1 / 28

Cooperation: Prof. Dr. J. Kortus

Cooperation: Prof. Dr. J. Kortus. Cooperation: Prof. Dr. H.J. Seifert. Thermodynamics and Kinetics of Processes of the Intercalation/De-Intercalation in Submicron Particles of Cathode Li-ions Batteries. С.Н. Поляков. World production.

fineen
Télécharger la présentation

Cooperation: Prof. Dr. J. Kortus

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Cooperation: Prof. Dr. J. Kortus Cooperation: Prof. Dr. H.J. Seifert Thermodynamics and Kinetics of Processes of the Intercalation/De-Intercalation in Submicron Particles of Cathode Li-ions Batteries С.Н. Поляков S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  2. World production S.N. Polyakov, J. Kortus, H.J. SeifertМГТУ им.Баумана, 26-28 января, 2011, Москва

  3. Lithium-ion batteryCathodes S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  4. Comparison of the gravimetric and volumetric energy densities of various rechargeable battery systems* *)A. Manthiram, Lithium batteries, Edited by Gholam-Abbas Nazri, USA, Springer, 2009. S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  5. Schematic illustration of the charge/discharge in lithium-ion cell Li O c Li Mn Charge (de-intercalation) Discharge (intercalation) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  6. Problem of the cyclability (Material degradation) Cycling crumbling (chemical corrosion) [**] Crack after cycling [*] Optimal distribution of size of the cathode particles [*] J. of Power Sources 140 (2005) 125-128 [**] J. of Power Sources 143 (2005) 203-211 [***] Solid State Ionics 167 (2004) 237-242 Cyclability data for LiMn2O4 cathode[***] S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  7. ThermodynamicLarch-Cahn-Theory (1) Maxwell’s relations The chemical strain tenzor for cubic symmetry (2) (3) For small deformations Partial molar volume of Li in the host lattice Cubic cell LiMn2O4 (4) - hydrostatic stress S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  8. Kinetics of the Li-ion in Electrode Porous electrode Li-ion flux density, Onsager Theory Particle Binder - Li-ion mobility Electrolyte Li-ion mobility, Larch-Cahn-Theory Kinetic model for one particle (5) (6) (7) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  9. DiffusionSpherical particle (8) (9) The Butler-Volmer equation (10) - exchange flux density S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  10. Open-circuit potential Experiment [*] Calphad-Method [**] (11) [**] J. Electrochem. Soc., 143, 1890 (1996) [*] Solid State Ionics, 69 (1994) 59. S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  11. Intercalation/De-Intercalation stressin a spherical particle Charge (contraction/expansion) (12) (13) Discharge (expansion/contraction) (14) E - elastic modulus - Poisson’s ratio S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  12. Analysis of the diffusion by stresses in a spherical particle (18) (15) (16) (17) (5) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  13. Numerical procedure (19) (20) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  14. Material properties of LiMn2O4 and parameters for the lithium intercalation reaction OCP Deintercalation Intercalation S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  15. Stress and Li-concentration Intercalation Deintercalation S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  16. Hydrostatic stress (deintercalation/intercalation) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  17. Hydrostatic stress (deintercalation/intercalation) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  18. Stress in a submicron particle (21) (22) (23) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  19. Stress in a 10μm particle S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  20. Hydrostatic stress in a particle r = 10μm (deintercalation, v = 1 μV/s) Dangerous zone Deintercalation Intercalation S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  21. Extreme values of hydrostatic stresses on the particle surface[*] Hydrostatic stress for various scan ratesin a particle of 2 μm radius Deintercalation Intercalation [* ]С. Н. Поляков, ПЖТФ, 2010, Vol. 36, No. 24, pp. 25–32. S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  22. Numerical simulation (diffusion) Deintercalation Intercalation S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  23. Numerical simulation (current density) Deintercalation Intercalation S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  24. Analysis of the current density in submicron particles (24) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  25. Current density in submicron particles (25) S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  26. Current density in submicron particles S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow

  27. Conclusions • Equations for calculating kinetics of mechanical stresses in submicron particles were derived. • The Li-ion current density dependence of the particle size and of the ID rate was obtained for a cathode material. • A kinetic equation for the current density in the absence of diffusion polarization was derived; it was shown that diffusion polarization decreased for submicron particles. • The influence of a particle size on the maximum Li-ion current density was evaluated. S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow The effect of stresses and deformations in a cathode material (LiMn2O4) is taken into account using the Larche–Cahn thermo-chemical theory.

  28. I thank you for your attention Большое спасибо за внимание! S.N. Polyakov, J. Kortus, H.J. Seifert Bauman MHTU, January 26-28, 2011, Moscow