NTP 334.088: 1999. CEMENTOS. Aditivos químicos en pastas, morteros y hormigón (concreto). Especificaciones. CONTENIDO: MÉTODOS DE ENSAYO. ING. VANNA GUFFANTI. MÉTODOS DE ENSAYO 11. MATERIALES 11.1 CEMENTO El propuesto para una obra específica,

naasir
Télécharger la présentation

NTP 334.088: 1999

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. NTP 334.088: 1999 CEMENTOS. Aditivos químicos en pastas, morteros y hormigón (concreto). Especificaciones CONTENIDO: MÉTODOS DE ENSAYO ING. VANNA GUFFANTI

  2. MÉTODOS DE ENSAYO • 11. MATERIALES • 11.1 CEMENTO • El propuesto para una obra específica, • Tipo I, o Tipo II ....NTP 334.009 o la • mezcla de dos o más cementos en partes iguales: Cada cemento debe cumplir los requisitos de I y II de la NTP 334.009.

  3. SI CEMENTO DIFERENTE: Y si el contenido de aire en la mezcla sin aditivo es > 3% se deberá seleccionar un cemento o mezcla diferente, para que sea de 3% o menos.

  4. 11.2 AGREGADOS • Cumplir con la NTP 400.037 – SALVEDAD • 11.2.1 GRADACIÓN DEL A. FINO • TAMIZ PORCENTAJE QUE PASA • 4,75 mm (No. 4) 100 • 1,18 mm (No. 16) 65 a 75 • 300 μm (No. 50) 12 a 20 • 150 μm (No. 100) 2 a 5

  5. 11.2.2GRADACIÓN DEL A. GRUESO • RECOMPONER EL MATERIAL SE DEBE • CUMPLIR CON LOS REQUISITOS DEL HUSO No. 57 – NTP 400.037 • HUSO 57 (25,0 mm a 4,75 mm) • SE TENDRÁ CUIDADO CON • LA CARGA Y ENTREGA PARA EVITAR • LA SEGREGACIÓN.

  6. HUSO 57 TAMIZ PORCENTAJE QUE PASA 37,5 mm (1 ½ pulg) 100 25,0 mm (1 pulg) 95 a 100 12,5 mm (1/2 pulg) 25 a 60 4,75 mm (No. 4) 0 a 10 2,36 mm (No. 8) 0 a 5

  7. 11.2.3 A. GRUESO UTILIZADO EN TANDAS DE REFERENCIA (PATRÓN) Y CON ADITIVO SERA EL MISMO. 11.2.4 SE DESCARTA ALGUNA TANDA CUYA MUESTRA NO CUMPLA CON EL TAMAÑO 57 PARA CADA DIMENSIÓN DEL TAMIZ.

  8. SE DESCHECHA CUALQUIER TANDA EN LA CUAL LA MUESTRA SE DESVÍE DEL PROMEDIO EN MÁS DE LA CANTIDAD QUE SE MUESTRA EN LA COLUMNA 3.

  9. (1) (2) (3) TAMIZ PORCENTAJE MÁXIMA VARIACIÓNQUE PASA (1 ½ pulg) 100 00 (1 pulg) 95 a 100 1,0 (1/2 pulg) 25 a 60 1,5 No. 4 0 a 10 4,0 (No. 8) 0 a 5 1,0

  10. 11.3. ADITIVO INCORPORADOR DE AIRE AL EMPLEARSE DEBE PRODUCIR UNA RESISTENCIA SATISFACTORIA AL CONGELAMIENTO Y DESCONGELAMIENTO. 11.4 MATERIALES UTILIZADOS EN ENSAYOS PARA USOS ESPECÍFICOS REPRESENTATIVOS. SE UTILIZARÁN EN LA MISMA FORMA Y TIEMPO Y SECUENCIA TAL COMO SE HARÁ EN OBRA.

  11. SI EL TM DEL AGREGADO GRUESO ES SUPERIOR A 1 PULG, SE DEBERÁ PASAR EL HORMIGÓN POR UN TAMIZ DE 1 PULG ANTES DE ELABORAR LAS MUESTRAS DE ENSAYO.

  12. 11.4.1 OTRAS CONDICIONES DE USO CONDICIONES COMO: HUMEDAD, TEMPERATURA AMBIENTAL, TEMPERATURA DE LOS MATERIALES PUEDEN AFECTAR A LA ADECUACIÓN DE LA MEZCLA, POR LO QUE LOS ENSAYOS SERVIRÍAN DE GUÍA.

  13. 11.5 PREPARACIÓN Y PESAJE: ASTM C 192 12. PROPORCIÓN DE LAS MEZCLAS DE HORMIGÓN 12.1 PROPORCIONES: ACI 211.1. A MENOS QUE SE ESPECIFIQUE DE OTRO MODO, SE INCLUIRÁ EL ADITIVO CON EL PRIMER INCREMENTO DE AGUA DE MEZCLA.

