The Breaking of Glass

The Breaking of Glass. Strobe 6: Friday 10am–1pm strobe6@mit.edu Adam Seering aseering@mit.edu Aubrey Tatarowicz altat@mit.edu Daniel Hernandez djh@mit.edu John Hawkinson jhawk@mit.edu. Strobe 6 Final Project. We want to characterize how glass breaks.

leann
Télécharger la présentation

The Breaking of Glass

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. The Breaking of Glass Strobe 6: Friday 10am–1pmstrobe6@mit.edu Adam Seering aseering@mit.edu Aubrey Tatarowicz altat@mit.edu Daniel Hernandez djh@mit.edu John Hawkinson jhawk@mit.edu Strobe 6 Final Project

  2. We want to characterize how glass breaks. • Does glass deform when impacted? • How does it deform? • Can we measure deformation? • After impact, how do the cracks form? • Can we measure crack formation speeds? • In what directions do cracks form?

  3. Basic HSV Setup

  4. A look at the Grid and Diffuser

  5. Edge Illumination for Viewing Cracks

  6. Results for Crack Formation Phantom. 50 mm lens. 75,000fps. aperture = f/1.8. 4 pumps on BB gun.

  7. Analysis of Crack Formation

  8. Data Points Collected Collected data in pixels and used the following to convert to mm: 178 pixels = 25mm

  9. Calculating Crack Formation Velocity from Data • Crack 5: • 36 mm x 75,000fps = 2.7 x 106 mm/s = 2700 m/s • Fastest Recorded Crack Speed: • 46mm x 75,000fps = 3.45 x 106 mm/s = 3450 m/s.