ECE 875: Electronic Devices

ECE 875: Electronic Devices. Prof. Virginia Ayres Electrical & Computer Engineering Michigan State University ayresv@msu.edu. Lecture 10, 03 Feb 14. Chp. 01 Concentrations Nondegenerate Degenerate Nondegenerate Intrinsic Contributed by impurities Wanted impurities: “dopants”

enan
Télécharger la présentation

ECE 875: Electronic Devices

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ECE 875:Electronic Devices Prof. Virginia Ayres Electrical & Computer Engineering Michigan State University ayresv@msu.edu

  2. Lecture 10, 03 Feb 14 • Chp. 01 • Concentrations • Nondegenerate • Degenerate • Nondegenerate • Intrinsic • Contributed by impurities • Wanted impurities: “dopants” • Unwanted impurities: “traps” Concentrations n Effect of temperature VM Ayres, ECE875, S14

  3. Example Pr. 1.12: VM Ayres, ECE875, S14

  4. Example Pr. 1.12: Need this ✔ Use: ✔ VM Ayres, ECE875, S14

  5. General Info: will use figure next slide to do Pr. 1.12: Centripetal force = Coulomb force Average is defined as the harmonic mean not the geometric mean. Used when E-field is present P and B are shallow impurities in Si VM Ayres, ECE875, S14

  6. Tabulated: can get EC – ED @ 300 K from Sze Fig 10 (useful): For P in Si: EC – ED = 0.046 eV This is the “ionization energy” Pr. 1.12: Given: ionization energy doesn’t change as a function of T VM Ayres, ECE875, S14

  7. Have: EC – ED Need: EF – ED Note: (EC – ED) – (EC – EF) = EF – ED Given: ND = 1016 cm-3 = nondegenerate in Si Therefore: use Sze (21): Need: NC @ 77K In App G: NC @ 300K = 2.8 x 1019 cm-3 VM Ayres, ECE875, S14

  8. Use the ratio to something you know method: 2 VM Ayres, ECE875, S14

  9. VM Ayres, ECE875, S14

  10. Also: kT at 77K: Plug and chug method: OR Ratio to something you know method: VM Ayres, ECE875, S14

  11. ✔ @ 77K = 3.64 X 1018 cm-3 Thus far: Sze (21): Problem: n ≠ ND+ = 1016 cm-3 at 77K because not all ND are ionized VM Ayres, ECE875, S14

  12. VM Ayres, ECE875, S14

  13. VM Ayres, ECE875, S14

  14. Important part: NOT EQUAL VM Ayres, ECE875, S14

  15. Important step: COMPARE: VM Ayres, ECE875, S14

  16. Lecture 10, 03 Feb 14 • Chp. 01 • Concentrations • Nondegenerate • Degenerate • Nondegenerate • Intrinsic • Contributed by impurities • Wanted impurities: “dopants” • Unwanted impurities: “traps” Concentrations n Effect of temperature VM Ayres, ECE875, S14

  17. Summary: concentration as a function of temperature and doping:For: nondegenerate doping (n-type Si shown in figure): VM Ayres, ECE875, S14

  18. Summary: Freeze-out range: concentration  partially ionized dopants: DONORS: Neutral ND Electron occupies a local energy level ED, h = 1, gD = 2 Ionized ND+ A local energy level ED is empty and available ACCEPTORS: Neutral NA A local energy level EA is empty and available Ionized NA- Electron occupies a local energy level EA, h = 1, gA = 4 F(E) is probability of an electron occupying an energy level E. If energy level E = local level ED (neutral ND) or local level EA (ionized NA-) use: VM Ayres, ECE875, S14

  19. Summary: Intrinsic range: concentration  partially ionized dopants: n ≈ p ≈ VM Ayres, ECE875, S14

  20. Summary: Saturation range: concentration  fully ionized dopants AND some probability of valence-to-conduction band transitions: Fully ionized dopants: single doping: n-type: p = ni2/n, solve quadratic for n p-type: n = ni2/p, solve quadratic for p VM Ayres, ECE875, S14

  21. Summary: Intrinsic range: concentration  fully ionized dopants AND high probability of valence-to-conduction band transitions: n ≈ pi = ni VM Ayres, ECE875, S14

  22. Summary: For all ranges: Egap = f(T); also f(P): VM Ayres, ECE875, S14

  23. Fig. 14: (a) Silicon; (b – not shown: GaAs) VM Ayres, ECE875, S14

  24. Example: Sun-side for a LEO (low-earth orbit) satellite is 200oC = 473 K. What doping concentrations can’t be used in Si electronics because all pn junctions will act like intrinsic Si, causing device inoperability? VM Ayres, ECE875, S14

  25. 473 K Answer: n and p doping concentrations 1013 cm-3 and below can’t be used. VM Ayres, ECE875, S14

