Transition Metal Oxide Perovskites: Band Structure, Electrical and Magnetic Properties

Transition Metal Oxide Perovskites: Band Structure, Electrical and Magnetic Properties. Chemistry 754 Solid State Chemistry Lecture #24 May 27, 2003. Transition Metal Oxides.

yvonne
Télécharger la présentation

Transition Metal Oxide Perovskites: Band Structure, Electrical and Magnetic Properties

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Transition Metal Oxide Perovskites:Band Structure, Electrical and Magnetic Properties Chemistry 754 Solid State Chemistry Lecture #24 May 27, 2003

  2. Transition Metal Oxides • To illustrate the relationship between crystal structure, bonding, band structure, electricalandmagnetic properties we are going to consider transition metal oxides of three structure types. • Perovskite (AMO3)/ReO3 • Rock Salt (MO) • Rutile (MO2) • For all three structures M-O interactions will dictate the properties. In the latter two structure types we also need to consider M-M bonding.

  3. Perovskites and Band Structure • Octahedral Molecular Orbital Diagram • p*(t2g) and s*(eg) Bands • Orbital Overlap and Bandwidth (ReO3 vs. MnO32-) • Structural Distortions (Octahedral Tilting) • Exchange Splitting (Spin Pairing Energy) • The d-electron count (SrTiO3 to SrFeO3) • Instabilities and the d4 electron count • SrFeO3 • LaMnO3 • CaFeO3

  4. Perovskite Crystal Structure M O A

  5. Generic Octahedral MO Diagram t1u (s* + p*) (n+1)p a1g (s*) Oxygen (n+1)s eg (s*) nd eg (dx2-y2, dz2) t2g (p*) O 2p p (6) - t2g, t1u O 2p NB(6)-t1g, t2u (n+1)d t2g (dxy, dxz, dyz) t1g & t2u O 2p s (6) a1g, t1u, eg Transition Metal t2g (p) eg (s) t1u (s + p) a1g (s)

  6. Simplified Band Structure Bands of interest s* [4] (n+1)p Oxygen (n+1)s M-O s* [2] nd eg (dx2-y2, dz2) M-O p* [3] (n+1)d t2g (dxy, dxz, dyz) O 2p p (12) O 2p NB O 2p s (6) a1g, t1u, eg M-O p Transition Metal M-O s

  7. Orbital Overlap s* and p* Bands p*Overlap (M d t2g – O 2pp) G M Band Runs Uphill Greater Spatial Overlap W(s*) > W(p*) M point (kx=ky=p/a) antibonding G point (kx=ky=0) non-bonding s*Overlap (M d eg – O 2ps) G M Band Runs Uphill

  8. y x X point Overlap in 3D So far we have been working mostly in 1D and 2D. In 3D keep the following overlap considerations in mind: X Point (kx=p/a, ky=kz=0) dxy, dxz 1/2 antibonding dyz  nonbonding 2 degenerate bands M Point (kx=ky=p/a, kz=0) dxy,  antibonding dyz, dxz  1/2 antibonding 2 degenerate bands R Point (kx=ky=kz=p/a) dxy, dyz, dxz antibonding 3 degenerate bands

  9. s*(eg) W~7 eV s*(eg) W~4 eV p*(t2g) W~5 eV p*(t2g) W~2 eV Band Structure ReO3 and MnO32- ReO3 MnO32-

  10. Mn Mn O Mn Mn O Structural Distortions: CaMnO3 Cubic (Pm3m) Linear Mn-O-Mn Orthorhombic (Pnma) Bent Mn-O-Mn

  11. Octahedral Tilting & Band Structure Cubic (Pm3m) Linear Mn-O-Mn Orthorhombic (Pnma) Bent Mn-O-Mn s*(eg) W~4 eV s*(eg) W~2.5 eV p*(t2g) W~2 eV p*(t2g) W~1.5 eV

  12. eg(s*)  EF DOS Spin Polarized Band Structure t2g(p*)  eg(s*)  t2g(p*)  CaMnO3 is a Mott-Hubbard Insulator, rather than a metal!

  13. 3d TM Oxide Perovskites p*, s* implies delocalized electrons t2g, eg implies localized electrons

  14. eg(s*)  t2g(p*)  eg eg eg(s*)  EF t2g(p*)  t2g t2g Fe4+ Fe4+ DOS SrFeO3-The Edge of Instability Cubic Structure No Jahn-Teller Distortion All Fe atoms equivalent Localized t2g electrons Delocalized eg electrons Metallic to at least 4 K

  15. Cubic Band Structure Calculations

  16. LaMnO3-Cooperative Jahn Teller Dist. Fe(Mn)-O Distances LaMnO3 2  1.907(1) Å 2  2.178(1) Å 2  1.968(1) Å SrFeO3  6  1.92 Å Fe(Mn)-O-Fe(Mn) Angles CaFeO3 155.48(5) 155.11(5) SrFeO3  180 Octahedral tilting and decreased covalency both narrow the s* (eg) band. This leads to electron localization and a cooperative Jahn-Teller Distortion

  17. dx2-y2 dx2-y2 (s*)  eg dz2(s*)  dz2 t2g(p*)  dx2-y2 (s*)  t2g EF t2g dz2(s*)  Mn3+ Mn3+ t2g(p*)  DOS LaMnO3-Cooperative Jahn Teller Dist. Symmetric MnO6 Jahn-Teller Distortion Orthorhombic Structure Pronounced Jahn-Teller Distortion All Mn atoms equivalent Localized t2g & eg electrons Semiconductor

  18. Ca CaFeO3-Charge Disproportionation Fe-O Distances CaFeO3 2  1.919(2) Å 2  1.927(2) Å 2  1.919(1) Å SrFeO3  6  1.92 Å Fe-O-Fe Angles CaFeO3 158.1(1) 158.4(2) SrFeO3  180 Octahedral tilting narrows s* (eg) band, leads to electron localization!

  19. eg eg eg eg t2g t2g t2g Fe5+ Fe3+ t2g Soft Mode Condensation (290 K) Oxygen shift alters crystal field splitting Localizes the eg electrons Drives Metal to Semiconductor Transition