An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 人力扎根計畫-整理加工 期末報告奈米TiO2與棉纖維抗UV 指導老師：黃國賢 學號：4960G004 姓名：蔡恩宗

  2. 前言 • Ti02為無機材具有活性高、穩定性和耐熱性好、對人體無毒及價廉等獨特的優點。 • 奈米Ti02粉體比表面積大，表面能高，極易團聚，造成整理劑穩定性差，處理後織物的手感、透氣性欠佳等問題。

  3. 整理劑的製備[1-3]

  4. 織物整理[1-3]

  5. XRD圖[1]

  6. 整理前後織物的X射線能譜分析[1]

  7. 不同溫度製備的Ti02乾燥所得粉末的XRD圖[2]

  8. 織物多次整理-XRD圖[3]

  9. 紫外線透過率曲線[3]

  10. 整理織物的紫外線防護性能[1-2]

  11. 紫外光一可見光吸光度圖[2]

  12. 1#～3#織物皂洗前後紫外線透過率[3]

  13. 織物整理前後的白度、強度、平挺度[3]

  14. 織物整理前後的回潮率、透氣性、抗靜電性[3]

  15. 結論 • 1.經過奈米Ti02處理後的棉織物，都能有效的提升抗UV功效並能具有抗靜電性及疏水性。 • 2.缺點是，處理後的織物，強力、透氣性及白度都略為下降。

  16. 參考文獻 • [1]邓桦， 邓宝祥，李秀明，李瀚宇 ，棉织物纳米Ti02抗紫外线整理，紡織學報，第29卷，第11期，2008年11月，第67頁 • [2]邓桦，李秀明，肖长发， Ti02纳米晶的低温制备及其抗紫外线性能，东华大学学报(自然科学版)，第35卷，第1期，2009年2月，第69頁 • [3]徐小峰，成春颖，林萍，郑利民，纳米Ti02在棉织物抗紫外整理中的应用，东华大学学报(自然科学版)，第35卷，第1期，2009年2月，第74頁