3. THE GLASS STATE AND THE GLASS TRANSITION : THERMODYNAMIC and KINETIC ASPECTS

3. THE GLASS STATE AND THE GLASS TRANSITION : THERMODYNAMIC and KINETIC ASPECTS. Differential Scanning Calorimetry. Differential Thermal Analysis. Is the glass transition a true thermodynamic phase transition ?.  T g depends on the cooling rate

judah
Télécharger la présentation

3. THE GLASS STATE AND THE GLASS TRANSITION : THERMODYNAMIC and KINETIC ASPECTS

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 3. THE GLASS STATE AND THE GLASS TRANSITION: THERMODYNAMIC and KINETIC ASPECTS

  2. Differential Scanning Calorimetry Differential Thermal Analysis

  3. Is the glass transition a true • thermodynamic phase transition ?  Tg depends on the cooling rate  Tg depends on the thermal history

  4. Ehrenfest relations Prigogine-Defay ratio must be = 1 if it were a phase transition with a single order parameter

  5. sub-Tg aging and annealing Tanneal .

  6. using Differential Scanning Calorimetry (DSC, TMDSC…) [J. M. Hutchinson, Thermochimica Acta 324 (1998) 165-174

  7. using Differential Scanning Calorimetry

  8. the fictive temperature Tf B2O3

  9. the fictive temperature Tf Ethanol

  10. the fictive temperature Tf  phenomenological Tool-Narayanaswamy-Moynihan (TNM) approach [ Tool, J. Am. Ceram. Soc. 29 (1946) 240. Narayanaswamy, J. Am. Ceram. Soc. 54 (1971) 491. Moynihan et al., J. Am. Ceram. Soc. 59 (1976) 12. ] • curve fitting method: • [I. M. Hodge, J. Non-Cryst. Solids 169 (1994) 211]

  11. THE KAUZMANN PARADOX EXCESS OF ENTROPY: TK

  12. W. Kauzmann, Chem. Rev.43, 219 (1948)

  13. THE KAUZMANN PARADOXNN 1.0

  14. STRONG AND FRAGILE GLASS-FORMING LIQUIDS 0 1

  15. Vogel-Tamman-Fulcher equation: (D: strength) fragility index m:

  16. STRONG AND FRAGILE GLASS-FORMING LIQUIDS C. A. Angell, J. Non-Cryst. Solids 102, 205 (1988)

  17. [I. Chang and H. Sillescu] Ecuación de Stokes-Einstein: [A. Einstein, Annalen der Physik 17, 549 (1905)]