, releasing constraints on the dipole, and reducing manufacturing and operation complexity. The study considers factors such as loadline margin, conductor properties, cable parameters, and protection delays.

robd
Télécharger la présentation

Optimization of FCC Quadrupole Parameters for Improved Performance

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. FCC Main QuadC. LorinInputs from: G. Dilasser, D. Schoerling, T. Salmi, H. Felice, E. Rochepault, M. Segreti 11 april 2018

  2. Philosophy Till last year* • Reaching the highest gradient to release constraints on the dipole (FODO cell filling) • 4cos2θ layers. • Loadline margin: 14% • Conductor : EuroCirCol cables – strands – Jc (2250 A/mm² @ 1.9 K, 16 T) New Philosophy • Quads in the shadow of the dipoles (manufacture + operation) • Assemblycomplexity: 4 layers -> 2 layers • Loadlinemargin: 14% -> 20% • Re-openedcableparameters: up to 60 strands • Re-openedstrandparameters: Φ = 0.7-0.9 mm • Challenge the protection: 40 to 30 ms 50 mm *C. Lorin et al., Design of a Nb3Sn 400 T/m quadrupole for the Future Circular Collider, IEEE Transaction on Applied Superconductivity, 4004905, (2018)

  3. Comparison with last year study 2 layers not efficient All designs with a 350 K hotspot(EuroCirCol) *Todesco et al, Semi-analyticalapproaches to magnet design, Wamsdo 2013 Rossi L., Todesco E. Electromagnetic design of superconductingquadrupoles, PRSTAB, 2006 * eq. coilwidth 30° 25 mm *C. Lorin et al., Design of a Nb3Sn 400 T/m quadrupole for the Future Circular Collider, IEEE Transaction on Applied Superconductivity, 4004905, (2018)

  4. 2D exploration of the parameter space Protection: 40 to 30 ms(Hotspot = 350 K) • + 20 T/m on the gradient (~5%) • 2 layersefficiency: • Lowerthan ~51 strands • Worry about windability(50 mm aperture) • Windability test with MBH 11 T cable or MQXF cable would be welcome • Strand diameter: 0.7 mm or 0.9 mm • Nb of strands: 40-51-60 • Protection delay: 30 ms or 40 ms MBH 11 T ~MQXF Design selected for this study: Most simple design in-line with the optics baseline of 360 T/m 60 strands 0.7 mm 30 ms 51 strands 0.9 mm 40 ms 40 strands

  5. 2D electromagnetic design - cable To beproperlyrealigned on 11 T MBH HiLumiDipole, And/ or use 11 T MBH cableexperience

  6. 2D electromagnetic design - magnet

  7. Collar structure investigation (1/3) • Emag forces: Roxie vs Cast3m (CEA-made code) Fx = 1.06 MN/m Fy = 1.46 MN/m Icast3m = 1.01 Iroxieto better match the forces Fx = 1.03 MN/m Fy = 1.48 MN/m Roxie

  8. Collar structure investigation (2/3) • Contact description: • Both layer glued • Sliding no friction elsewhere • Nb3Sn Coilproperties • Ecoil = 30 GPa (+10% at cold), isotropic • Thermal shrinkage: 3.2E-3

  9. Collar structure investigation (3/3) • Target: contact at nominal of 10 to 15 MPa MPa 0 0 Cablewidth Average contact pressure at nominal: 30 MPa Lowest contact pressure spot: 11 MPa

  10. Collar structure investigation (4/3) • Collaring • Under powering(1.9 K) Average azimutal stress: 73 MPa Peak azimuthal stress: 142 MPa< 150 MPa Average azimutal stress: 58 MPa Peak azimuthal stress: 153 MPa< 200 MPa

  11. Conclusion • I wouldsuggest to stay in the blue area, but: • CLIQ simulations needed to propelyassess the hotspot • Windability trials to avoid ‘too’ bigcabletemptation • Try to keep the forces as low as possible to use the collartechnology (creep to beestimated) • 3D design underdevelopmenttowardswindability trials + peakfieldoptimization • No time for a slide for fun today Thankyou.

  12. Daniel Schoerling talk 60 strands 0.7 mm 30 ms 51 strands 0.9 mm 40 ms 40 strands

  13. List of FCC quad parameters Inputs for the FCC quad optimization are ticked in the open column with associated values/limits/comments. Some design inputs have already been fixed based on past experience and philosophy approach for the FCC quad.