An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 材料試驗---破壞性試驗 1.拉伸 試驗 2.硬度試驗 3.衝擊試驗 4.金相顯微試驗

  2. 名詞解釋 • 壓痕器(indenter)：硬度試驗時將試片壓成凹痕的工具

  3. 常用硬度試驗 • 勃氏硬度試驗 • 洛氏硬度試驗 • 維克氏硬度試驗 • 蕭氏硬度試驗

  4. 勃氏硬度試驗(HB) • 壓痕器：直徑10mm硬鋼球 • 荷重： a.硬質材料(如鋼、鐵等)—3000kgf b.軟質材料(如銅、鋁等)—500kgf • 加壓時間：10~15秒

  5. 洛氏硬度試驗(HR) • A尺度(HRA) • B尺度(HRB) • C尺度(HRC) • 操作步驟

  6. 洛氏硬度試驗(HRA) • 壓痕器：120°金剛石圓錐 • 荷重：60kgf • 適合測試材料—超硬材料(如碳化鎢) • 加壓時間：6~8秒

  7. 洛氏硬度試驗(HRB) • 壓痕器：直徑 1/16〞硬鋼球 • 荷重：100kgf • 適合測試材料：一般硬材料(如低碳鋼、銅合金) • 加壓時間：6~8秒

  8. 洛氏硬度試驗(HRC) • 壓痕器：120°金剛石圓錐 • 荷重：150kgf • 適合測試材料：淬火材料(如高速鋼、合金鋼、 高碳鋼) • 加壓時間：6~8秒

  9. 洛氏硬度試驗機操作步驟 • 選擇適當墊塊，再將試片置於其上，試片需穩定不能動搖 • 選擇適當荷重置於槓桿架上的配重 • 檢查手搖柄是否放鬆 • 上昇試片到接觸壓痕器，致使刻度盤上的短指針回轉至小紅點中央處(10kgf) • 轉動刻度盤黑色刻度〝0〞對正長指針的位置(歸零)

  10. 洛氏硬度試驗機操作步驟 • 推動槓桿手搖柄(長指針會順時鐘方向旋轉) • 長針停止後等待(HRC：5~6s、HRB：6~8s) • 放鬆槓桿手搖柄 • 紀錄硬度值 • 降下試片 • 重複前述步驟再測試四點

  11. 洛氏硬度測試點選擇 • 一般為中央及邊緣每間隔90度做五點 • 測試值差〝3〞以上時應另尋測試點重新試驗

  12. 維克氏硬度試驗(HV) • 壓痕器：136°金剛石角錐 • 常用荷重：5、10、20、30、50kgf • 適合測試材料—表面硬化鋼、鍍鉻層 • 利用對角線長度計算面積