1 / 27

Superconducting High-Field Accelerator Magnets: Status and Perspectives

Superconducting High-Field Accelerator Magnets: Status and Perspectives. Arnaud Devred CEA/DSM/DAPNIA/SACM & CERN/AT/MAS on behalf of the NED Collaboration SPIE International Congress on Optics and Electronics (Photonics Applications in Industry and Research IV)

chancellor-rodrigo
Télécharger la présentation

Superconducting High-Field Accelerator Magnets: Status and Perspectives

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Superconducting High-Field Accelerator Magnets: Status and Perspectives Arnaud Devred CEA/DSM/DAPNIA/SACM & CERN/AT/MAS on behalf of the NED Collaboration SPIE International Congress on Optics and Electronics (Photonics Applications in Industry and Research IV) Warsaw University of Technology 30 August 2005

  2. Contents • Why do we need high-field • accelerator magnets? • State of the art in superconducting • accelerator magnet technology • Ongoing Nb3Sn accelerator magnet • programs

  3. The Push Towards Higher Fields • For a given tunnel size, the energyof a circular accelerator is limited by the strength of bending (dipole) magnets. • For both linear and circular colliders, the luminosity is determined (mainly) by the optics of Interaction Regions (IR’s), which is itself limited by the strength and quality of final-focusing (quadrupole) magnets. • Over the years, there has been a constant push from the High-Energy Physics (HEP) community to keep developing higher-field and higher-field-gradient accelerator magnets.

  4. Superconducting Accelerator Magnets • The push towards higher fields led naturally to the use of superconductors. • One of the pioneers in the development of superconducting accelerator magnets was W.B. Sampson at BNL in the mid 1960’s. 76-mm-aperture, 85-T/m quadrupole magnet model wound from Nb3Sn ribbons and cold tested at BNL in January 1966 (Courtesy W.B. Sampson)

  5. The Tevatron • The first successful use of sc magnets in an machine took place at the Tevatronat Fermilab, which was commissioned in 1983 and which has been running very reliably since then. • The Tevatron was instrumental in demonstrating the feasibility and reliability of superconducting magnet systems and has paved the way to their commercial applications (such as MRI systems). 76.2-mm-aperture, 4-T Tevatron dipole magnet

  6. The LHC • Since the time of the Tevatron, significant progress has been made in the design and production of superconductors and magnets, enabling a gain of a factor ~2 in field. • The most advanced superconducting particle accelerator is the LHC presently under construction at CERN. • The industrial production of the required 1232 dipole magnets and ~400 quadrupole magnets is well underway and will be completed by the end of 2006. 56-mm-twin-aperture, 8.33-T LHC arc dipole magnet

  7. What’s Next? • Due to the high radiation doses to which they will be submitted, the life expectancy of LHC IR quadrupole magnets is estimated ~7 years. • Hence, it is likely that these magnets will have to be replaced around 2015, thereby offering an opportunity of upgrading LHC IR optics to improve luminosity. • Mid-2010’s is also the earliest time frame when one can expect to need final-focusing quadrupole magnets for the International Linear Collider (ILC).

  8. Magnets for LHC IR Upgrade • Several scenarios of LHC IR upgrade are presently being considered,e.g. New layout where beam-separation dipoles are positioned in front of final focusing quadrupoles (Courtesy O. Brüning) Same layout as presently, but with larger-aperture and stronger final-focusing quadrupoles (Courtesy T. Sen) • The various scenarios call for the development of large-aperture, high-field or high-field gradient magnets.

  9. Magnets for ILC IR’s • Magnet requirements are IR-design dependent,e.g. NLC-type IR with large crossing angle requires strong but very compact quadrupole magnets to clear the way for crossing beam (Courtesy B. Parker, BNL) TESLA-type IR requires LHC-type quadrupole magnets to be operated in a 4-T solenoidal background field (Courtesy F. Kircher, CEA)

  10. Roadmap for High-Field Accelerator Magnet R&D • A reasonable roadmap for high-field accelerator magnet development appears to be • to get ready for LHC-IR upgrade in 2015 • (large-aperture, high-performance dipole and/or quadrupole magnets; cost is not the primary issue), • to develop final-focusing quadrupole magnets for implementation in alinear collider IR in the mid-2010’s • (LHC-type quadrupole magnets in a solenoidal background field, or compact quadrupole magnets; cost is not the primary issue), • to promote generic magnet R&D aimed at LHC energy upgrade or a super LHC in the 2020’s • (high-performance, low-cost dipole and quadrupole magnets).

  11. Contents • Why do we need high-field • accelerator magnets? • State of the art in superconducting • superconducting magnet technology • Ongoing Nb3Sn accelerator magnet • programs

  12. State of the Art in NbTi • Since the Tevatron, the most widely used superconductor is the ductile alloy NbTi (world production: ~1500 t/year). • The LHC magnet R&D programs have shown that the limit of NbTi at 1.8 K was around 10 to 10.5 T. • Hence, to go beyond the 10-T threshold, it is necessary to change the material. Quench performance of 88-mm-aperture MFRESCA dipole magnet at CERN (Courtesy D. Leroy)

  13. Beyond NbTi: Nb3Sn • At present, the only serious candidate to succeed NbTi is the intermetallic compoundNb3Sn (world production: ~15 t/year). (Courtesy P.J. Lee, University of Wisconsin at Madison)

