耐电弧测定

耐电弧测定. 耐电弧测定. 定义与方法原理 耐电弧性 在规定的试验条件下，绝缘材料耐受沿着它的表面电弧作用的能力。通常用电弧焰在材料表面引起碳化至表面导电所需的时间表示。 方法原理 借助高压小电流或低压大电流在两电极间产生的电弧，作用于材料表面使其产生导电层。其测试原理如图所示。线路最大可产生 40mA 的连续电流. 方法要点. 试样 板状试样厚度 2 — 4mm 、长宽皆为 100mm ；测漆膜时，应将漆膜涂在 3240 环氧酚醛玻璃布板上，漆膜厚 0.10 — 0.12mm 。

erasmus-karsten
Télécharger la présentation

耐电弧测定

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 耐电弧测定

  2. 耐电弧测定 定义与方法原理 • 耐电弧性 在规定的试验条件下，绝缘材料耐受沿着它的表面电弧作用的能力。通常用电弧焰在材料表面引起碳化至表面导电所需的时间表示。 • 方法原理 借助高压小电流或低压大电流在两电极间产生的电弧，作用于材料表面使其产生导电层。其测试原理如图所示。线路最大可产生40mA的连续电流

  3. 方法要点 • 试样 板状试样厚度2—4mm、长宽皆为100mm；测漆膜时，应将漆膜涂在3240环氧酚醛玻璃布板上，漆膜厚0.10—0.12mm。 • 电极 电极用没有龟裂和损伤的钨棒制成,电极的一端要磨成一个相对轴线成30º角的椭圆面。 电极应处在与试样面相垂直的平面内，和水平面间夹角为35º，电极椭圆面短轴应水平,且对着样品，两电极尖端间距离为6.0土0.1mm

  4. 操作要点 • 耐电弧试验大致分两类，一类是低压大电流．一类是高压小电流。塑料材料较多采用高压小电流。 • 将试样与电极接于线路，将工频高压小电流接于两电极间产生电弧，起初间歇作用于材料表面。通过电弧间歇时间逐步缩短、电流逐渐加大的方式，使材料经受逐渐严酷的燃烧条件，直至使试样破坏。从而分辨出材料的耐电弧性能。记录自电弧产生直至材料破坏所经过的时间

  5. 破坏的判定原则 （1）在材料表面上，两电极间产生了细线状的导电通路，此时电弧声音明显变化，弧光发亮，电弧立即熄灭； （2）由于材料表面产生了足够的碳而形成了导电通路； （3）有些有机绝缘材料电弧作用呈火焰状，在材料表面虽没有形成明显的导电通路，但应认为已破坏； （4）有些材料在电弧作用下，产生龟裂而破坏。注意:本方法不宜不能使材料表面形成破坏的材料