CdTe 量子点与磁性纳米粒子的合成

CdTe 量子点与磁性纳米粒子的合成. 2012.12.09 郑昊. CdTe 量子点的合成. 水热合成法： 一、前驱 体 制备 1.NaBH 4 与 Te 粉反应生成 NaHTe 作为 Te 源 2.Cd 2+ 水溶液中加入 MPA ，用 NaOH 调节 PH 至 8.5 3. 将 1 加入氮气保护的 2 溶液形成前驱体溶液 二、控温水热回流. 第一次实验由于 NaBH 4 与 Te 粉反应的条件控制不佳，最后所得溶液基本无荧光. 两组 实验探究 NaBH 4 与 Te 粉反应条件. 第一 组 40 度水浴反应 8 个小时

burke
Télécharger la présentation

CdTe 量子点与磁性纳米粒子的合成

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. CdTe量子点与磁性纳米粒子的合成 2012.12.09 郑昊

  2. CdTe量子点的合成 水热合成法： 一、前驱体制备 1.NaBH4与Te粉反应生成NaHTe作为Te源 2.Cd2+水溶液中加入MPA，用NaOH调节PH至8.5 3.将1加入氮气保护的2溶液形成前驱体溶液 二、控温水热回流

  3. 第一次实验由于NaBH4与Te粉反应的条件控制不佳，最后所得溶液基本无荧光 两组实验探究NaBH4与Te粉反应条件

  4. 第一组40度水浴反应8个小时 第二组40度水浴反应2个小时 其它条件一致回流20小时

  5. 第一组： 发射波长577nm；强度519；半峰宽52 第二组： 发射波长540nm；强度318；半峰宽42 第一组反应比较完全，所以强度高 第二组反应未被氧化，所以粒径较均一 选择第二组进行后续实验

  6. 第三组峰值660nm；强度66；半峰宽62；

  7. 1.从颜色上判断2小时的反应不够充分，8个小时氧化比较严重1.从颜色上判断2小时的反应不够充分，8个小时氧化比较严重 2.红光那组还有待重做一组，光强度较差 3.对合成的探究基本到位，后面重点放到磁性纳米粒子的合成和检测的探究

  8. 第二组：发射峰540；强度318；半峰宽42 绿光组：发射峰552；强度575；半峰宽40

  9. Fe3O4磁性纳米粒子的合成 1.FeCl3分散在H2O中 2.加入乙醇，己烷，油酸，搅拌30min 3.加入NaOH，封闭容器70度搅拌4h

  10. 谢谢