AN ANALYTICAL APPROACH TO WEDGE ASPERITIES AND THEIR INFLUENCE ON FRICTIONAL LOADS OF STRUCTURAL SURFACES. CHRISTOPHER STUBBS FRICTION , WEAR, AND LUBRICATION OF MATERIALS RENSSELAER POLYTECHNIC INSTITUTE. PLOUGHING-INDUCED FRICTION CLOSE FORM SOLUTION.

una
Télécharger la présentation

CHRISTOPHER STUBBS FRICTION , WEAR, AND LUBRICATION OF MATERIALS RENSSELAER POLYTECHNIC INSTITUTE

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. AN ANALYTICAL APPROACH TO WEDGE ASPERITIES AND THEIR INFLUENCE ON FRICTIONAL LOADS OF STRUCTURAL SURFACES CHRISTOPHER STUBBS FRICTION, WEAR, AND LUBRICATION OF MATERIALS RENSSELAER POLYTECHNIC INSTITUTE

  2. PLOUGHING-INDUCED FRICTIONCLOSE FORM SOLUTION • From the free body diagram the following definitions can be made: • And: • Such that: • Furthermore, the analyses presented in this report all use a wedge asperity geometry with an angle of 60⁰, which results in the following close form solution:

  3. MODELOVERVIEW • Elastic-perfectly-plastic material model • Hardness of the wedge is set to 1:1, 2:1, 3:1, and 4:1 • Quasi-Static Abaqus/Eplicit Model • Full contact • Wedge asperity driven 2.0” (2X the length of the asperity) over 1.0 seconds • Reaction loads taken from boundary conditioned nodes

  4. RESULTS (4:1 WEDGE HARDNESS) 0.0” Penetration

  5. RESULTS (4:1 WEDGE HARDNESS) 0.5” Penetration

  6. RESULTS (4:1 WEDGE HARDNESS) 1.0” Penetration

  7. RESULTS (4:1 WEDGE HARDNESS) 1.5” Penetration

  8. RESULTS (4:1 WEDGE HARDNESS) 2.0” Penetration

  9. CONCLUSIONS • As expected, as the relative hardness is increased, the closed-form solution becomes more representive. • For this analysis, once a hardness ratio of approximately 3:1 is obtained, the close-form solution in with 10% of the finite element solution.