Novel Ultra-High Straining Process for Bulk Materials—Development of the Accumulative Roll-Bonding (ARB) Process

Novel Ultra-High Straining Process for Bulk Materials—Development of the Accumulative Roll-Bonding (ARB) Process. Authored by Y. Saito, H. Utsunomiya, N. Tsuji, T. Sakai Presented by Chris Reeve September 13, 2004. Outline. Introduction Model Design Application Experimental Procedure

kaylee
Télécharger la présentation

Novel Ultra-High Straining Process for Bulk Materials—Development of the Accumulative Roll-Bonding (ARB) Process

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Novel Ultra-High Straining Process for Bulk Materials—Development of the Accumulative Roll-Bonding (ARB) Process Authored by Y. Saito, H. Utsunomiya, N. Tsuji, T. Sakai Presented by Chris Reeve September 13, 2004

  2. Outline • Introduction • Model • Design Application • Experimental Procedure • Results • Conclusion • Questions

  3. Introduction • Why is Accumulative Roll-Bonding important? • Ultra-fine grain materials exhibit desirable properties • High strength at ambient temperatures • High-speed superplastic deformation at elevated temperatures • High corrosion resistance • Commonly accomplished by intense plastic straining

  4. Introduction • Processes used such as cyclic extrusion compression have two main drawbacks • Requires large load capabilities, expensive dies • Low production rate limits economic viability • Function of paper is to introduce Accumulative Roll-Bonding (ARB) as a bulk manufacturing process

  5. Introduction • References: • 1. Richert, J. and Richert, M., Aluminum, 1986, 62, 604 • 2. Valiev, R. Z., Krasilnikov, N. A. and Tsenev, N. K., Mater. Sci. Engng, 1991, A137, 35. • 3. Horita, Z., Smith, D. J., Furukawa, M., Nemoto, M., Valiev, R. Z. and Langdon, T. G., J. Mater. Res., 1996, 11, 1880. • 4. Saito, Y., Utsunomiya, H., Tsuji, N. and Sakai, T., Japanese Patent applied for. • 5. Nicholas, M. G. and Milner, D. R., Br. Weld. J., 1961, 8, 375. • 6. Helmi, A. and Alexander, J.M., J. Iron Steel Inst., 1968, 206, 1110. • 7. Metals Handbook, 9th edn, Vol. 2. American Society for Metals, Metals Park, OH, 1979, pp. 65-66. • 8. Sakai, T., Saito, Y., Hirano, K. and Kato, K., Trans. ISIJ, 1988, 28, 1028. • 9. Saito, Y., Tsuji, N., Utsunomiya, H., Sakai, T. and Hong, R. G., Scripta mater., 1998, 39, 1221. • 10. Tylecote, R. F., The Solid Phase Welding of Metals. Edward Arnold, London, 1968.

  6. Model • Principle • Rolling bond surfaces together • Refines microstructure • Improves properties. • Iterative process • Process design steps • Surface treatment • Stacking • Roll bonding (heating) • Cutting

  7. Model • Important parameters: t, tn, n, ε, rt • For reduction of 50% in a pass • Thickness after n cycles • t = t0 / 2n • Total reduction after n cycles • rt = 1 – t / t0 = 1 – 1 / 2n • Equivalent plastic strain

  8. Design Application

  9. Experimental Procedure • No “special” equipment needed! • Three alloys chosen • Al 1100 (commercially pure) • Al 5083 (Al-Mg alloy) • Ti-added interstitial free (IF) steel • Surfaces degreased, brushed • Strips were heated • 50 % reduction rolling under dry conditions

  10. Experimental Procedure

  11. Results

  12. Results • Expected that grain refinement: • Improves mechanical properties related to strength • Decreased % elongation in direction of roll-bonding • The number of cycles required to obtain peak strength can only be determined experimentally

  13. Results

  14. Conclusions • Practical industrial use for high strength structural applications • Advances rolling technology by application to a specific materials processing method • Industries most impacted: construction, marine, aerospace, automotive