An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Chem-Trend Nordic Gert Nielsen Chem-Trend Europe RCR Industry Meeting 2010 February 2010

  2. I investigated: • Which possible customers are there still to gain in the Windturbine industry?(Blade, Nacelles, Moulds ect.) • And what are the potential for each possible customer?

  3. How do they produce parts? • All Nacelles and small blades is produced with double mould + vacuum injectionThis method is used by approximately 80% of the previous mentioned customers.

  4. The largest problem for these customers • The lagest problems for these customers was Styren build-up, sticking and mat surface. Styren build-up Sticking Mat surface

  5. With what product can we solve these problems...... • .... And gain these customers? • Product for the Male mould • CL 712 EZ • CL 15 EZ • CL 75 • Product for the Female mould (Gelcoate side) • CL 15 EZ • CL 2172

  6. How to solve the problems • Did a Start-up test with fine results and established a n application guide.(See the following slides)

  7. Guide - Internal environment • Equipment

  8. Guide - Cleaning the Mould with Mould Cleaner EZ • Clean 2 times with clean cotton cloths

  9. Guide - Polishing the mould • Secure the best base

  10. Guide - Cleaning mould with Mould Cleaner EZ • Clean 2 times with clean cotton cloth

  11. Guide - Sealing the Mould with Chemlease 15 EZ • Apply 2 layers (wipe on/wipe of)

  12. Guide - Sealing the Mould with Chemlease 15 EZ • Drying time between layers is 15 minutes • Drying time after final layer is 1 hour

  13. Guide - Apply Release Agents Chemlease 2172 • Apply 5 layers with 15 minutes between layer • Drying time after final layer is 1 hour

  14. Guide - Flance Wax 5141 • Apply 1 layer after each de-molding

  15. Guide - Cleaning the male mould • Clean 2 times with Mould Cleaner EZ

  16. Guide - Polishing male mould • Check that the mould is clean

  17. Guide - Clean the mould • Clean 2 times with Mould Cleaner EZ

  18. Guide - Priming the male mould with CL 712EZ • Apply 1 thick layer wipe on and let it dry in 1,5 – 2 hours

  19. Guide - Sealing the Male mould with CL 15 EZ • Apply 2 layers (wipe on/wipe of) • Drying time between layers is 15 minutes

  20. Guide - Sealing the Male mould with CL 15 EZ • Drying time after final layer is 1 hour

  21. Guide - Apply Release agent Chemlease 75 • Apply 4 layers wipe on/of with 15 minutes between layers • Drying time after final layer is 1 hour

  22. Guide - Flance Wax Chemlease 5141 • Apply 1 layer after each de-molding

  23. Test at Danplastas • Test showed improvements against ZYWAX! With ZYWAX system:Styren build-up after 5-10 demouldings. With Chem-Trend system:NO styren build-up after 65 demouldings!!!!