An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Reactorpressurevessel embrittlement in Doel 3/Tihange 2 Ilse Tweer INRAG Public Conference, April 13 – 14, Aachen, Germany

  2. Reactor pressure vessel embrittlement D3/T2 The reactorpressurevessel (RPV) isthecentralcomponentof a nuclearreactor, - forsafeoperationofthe NPP throughoutservicelife RPV failurehastobeexcluded, becausesafetysystemsare not designedtocopewith RPV failure Hazardsforthestructuralintengrityofthe RPV: - developmentand/orgrowthofdefects (cracks)- material degradation due toradiation embrittlement and thermomechanical fatigue Demonstration ofthe RPV structuralintegrity (PTS analysis): comparisonofthecalculatedload on eachdetected crack forthemostsevereaccidenttransientswiththeactual material properties (fracturetoughness) ofthe RPV steel, consideringtheagingdegradation INRAG Public Conference April 13 – 14 Aachen, Germany

  3. Pressurized thermal shock (PTS) analysis Source: SCK-CEN Eric van Walle, NENE 2013, Bled, Slovenia, September 11, 2013The Detection of Hydrogen Flakes in the Belgian Doel3/Tihange2 Reactor Pressure Vessels INRAG Public Conference April 13 – 14 Aachen, Germany

  4. Determination of the actual RPV steel properties Surveillance irradiation experiments are supposed to monitor radiation-induced material embrittlement using plant-specific archive material National regulations include embrittlement trend curves – empirical formulas based on irradiation experiments using similar steel samples The trend curves allow to calculate the shift of the fracture toughness curve due to radiation-induced embrittlement (shift of the ductile-brittle transition temperature to higher temperatures) in dependence of the neutron fluence The surveillance program results should be enveloped by the trend curves INRAG Public Conference April 13 – 14 Aachen, Germany

  5. RPV embrittlement in Doel 3/Tihange 2 The detection of large amount of defects (hydrogen flakes/cracks) in the RPVs of D3/T2 has raised the question whether the defect-free surveillance program material can represent the defect-containing RPV steel No defect containing archive material for D3/T2 is available Electrabel performed irradiation experiments using samples from the AREVA shell VB 395, a rejected steam generator block containing hydrogen flakes, and samples from a German research project ; the representativeness of these samples for the RPVs D3/T2 is doubtful The observed radiation embrittlement of the VB 395 samples was significantly higher than expected; Electrabel excluded radiation effects due to the defects and declared the high-embrittlement results as „abnormal outliers“ due to an unknown embrittlement mechanism Electrabel defined new embrittlement trend curves and replaced the FIS curves INRAG Public Conference April 13 – 14 Aachen, Germany

  6. Safety Cases 2015Replacement of the FIS curve by a new trend curve (Electrabel 2015) • Safety Case 2012: Electrabel proposed an extra shift of 50°C on top of the FIS-curves to cover unknown radiation effects • Safety Case 2015: Electrabel replaced the FIS curve by a new trend curve • The new trend curve is in the SIA (structural integrity assessment) relevant fluence range (about 3x1019 n/cm2) less conservative than the proposed trend curve from 2012 INRAG Public Conference April 13 – 14 Aachen, Germany

  7. Conclusions The radiation influence on the real defect-containing D3T2 RPV material has not been clarified due to the lack of representative samples The declaration of irradiation results using VB 395 samples (that were supposed to represent hydrogen flakes containing materials) as „abnormal outlier“ is not acceptable In the fluence range relevant for structural integrity assessment the new embrittlement trend curve is less conservative than the proposed embrittlement curve in the frame of the safety case 2012; thus the stated consideration of possibly higher embrittlement due to unknown processes in consequence of the irradiation campaigns is not existent INRAG Public Conference April 13 – 14 Aachen, Germany

  8. Comment to the situation in Beznau In the frame of the safety case Beznau-1 (2018) a Replika of the defect containing RPV shell was produced to study the effect of Al2O3 inclusions on material properties No irradiation experiments were performed ENSI: „In the past, extensive research has been undertaken to investigate microstructural characteristics of embrittlement, develop models and provide databases. In comparison, there are only few investigations into the influence of non-metallic inclusions on irradiation embrittlement. This is because non-metallic inclusions are not bonded with the surrounding matrix and there is no doubt that non-metallic inclusions themselves are not subject to irradiation embrittlement. “ Remark: This argument is not sufficient, radiation- enhanced diffusion and radiation-induced segregation of impurities and radiation-induced defects cannot be excluded and could trigger defect growth by attachment at the existing inclusions INRAG Public Conference April 13 – 14 Aachen, Germany