An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Training at Stockholm University (2007 09 12 - 10 02) Martynas Lelis

  2. Contents • Background • Objectives and tasks of the visit • Measurements at SU • Equipment • Results • Discussions

  3. Background • In latter years in LEI there were experiments of formation of Mg2Ni alloys and their hydrogenation to Mg2NiH4 • There are three phases of Mg2NiH4 – LT1, LT2 (with microtwining) and HT • At ~235° C LT transforms to HT

  4. Background • Initial investigation of Mg2NiH4 samples prepared at LEI seems to be pseudo cubic HT phase (even at room temperatures) • Moreover, it exhibits unusual stability

  5. Objectives and tasks • Objective • To acquire new skills and better understanding in analyzing and characterization of hydrogen storage materials

  6. Objectives and tasks • Tasks • to learn the working principles of Differential scanning colorimeter (DSC) and spectrophotometer • to prepare and to measure samples from LEI • to analyze the results and to make conclusions

  7. Measurements at SU - equipment • Differential scanning calorimetry or DSC is a thermoanalytical technique in which the difference in the amount of heat required to increase the temperature of a sample and reference are measured as a function of temperature.

  8. Measurements at SU - equipment • The basic principle underlying this technique is that, when the sample undergoes a physical transformation such as phase transitions, more (or less) heat will need to flow to it than the reference to maintain both at the same temperature.

  9. Measurements at SU - equipment Perkin Elmer Pyris 1 • It can be used to find Heat Flow, Melting Temperature, Phase Transition Temperature etc. • Typical sample weights are 5-10mg

  10. Measurements at SU - results

  11. Measurements at SU - results

  12. Discussions

  13. Discussions - XRD

  14. Discussions - XRD • Thin film: • a=6.440 Å • Scratched powders: • a=6.507998 Å • Powder material: • 6.5295 Å

  15. Discussions - TEM D. Noréus, L. Kihlborg, J. Less-Comm. Met. 123 (1986) 233

  16. Discussions - TEM

  17. Discussions – DSC - powder

  18. Discussions – DSC – thin film

  19. Discussion – Band gap

  20. Discussion – Band gap

  21. Discussion - model Mg2Ni zones MgO Powder Mg zones Thin film

  22. Conclusions • During the visit to Stockholm university new analytical techniques were successfully learned and employed for sample characterization • Measurement of thin film samples has given some proving evidence (not complete) for the existence of pseudo cubic HT phase of Mg2NiH4