  14. 12.1.1 CONTENIDO DE CEMENTO: 307 kg/m3 ± 3 kg/m3 12.1.2 LA PRIMERA MEZCLA DE PRUEBA DEBERÁ CONTENER LA CANTIDAD DE AGREG. GRUESO DE ACUERDO AL ACI 211.1 PARA TM DEL AGREGADO GRUESO Y EL MF DEL AGREG. FINO.

  15. 12.1.3 PARA MEZCLAS SIN AIRE INCOR- PORADO, EL CONTENIDO DE AIRE AL CALCULAR LAS PROPORCIONES DEBE SER DE 1,5. PARA LAS MEZCLAS CON AIRE INCORPORADO, EL CONTENIDO DE AIRE UTILIZADO DEBERÁ SER DE 5,5...SEGÚN ACI 211.1.

  16. 12.1.4 AJUSTAR ASENTAMIENTO A 3,5 PULG  0,5 PULG. LA TRABAJABILIDAD DE LA MEZCLA SERÁ LA ADECUADA PARA SU COLOCACIÓN MEDIANTE APISONADO A MANO. LA MEZCLA DEBERÁ TENER EL MÍNIMO CONTENIDO DE AGUA POSIBLE.

  17. 12.2 CONDICIONES: PREPARAR LAS MEZCLAS CON Y SIN ADITIVO. EL ADITIVO SE AGREGARÁ COMO LO RECOMIENDE EL FABRICANTE Y EN LA CANTIDAD NECESARIA PARA QUE CUMPLA CON LOS REQUISITOS RESPECTIVOS.

  18. 12.2.1 HORMIGÓN SIN AIRE INCORPORADO EL CONTENIDO DE AIRE EN LA MEZCLA CON ADITIVO Y EL DE REFERENCIA DEBE SER 3 % Y LA DIFERENCIA ENTRE LAS MEZCLAS NO EXCEDERÁ DE 0,5 .

  19. 12.2.2 HORMIGÓN CON AIRE INCORPORADO EL CONT. DE AIRE EN LA MEZCLA CON EL ADITIVO EN EL HORMIGÓN CON AIRE INCORPORADO ESTARÁ ENTRE EL INTERVALO DE 3,5 % A 7,0 % .... EXCEPTO QUE PARA LOS ENSAYOS DE RESISTENCIA AL CONGELAMIENTO Y AL DESCONGELAMIENTO EL INTERVALO ESTARÁ ENTRE 5,0 % A 7,0 %. LA DIFERENCIA ENTRE LAS MEZCLAS DE REFERENCIA Y CON ADITIVO NO EXCEDERÁN DE 0,5.

  20. MEZCLADO • MECÁNICO ... ASTM C 192 • ENSAYOS Y PROPIEDADES DEL HORMIGÓN • FRESCO • 14.1 SE SOMETERÁN A ENSAYO MUESTRAS • DE POR LO MENOS 3 TANDAS DISTINTAS PARA • CADA CONDICIÓN DE HORMIGÓN, DE ACUERDO • A LOS SIGUIENTES MÉTODOS:

  21. 14.2 ASENTAMIENTO: NTP 339.035 14.3 CONTENIDO DE AIRE: NTP 339.083 14.4 TIEMPO DE FRAGUADO: NTP 339.082 CON LA EXCEPCIÓN QUE LA TEMPERATURA DE LOS COMPONENTES DE LA MEZCLA ANTES DEL MEZCLADO Y LA TEMPERATURA DE ALMACENAMIENTO DE LOS ESPECÍMENES DURANTE EL ENSAYO ESTARÁ ENTRE 23,0 °C ± 1,7 °C .

  22. 14.5 CONTENIDO DE AGUA 14.5.1 REGISTRAR LA RELACIÓN A/C CON APROXIMACIÓN DE 0,001. DETERMINAR EL CONTENIDO NETO DE AGUA DE LA TANDA. 14.5.2 CALCULAR EL CONTENIDO RELATIVO DE AGUA DEL HORMIGÓN QUE CONTIENE EL ADITIVO EN ENSAYO.

  23. PREPARACIÓN DE LOS ESPECÍMENES • DE ENSAYO • 15.1 ELABORAR ESPECÍMENES PARA LOS • ENSAYOS DE HORMIGÓN ENDURECIDO, QUE • REPRESENTEN CADA EDAD Y CADA • CONDICIÓN DE HORMIGÓN QUE SE COMPARA. • DE POR LO MENOS 3 TANDAS SEPARADAS • EL NÚMERO MÍNIMO DE ESPECÍMENES DEBE • SER EL INDICADO EN LA TABLA 2. • EL HORMIGÓN DE ENSAYO Y EL DE CONTROL • SERÁN ELABORADOS EL MISMO DÍA.