  26. Lecture 10, 03 Feb 14 • Chp. 01 • Concentrations • Nondegenerate • Degenerate • Nondegenerate • Intrinsic • Contributed by impurities • Wanted impurities: “dopants” • Shallow dopants • Deep level dopants • Unwanted impurities: “traps” Concentrations n Effect of temperature VM Ayres, ECE875, S14

  27. Donors and acceptors don’t have to be “shallow”. Many atoms can get into Si: reason for cleanrooms VM Ayres, ECE875, S14

  28. How to read graph: DONORS: Neutral ND Electron occupies a local energy level ED, h = 1, gD = 2 Ionized ND+ A local energy level ED is empty and available ACCEPTORS: Neutral NA A local energy level EA is empty and available Ionized NA- Electron occupies a local energy level EA, h = 1, gA = 4 Above Ei: read EC – ED Below EI: read EA - EV Generally for single substitutional impurities: Donor Levels/two charge states: ED (neutral 0, positive +1) Acceptor levels/two charge states: EA (neutral 0, negative -1)

  29. Can have donor levels below Ei and acceptor levels above Ei: VM Ayres, ECE875, S14

  30. Pr. 1.16 (a): gold dopant/impurity: Au: The acceptor level at EA-0.54 has two charge states: neutral 0 to start and -1 if it gets an e-. The donor level at ED-0.29 has two charge states: neutral 0 to start and +1 if it loses an e- At start: “state of charge of the Au levels in Si”: EA-.54 = neutral 0 ED-.29 = neutral 0 VM Ayres, ECE875, S14

  31. Pr. 1.16 (a): Add neutral B to Au dopant/impurity: The acceptor level at EA-0.54 has two charge states: neutral 0 to start and -1 if it gets an e-. The donor level at ED-0.29 has two charge states: neutral 0 to start and +1 if it loses an e- The acceptor level at EA-0.044 has two charge states: neutral 0 to start and -1 if it gets an e-. It does get e- from the ED-0.29 donor level. VM Ayres, ECE875, S14

  32. Pr. 1.16 (a): After neutral B addition to Si with Au dopant/impurities: The acceptor level at EA-0.54 is neutral 0 at start and WHAT at finish The donor level at ED-0.29 is neutral 0 at start and WHAT at finish The acceptor level at EA-0.44 is neutral 0 at start and WHAT at finish Neutrality is maintained overall. VM Ayres, ECE875, S14

  33. Pr. 1.16 (b): effect of Au impurities on electron concentration n and hole concentration p, both from Si: Consider what the acceptor level at EA-0.54 can do with n from Si Consider what he donor level at ED-0.29 can do with p in Si Result: Si e- and holes that would have participated in current I are both being tied up (“trapped”) instead by the Au impurity levels. They are NOT contributing to current I while they are in traps. VM Ayres, ECE875, S14

  34. Effect on currents: 1.5.4: Will show: recombination and generation due to deep level dopants has greatest effect on ordinary current Ordinary current: Current I is in an assumed pn junction device VM Ayres, ECE875, S14

  35. 1.5.4: Rate U is related to current I: VM Ayres, ECE875, S14

  36. What is U: Net transition rate driven by powerful pn = ni2 at thermal equilibrium Fig 25 (a) matches Fig. 4 (b) Note: Recombining e- must have a momentum value that matches the crystal momentum of the hole it is dropping into. Direct bandgap = OK all the way to the valence band Recombination with emission of photon Has a rate Re Generation with creation of e- hole pair Has a rate Gthermal VM Ayres, ECE875, S14

  37. What is U: Net transition rate driven by powerful pn = ni2 at thermal equilibrium Fig 25 (a) matches Fig. 4 (b) Recombination decreases both n and p by 1 Now: pn < ni2 Think: what if just recombination kept going? VM Ayres, ECE875, S14

  38. What is U: Net transition rate driven by powerful pn = ni2 at thermal equilibrium VM Ayres, ECE875, S14

  39. What is U: Net transition rate driven by powerful pn = ni2 at thermal equilibrium Fig 25 (a) matches Fig. 4 (b) Recombination rate Re depends on having: - Concentration of electrons in EC, - Concentration of holes in EV to take the e- - Probability of spontaneous recombination Rec Therefore: Re = Rec np = Rec ni2 VM Ayres, ECE875, S14

  40. What is U: Net transition rate driven by powerful pn = ni2 at thermal equilibrium VM Ayres, ECE875, S14

  41. What is U: Net transition rate driven by powerful pn = ni2 at thermal equilibrium General: Specific: pn junction VM Ayres, ECE875, S14

  42. Evaluate U: within 1 diffusion length of the junction on the n-side of a pn junction: VM Ayres, ECE875, S14

  43. Within 1 diffusion length Lp of the junction on the n-side of a pn junction: Review: For a pn junction with low level injection Dp on n-side and Dn on p-side: pp0 ≈ NA- nn0 ≈ ND+ pn0 ≈ ni2/n=ND+ Lp np0 ≈ ni2/p=NA- Ln excess holes: Dp electrons: Dn VM Ayres, ECE875, S14