  14. Pros and Cons of Nb3Sn • Nb3Sn has a critical temperature (qC) and an upper critical magnetic flux density (BC2) that are about twice those of NbTi; however, once formed, it becomes brittle are its qC, BC2 and JC are strain sensitive. • The brittleness and strain sensitivity require a rethinking of all manufacturing processes and, so far, have limited the use of Nb3Sn to specific high field applications (such as high field NMR magnet systems). (Courtesy J.W. Ekin, 1983)

  15. Progress on Nb3Sn • Over the last decade, significant progress has been made on Nb3Sn, thanks to the ITER Engineering Design Activities (EDA) and vigorous R&D programs carried out in the USA. Progress on maximum quench field of dipole magnet models Progress on non-Cu JC (at 4.2 K and 12 T) of multifilament composite wires

  16. Main Challenges for High-Field Accelerator Magnet R&D • Although Nb3Sn technology is far from being mature, it seems at hand for the high-field and high-field-gradient accelerator magnets that may be needed for LHC IR upgrade and ILC IR’s. • However, we do need to keep working hard if we want to turn the few successful demonstrator magnets built so far into accelerator-class devices that can be implemented in a machine in a 10-year time frame.

  17. Contents • Why do we need high-field • accelerator magnets? • State of the art in superconducting • accelerator magnet technology • Ongoing Nb3Sn accelerator magnet • programs

  18. Ongoing Nb3Sn Accelerator Magnet R&D Programs • At present, two main, complementary, Nb3Sn accelerator magnet programs have been launched • the US-LHC Accelerator Research Program (LARP) in the USA, • the Next European Dipole (NED) Joint Research Activity (JRA), within the framework of the Coordinated Accelerator Research in Europe (CARE) Integrated Activities. • Note that CEA, Fermilab and LBNL are also pursuing (independently-funded) “base” programs.

  19. US-LARP (1/2) • The US-LHC Accelerator Research Program is aimed at supporting US efforts in LHC commissioning and at designing and developing equipment for LHC upgrade (such as advanced beam instrumentation and Nb3Sn magnets). • It is carried out by a collaboration made up of BNL, Fermilab, LBNL and SLAC. • Serious things will start in FY06, with a budget of 11 M$ (5 for magnets, 4 for accelerator-related R&D and 2 for management); this budget is expected to be maintained at a constant level for a few years.

  20. US-LARP (2/2) • The magnet part of LARP is aimed at building by 2009 one or two 4-m-long, 90-mm-aperture, 200 T/m quadrupole magnet prototypes, so as to demonstrate the feasibility of “long”, accelerator-class Nb3Sn magnets. • It will also support the continuous development of high-performance Nb3Sn wires in US industry.

  21. EU-CARE/NED (1/2) • The CARE/NED JRA is a more modest program, that was re-scoped in 2004 to match the allocated EU funding (1 M€ total over 2004-2006). • At present it is articulated around three main tasks • high-performance Nb3Sn conductor development and characterization (in collaboration with EU industry), • insulation development and characterization, • design studies for a large aperture (88 mm) high field (15 T conductor peak field) dipole magnet.

  22. EU-CARE/NED (2/2) • In spite of the limited funding, NED is supported by a very active collaboration made up of eight institutes • CCLRC/RAL (UK), • CEA (France), • CERN (International), • CIEMAT (Spain), • INFN-Genoa and Milano (Italy), • Twente University (The Netherlands) • Wroclaw University of Technology (Poland).

  23. NED Status: Conductor • Contracts for the Nb3Sn conductor development (aiming at a non-Cu JC of 1500 A/mm2 at 4.2 K and 15 T) have been awarded last fall to Alstom/MSA in France and SMI in the Netherlands. • The first rounds of R&D wires are expected in the oncoming month. • The final conductors should be produced by the end of 2006.

  24. GHe LHe Pumping Cryogenic vessel Heat exchanger piping Insert Heat exchanger Expansion valve He I Radiation shields He IIp Experimental volume He IIs Vacuum container NED Status: Insulation • The insulation characterization task includes heat transfer measurements in He-II environment. • To perform these measurements, a new double-bath cryostat has been designed by CEA and built in Poland under Wroclaw University supervision. • The cryostat will be delivered to CEA mid-September. NED Cryostat Design (Courtesy B. Baudouy, CEA) Elements of NED Cryostat (Courtesy M. Chorowski, WUT)

  25. NED Status: Design Studies • Several magnet configurations are being compared so as to determine which one is the most efficient in terms of manufacturability, performance and costs. Coslayer design (courtesy D. Leroy, CERN) Block design (courtesy H. Felice, CEA) Motor-type design (courtesy F. Toral, CIEMAT)

  26. NED Outlook • The NED collaboration is working hard at finding the money to complete the R&D program and build the proposed model magnet.

  27. Conclusion • Superconducting NbTi magnets have been used successfully in particle accelerators for close to 25 years. • The LHC magnet R&D program has demonstrated that the performance limits of NbTi have been achieved and that to go beyond we need to switch to Nb3Sn. • The US-LARP and the EU NED JRA are assessing the feasibility of accelerator-class Nb3Sn magnets, so as to open new ranges of options for LHC-IR upgrade and ILC IR’s. • Bringing a new technology to maturity is always a challenge that requires dedicated resources; let us hope that both programs will be given the opportunity to achieve their goals in a timely manner.