1 / 22

Polymerisation

Polymerisation. Addition Polymerisation Condensation Polymerisation Uses of polymers. Addition Polymerisation. A carbon – carbon double bond is needed in the monomer A monomer is the small molecule that makes up the polymer. Addition Polymerisation. The polymer is the only product

warren
Télécharger la présentation

Polymerisation

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Polymerisation Addition Polymerisation Condensation Polymerisation Uses of polymers

  2. Addition Polymerisation • A carbon – carbon double bond is needed in the monomer • A monomer is the small molecule that makes up the polymer

  3. Addition Polymerisation • The polymer is the only product • Involves the opening out of a double bond • The conditions of the reaction can alter the properties of the polymer • Reaction proceeds by a free radical mechanism • Oxygen often used as the initiator

  4. Addition polymerisation • The board specifies that you know this addition polymerisation reaction

  5. Addition polymerisation • Conditions are high pressure and an oxygen initiator (to provide the initial free radical). • Monomer = phenylethene • Polymer = poly(phenylethene)

  6. Addition Polymerisation • You are expected to be able to do the following things with addition polymers: • Predict the repeating unit of the polymer given the monomer • Predict the monomer from the polymer – displayed formula and even empirical formula. • Know about stereochemistry of addition polymers.

  7. Prediction the repeating unit • This is easy, basically open out the double bond.

  8. Predicting the monomer from the polymer • This is kind of the opposite to what you have just done. • They may ask you to draw different formulae. • You need to make sure you can convert repeating units into monomers, and draw a ring around the repeating unit

  9. Stereoisomerism in Addition polymers. • Ziegla and Natta in the 1950s cam up with a way of controlling the repeating unit. • They won a Joint Nobel prize for their work • The polymerisation process can be controlled used a tin/aluminium catalyst at 50°C and 1.5atm

  10. Stereoisomerism in Addition polymers. • Previous to this only one type of poly(ethene) could be made, called LDPE or low density poly(ethane). • The chains formed a tangled mass. • HDPE could now be produced. • This has a much stiffer structure due to areas of crytallinity where the polymer chains are much more ordered.

  11. Stereoisomerism in Addition polymers. • HDPE has a much higher boiling point due to these more ordered regions. • Generally used to make plastic bottles. • Ziegler and Natta also discovered that they could make stereo regular polymers. Isotactic, syndiotactic and atactic.

  12. Poly(propene) and stereoisomerism • Isotactic. This is a very regular type of polymer chain. All the methyl groups are on the same side.

  13. Poly(propene) and stereoisomerism • Syndiotactic. A slightly less regular but still very ordered polymer. • The methyl groups alternate the side of chain they are on.

  14. Poly(propene) and stereoisomerism • Atactic. • This is a completely random allocation of methyl groups along the carbon skeleton.

  15. Poly(propene) and stereoisomerism • This varying degree of randomness will affect the strength and melting point of the polymer. • The less random, the stronger the polymer and the higher the melting point • This is because in a more ordered polymer they chains can get closer together and hence the van der Waal’s forces will be greater.

  16. Condensation Polymers • Involves 2 monomers that have different functional groups. • They also involve the elimination of water or another small molecule. • Hence the term condensation polymer. • Monomer A + Monomer B  Polymer + small molecule (normally water). • Common condensation polymers include polyesters (the ester linkage) and polyamides (the amide linkage as in proteins).

  17. Polyesters • The OCR example here is terylene, a polymer of benzene-1,4-dicarboxylic acid and ethane-1,2-diol. • The ester linkage is formed between the monomers

  18. Polyesters • You need to be able to reproduce the formation of terylene, and possibly predict the structures of other polyesters

  19. Polyamides • These involve the linkage of two monomers through the amide linkage as in proteins (e.g. silk)

  20. Nylon 6,6 a polyamide

  21. Kevlar a polyamide

  22. Uses of polyamides • The main use of polyesters and polyamides is as fibres in clothing. • Most clothing now has a degree of manufactured fibres woven into the natural material (such as cotton). • This gives the material more desirable characteristics, such as stretchiness, and better washability. • Don’t forget that proteins are also polyamides, you must know how the linkage works with natural polymers such as proteins.