UTICAJ HOMOGENIZACIJE NA STRUKTURU TOPLO VALJANIH Al-Mg LEGURA ZA BRODOGRADNJU

UTICAJ HOMOGENIZACIJE NA STRUKTURU TOPLO VALJANIH Al-Mg LEGURA ZA BRODOGRADNJU. E. Romhanji, M. Popović, D. Glišić, T. Radetić. Tehnološko-metalurški fakultet, Univerzitet u Beograd u. R. Dodok, B. Milović, D. Jovanović. Valjaonica aluminijuma Impol-Seval. Ministarstvo nauke

brent
Télécharger la présentation

UTICAJ HOMOGENIZACIJE NA STRUKTURU TOPLO VALJANIH Al-Mg LEGURA ZA BRODOGRADNJU

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. UTICAJ HOMOGENIZACIJE NA STRUKTURU TOPLO VALJANIH Al-Mg LEGURA ZA BRODOGRADNJU E. Romhanji, M. Popović, D. Glišić, T. Radetić Tehnološko-metalurški fakultet, Univerzitet u Beogradu R. Dodok, B. Milović, D. Jovanović Valjaonica aluminijuma Impol-Seval Ministarstvo nauke Republike Srbije

  2. Al-Mg legure za brodogradnju • Standardne legure za brodogradnju: • Serija 5000 (Al-Mg) – limovi i trake • 5083, 5086, 5754, 5052, 5454, 5456. • Serija 6000 (Al-Mg-Si) – profili i šipke • 6005, 6061, 6082.

  3. >3% Mg - problem intergranularne i raslojavajuće korozije. • Sprečiti taloženje -faze u vidu neprekidnog filma po granicama zrna • Izbeći strukturu sa izduženim zrnima (“pancake”)

  4. Mogućnost poboljšanja osobina • Dodatak Zn i Cu • kontrola raspodele -faze po granicama zrna • promena kinetike taloženja -faze • Dodatak Zr • otežava rekristalizaciju i stvaranje prskotina pri zavarivanju • Homogena rekristalisana mikrostruktura TV trake • Ubrzana rekristalizacija u procesu toplog valjanja

  5. Materijal

  6. Homogenizacija • Zavisnost električnog otpora od temperature homogenizacije 565°C/6h (35°C/h) + 460°C/6h

  7. Termo-mehanički režim

  8. 5083 +Zn+Zr +Zn +Zn+Zr TV 65% Mikrostruktura TV trake

  9. +Zn+Zr TEM +Zn

  10. Rezime • Ubrzana rekristalizacija posle “heterogenizacije” • Legura sa Zn potpuno rekristalizovana • Sitne čestice na bazi Zr blokiraju granice zrna – nepotpuna rekristalizacija