1 / 22

PVC : the long term building material

PVC : the long term building material. Joël Fumire Research & Technology SBU Vinyls . São Paulo, 2005. PVC in building. PVC is one of the most used plastics in building Why ?. PVC in building. Building means … … Strength , see the rigidity modulus !

lycoris
Télécharger la présentation

PVC : the long term building material

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. PVC : the long term building material Joël Fumire Research & Technology SBU Vinyls São Paulo, 2005

  2. PVC in building • PVC is one of the most used plastics in building Why ?

  3. PVC in building Building means … • … Strength , see the rigidity modulus ! • … weather resistance in all climates • … well adapted to specific use (e.g. pipes) • … Durability from 30 to > 100 years • … competitive cost ! • … recyclable

  4. Comparison E Modulus

  5. Rigidity in Sewage Key property : annular stiffness. Directly related to the E-modulus of the material : Stiffness : SN = K. E. I / D3

  6. Good Weathering resistance UV-resistance : PVC can be formulated easily to be used on a long term basis in very sunny climates

  7. PVC adapted for use : drinking water pipes Key properties : • Pressure resistance • No modification of the water quality • Long term durability

  8. PVC adapted for drinking water pipes Key property : long term pressure resistance PVC-U PE100 50 y.

  9. PVC adapted for drinking water pipes No modification of water quality : • No significant leaching of substances to the water • No taste or smell transferred to water • PVC pipes comply with the requests of drinking water contact in the most severe regulations (CEE, NSF, BGVV, etc…) • Excellent resistance to bacteria growth • PVC is approved for drinking water transportation in the majority of countries

  10. Other key properties for PVC pipes • Chemical inertia towards many chemicals : • Cleaning liquids, acids, • No sensitivity towards oxidising substances • Good Fire resistance • Among plastics, PVC is one of the most difficult to ignite. • It is self-extinguishing

  11. Durability • PVC pressure pipes are in use since more than 60 years • PVC pressure pipes are designed theoretically for 50 years but can last more than 100 years • PVC Window profiles are used since more than 40 years and are still performing well

  12. Pressure pipes 60 years old – Dr Nowack study • Study realised in Germany : published in KRV (1995) by Dr. Nowack • PVC pipes were produced and installed in Bitterfeld in 1935-1940 with the technology available at that moment (physical, chemical) Pipes from 1938 extracted from Bitterfeld

  13. Pressure pipes 60 years old – Dr Nowack study • Tests on these pipes show that : • Burst-pressure curve is still linear with no "knee" • Burst-pressure at 60°C is found still > 5 N/mm² after 600 h • Some of the pipes are still operating today at 20°C under 5.0 bar with satisfactory performance

  14. TNO study on residual lifetime of PVC pipes • Are 50 years old pipes to be replaced ? • Study was realised between 2002 and 2005 by the Dutch institute TNO Science and Industry(A. Boersma & J. Breen) • Water pipes from the 1950's until today were excavated and extensively tested :

  15. TNO study on residual lifetime of PVC pipes • Physico-chemical analysis : • The K values were close to 66 (1 exception at 72) • The level of gelation was between 38% and 80% (the pipes from the 1970's showed the lowest gelation) • Analysis of the transformation of the stabiliser system indicates negligible consumption (at room temperature)

  16. Mechanical testing : Craze initiation is affected by the physical ageing and by fatigue phenomenon Burst pressures are still at a good level (and still compliant to ISO standard) TNO study on residual lifetime of PVC pipes

  17. TNO study on residual lifetime of PVC pipes • Main conclusions of this study are : • No chemical degradation appears • Gelation : seems to be correlated with craze initiation • Fatigue could lead to an increased mechanical ageing • Production and laying conditions induce additional stresses in the material • The lifetime can be expected to be 100 years or more for high quality produced and installed pipes.

  18. Window frames since the 1970's • Window frames are installed since the 1960's • This window was installed in Germany in1972 • and is still in operation after more than 30 years of good operation! • Usually PVC frames are not replaced because of damage

  19. Competitive price : costs of piping systems (installation and assembling) Steel Cast Iron Cast Iron PE Steel Cast Iron PVC-U Steel PE PVC-U PE PVC-U Source : DVGW 1998 DN 100 DN 200 DN 150

  20. Recycling • Today in Europe > 7 000 t/y of PVC is recycled in pipes • For homogeneous rigid PVC, recycling is mainly a collecting process • For composite material (or heavily contaminated PVC) a special separation process has been developped :

  21. Recycling • PVC material can be extruded several times • The problem is the availability of recycled material since the articles installed in the 1970's are not available for recycling !

  22. Thank you for your attention !