Progressive failure of laminates

Progressive failure of laminates. After first-ply failure, the stiffness of failed plies is degraded. A conservative approach is to set their stiffness very low. A less conservative approach is to degrade stiffness based on the type of failure. Fiber failure would degrade E 1

dannon
Télécharger la présentation

Progressive failure of laminates

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Progressive failure of laminates • After first-ply failure, the stiffness of failed plies is degraded. • A conservative approach is to set their stiffness very low. • A less conservative approach is to degrade stiffness based on the type of failure. • Fiber failure would degrade E1 • Matrix failure would degrade E2and G12

  2. Example 6.3.2 • Calculate the ultimate x-load that a graphite-epoxy laminate can carry. • What is another way to define the laminate? • Use max-strain criterion • Elastic properties , t=0.25mm • Strength • Which part of the data is not needed?

  3. Missing preliminaries • Same material was used in Example 2.4.1 where we obtained • This is also the Q for the 0-deg plies. For 90-deg what do we get? • Altogether

  4. First-ply failure • Laminate strains • Strain limits millistrains • Obviously , so failure will be due to 90-plies when . Why? • From second equation we calculate 0.0117 millistrain • Then from first equation

  5. What happens if we throw away the 90 plies? • Thickness will reduce to 1.5mm. • First-ply failure load is • This would also be the ultimate failure load of our laminate. • Textbook carries on a more complex calculation based on the assumption that the strain will remain the same when the 90’s fail.