本周工作： 一 . mPEG-LA/CL(4:6,2:8,3:7,5:5 ） -COOH 样品纯化

本周工作： 一 . mPEG-LA/CL(4:6,2:8,3:7,5:5 ） -COOH 样品纯化 二 . mPEG-LA/CL(4:6,2:8,3:7,5:5 ） - COOH-PEI(1800/600) 的 合成及其处理 三 . 纳米粒的制备及表征. LA:CL=4 ： 6 PEG: 丁二酸 =45:1.8. LA:CL=2 ： 8 PEG: 丁二酸 =45:1.8. LA:CL=3 ： 7 PEG: 丁二酸 =45:2.7. LA:CL=5 ： 5 PEG: 丁二酸 =45:1.8. 三 .

may-ratliff
Télécharger la présentation

本周工作： 一 . mPEG-LA/CL(4:6,2:8,3:7,5:5 ） -COOH 样品纯化

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 本周工作： 一.mPEG-LA/CL(4:6,2:8,3:7,5:5）-COOH样品纯化 二.mPEG-LA/CL(4:6,2:8,3:7,5:5）-COOH-PEI(1800/600)的合成及其处理 三.纳米粒的制备及表征

  2. LA:CL=4：6 PEG:丁二酸=45:1.8

  3. LA:CL=2：8 PEG:丁二酸=45:1.8

  4. LA:CL=3：7 PEG:丁二酸=45:2.7

  5. LA:CL=5：5 PEG:丁二酸=45:1.8

  6. 三. 羧基纯化好以后连接PEI的产品不粘了，是白色粉末，放置几天吸水也不明显，但是溶解性还是不行，在氯仿和甲醇里微溶，DMF中的溶解性也不是很好，只在DMSO中很好溶解。 将连接PEI的样品在DMSO中配置成1mg/mL和2mg/mL的溶液，用水向其中滴加制备纳米粒，等溶液变浑浊的一刹那间停止滴加，将胶束溶液在二次水中透析，使纳米粒趋于稳定。

  7. 浓度：1mg/mL 平均尺寸：218.5 nm PDI:0.262 浓度：2mg/mL 平均尺寸：340 nm PDI:0.325 结果可能有些不准确，测试条件选择的是水，但是透析时间较短，有DMSO残留。 但也可以看出纳米粒还是较大，应该再仔细控制胶束形成过程。

  8. 下一步工作 继续攻破连接PEI的工作，增加其表征手段。两方面努力： 1.精确调整加入PEI比例，使之既不交联，又不过量太多，减少后期提纯过程。 2.准确精细制备纳米粒，通过对比聚合物连接PEI前后表面zeta电位变化情况 增加对PEI的表征。