  24. TABLA No. 2

  25. 15.2 ESPECÍMENES MANIFIESTAMENTE DEFECTUOSOS SE EXAMINA VISUALMENTE ANTES O DURANTE EL ENSAYO, O EN AMBAS ETAPAS. SE DESCARTA SIN ENSAYAR CUALQUIER ESPECIMEN QUE SE CONSIDERE MANIFIESTAMENTE DEFECTUOSO. DESPUÉS DEL ENSAYO SE EXAMINAN VISUALMENTE TODOS LOS ESPECÍMENES Y SI SE CONSIDERA QUE ALGUNO ES CLARAMENTE DEFECTUOSO, NO SE DEBEN TENER EN CUENTA LOS RESULTADOS OBTENIDOS.

  26. SI MÁS DE UN ESPECIMEN QUE REPRESENTE UN ENSAYO A UNA EDAD DETERMINADA SE CONSIDERA DEFECTUOSO, ANTES O DESPUÉS DEL ENSAYO, SE DESCARTA EL ENSAYO COMPLETO Y SE REPITE. EL RESULTADO DEL ENSAYO DEBE SER EL PROMEDIO DE LOS RESULTADOS INDIVIDUALES DE LOS ESPECÍMENES ENSAYADOS.

  27. 16. ESPECÍMENES DE ENSAYO DE HORMIGÓN ENDURECIDO 16.1 NÚMERO DE ESPECÍMENES PARA CADA CONDICIÓN DEL HORMIGÓN QUE SE VA A COMPARAR, SE DEBEN ELABORAR SEIS O MÁS ESPECÍMENES, PARA EL ENSAYO DE CONGELAMIENTO Y DESCONGELAMIENTO, Y 3 Ó MÁS PARA CADA TIPO Y EDAD DE ENSAYO ESPECIFICADOS EN LA TABLA 2.

  28. 16.2 TIPOS DE ESPECÍMENES CON Y SIN ADITIVOS QUÍMICOS SE PREPARARÁN DE ACUERDO A LO SIGUIENTE: 16.2.1 RESISTENCIA A LA COMPRESIÓN ASTM C 192 16.2.2 RESISTENCIA A LA FLEXIÓN ASTM C 192

  29. 16.2.3 RESISTENCIA AL CONGELAMIENTO Y AL DESCONGELAMIENTO: ELABORACIÓN Y CURADO POR LA ASTM C 192 DIMENSIONES DE LOS ESPECÍMENES DE ACUERDO A ASTM C 666. 16.2.4 CAMBIO DE LONGITUD ASTM C 157.

  30. ENSAYOS EN HORMIGÓN ENDURECIDO 17.1 MÉTODOS: TABLA 1 17.1.1 RESIST. COMPRESIÓN: NTP 339.034 EDADES: 1 DÍA, 3 DÍAS, 7 DÍAS, 28 DÍAS, 6 MESES Y 1 AÑO.

  31. 17.1.2 RESIST. A LA FLEXIÓN NTP 339.078 EDADES: 3 DÍAS, 7 DÍAS Y 28 DÍAS. 17.1.3 RESIST. AL CONGELAMIENTO Y DESCONGELAMIENTO PROCEDIMIENTO “ A “ DE ASTM C 666. EDAD: A LOS 14 DÍAS. CALCULAR FACTORES DE DURABILIDAD SEGÚN NTP 339.089.

  32. 17.1.4 CAMBIO DE LONGITUD PRISMAS MOLDEADOS, ELABORADOS Y ENSAYADOS SEGÚN ASTM C 157.

  33. 18. ENSAYOS DE UNIFORMIDAD Y EQUIVALENCIA 18.1 ANÁLISIS INFRARROJO ENSAYO CUALITATIVO (NO CUANTITATIVO). 18.1.1 ADITIVOS LÍQUIDOS. 18.1.2 ADITIVOS NO LÍQUIDOS. 18.2 RESIDUO MEDIANTE SECADO EN HORNO (ADITIVOS LÍQUIDOS).

  34. 18.3 RESIDUO MEDIANTE SECADO EN HORNO (ADITIVOS NO LÍQUIDOS). 18.4 GRAVEDAD ESPECÍFICA (ADITIVOS LÍQUIDOS) SE UTILIZARÁN DENSÍMETROS QUE CUMPLAN CON ASTM E 100, PARA LA DETERMINACIÓN A 25 °C ± 1 °C .

  35. 19. INFORME RESULTADOS DE LOS ENSAYOS ESPECIFICADOS. MARCA NOMBRE DEL FABRICANTE NÚMERO DEL LOTE TIPO Y CANTIDAD DE MATERIAL DESCRIPCIÓN DE AGREGADOS FINO Y GRUESO. DATOS DETALLADOS SOBRE LAS MEZCLAS UTILIZADAS.

  36. 20. ANTECEDENTE ASTM C 494-98 SPECIFICATION FOR CHEMICAL ADMIXTURES FOR CONCRETE.