ASTM E08.04.01 Workshop

ASTM E08.04.01 Workshop. Life Prediction Methodology and Validation for Surface Cracks Norfolk, Virginia May 23, 2007. Goals.

yeriel
Télécharger la présentation

ASTM E08.04.01 Workshop

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ASTM E08.04.01 Workshop Life Prediction Methodology and Validation for Surface Cracks Norfolk, Virginia May 23, 2007

  2. Goals • Develop validation procedures for surface cracks in monotonic and cyclic loading with regard to crack shape evolution, crack driving force, and fatigue life prediction. • Gather the basis for an ASTM guideline for software validation of analyses of surface cracks in monotonic or cyclic loading.

  3. George Irwin on Surface Cracks “In the examination of fracture failures one rarely finds that the initial starting crack extended completely through the thickness or that the starting-crack development, say by fatigue, occurred along a line extending completely through a cross section of a component. A part-through crack is more typical of the starting-crack shape customarily found.” Dec. 1962 J. Appl. Mech.

  4. We Don’t Have X-Ray Vision… …or do we?

  5. Schedule—1:15-2:45PM • The Evolution and Application of Three-Dimensional Stress-Intensity Factors • J. C. (Jim) Newman, Jr., I. S. Raju, and S. A. Fawaz • A Framework for Investigating Crack Shape Evolution of Surface Cracks • Will Riddell • Surface Crack Testing of Welded Titanium Sheet According to ASTM E740 • Dan Garcia • BREAK 2:45-3:15PM

  6. Schedule—3:15-5:00PM • Crack Shape Evolution Studies with NASGRO 3.0 • Elizabeth Watts and Chris Wilson • Comparison of Elastic-Plastic J Solutions for the Surface Crack • Chris Wilson and Eric Quillen • Investigations into Deformation Limits for SSY and LSY for the Surface Crack in Tension • Phillip Allen and Doug Wells • Closing Remarks 4:45-5:00PM

  7. Closing Remarks • Task Group E08.04.01 Life Validation meets Monday AM of Committee Week • Contact me at Chris Wilson Dept. of Mechanical Engineering Tennessee Tech University 931-372-3216 chriswilson@tntech.edu

  8. Why We Do What We Do…