IMPLICATIONS OF AGGREGATION AND MASS FRACTAL NATURE OF AGGREGATES ON THE PROPERTIES OF ORGANIC PIGMENTS AND POLYMER COMPOSITES By N. Agashe * , G. Beaucage * , D. Kohls * , S. Sukumaran * , G. Skillas † , G. Long ‡ , J. Ilavsky # , P. Jemian § , L. Clapp & , R. Schwartz &

sonia-roy
Télécharger la présentation

What are Pigments ?? Most Common types of Pigments are, Inorganic Pigments Organic Pigments

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. IMPLICATIONS OF AGGREGATION AND MASS FRACTAL NATURE OF AGGREGATES ON THE PROPERTIES OF ORGANIC PIGMENTS AND POLYMER COMPOSITES By N. Agashe*, G. Beaucage*, D. Kohls*, S. Sukumaran*, G. Skillas†, G. Long‡, J. Ilavsky#, P. Jemian§, L. Clapp&, R. Schwartz& *Department of Materials Science and Engineering, University of Cincinnati, Cincinnati, OH 45220, USA †Inst. f. Verfahrenstechnik, ETH Zentrum ML F24, CH–8092 Zurich, Switzerland. ‡Ceramics Division NIST, Gaithersburg, MD 20899, USA. #University of Maryland, College Park, MD 20742, USA. §University of Illinois at Urbana–Champaign, IL 61801 , USA. &Colors Group, Sun Chemical Corp., Cincinnati, OH 45232 , USA.

  2. What are Pigments ?? • Most Common types of Pigments are, • Inorganic Pigments • Organic Pigments • Other types include Metallic and Pearlescent. The smallest size of an aggregate necessary for scattering is given by Bragg’s Law, The optimum size of the aggregate can be estimated by integrating the Guinier Law,

  3. Why Organic Pigments ? • Most of the research in the pigment industry is concentrated on inorganic pigments like titania. • Until now all work on organic pigments has examined only the surface fractal nature of the organic pigment particles. • We make the first attempt to study the aggregation of organic pigments, the mass fractal nature of these aggregates and their relationship to the optical properties. • The typical size of primary particles of organic pigments is 0.05 to 0.1 mm. The optimal size necessary for good scattering is about 0.5 mm.

  4. Fractal Structures – have Fractional Dimension • Surface Fractal Object, (ds) • Irregular Surface • Mass Fractal Object, (df) • Irregular Structure

  5. Common Organic Pigments are, • Azo Pigments: Monoazo (-NH-) or Diazo (-N=N-) • Quinacridones, Naphthol Reds, Diarylides, Rhodamines, and Naphthoic Acid. • Phthalocyanines: (Naphthol) & (-CN) • Metal and Non-metal • Perylenes • Carbazoles • Triphenyl Methane • Anthraquinone and Indigoid Pigments • Denotation: C.I. PR 122 (Pigment Red 122)

  6. Transport Limited Reaction Limited • Regimes of Aggregation • Diffusion Limited Aggregation,df < 2 (df ~ 1.8) • Reaction Limited Aggregation,df > 2 (df ~ 2.5) • Intermediate Regime

  7. Any Scattering Best Scattering • Aggregation of Organic Pigments • Forces behind aggregation of organic pigments are weak electrostatic forces like van Der Waal’s forces, static charge, chemical polarity and surface tension. • Processing also dictates the nature of the aggregates. • Color is produced in pigments by scattering. For visible light, l ~ 0.5 mm • The typical particle size for organic pigments is 0.05 to 0.1 mm. Aggregation is necessary for good scattering.

  8. Scattering in Organic Pigments Mie Scattering Dilute Systems, Large Particles, Higher Index Difference Rayleigh Ganz Approximation All Systems, All Particles Particles, Lower Index Difference For X-Rays, the comparable contrast difference is very small between the pigment and the polymer.

  9. - 4 G1, Rg1 B3 - df Log (I) B2 - 4 B1 G2, Rg2 df is the mass fractal dimension For fractal objects, Log (q) (q in Å-1) Small and Ultra Small Angle X-Ray Scattering (SAXS/USAXS) Range of q for SAXS is 0.01 to 0.1, while USAXS can go down to q value of 0.0001

  10. Unified Function for Mass Fractal Model • Unified Function, used to fit the scattering data, is based on six parameters, • Guinier Prefactors: G1 and G2 • Radius of Gyration: Rg1 and Rg2 • Power law Prefactor: B1 • Fractal Dimension: df The diameter of a sphere having similar Rg as the aggregate can be used to estimate the size of the aggregate.

  11. Results • The results are a survey of some of the behavior seen when organic pigments are milled into polymers. • This is the first attempt to characterize the aggregation according to the process by which the aggregates are formed. • The mass fractal behavior of these aggregates is studied. • The primary particle of each organic pigment is examined to see if it is made up of a single crystal or multi crystals.

  12. Diazo Pigment Red 170 (235-0170) TEM – Dpp = 0.2 mm LS – Dagg = 0.4 mm Powder – Non Mass Fractal Dpp = 0.2 mm 20% in PMMA – Mass Fractal, df = 2.5 (RLA) Dagg = 2.35 mm

  13. Diazo Pigment Red 170 (235-1170) Higher Luminosity TEM – Dpp = 0.15 mm LS – Dagg = 0.35 mm Powder – Non Mass Fractal Dpp = 0.156 mm 20% in PMMA – Mass Fractal, df = 2.67 (RLA) Dagg = 2.01 mm

  14. PMMA, used earlier, is a non-crystalline polymer. • PP is a semi-crystalline polymer. The addition of pigments has an effect on the crystallinity of PP.

  15. C. I. PR 122 Monoazo Pigment Red 122 TEM – Dpp = 0.1 mm (length) LS – Dagg = 0.2 mm Powder – Non Mass Fractal Dpp = 0.13 mm 1% in PP – Mass Fractal, df = 1.91 (DLA) Dpp = 0.13 mm 5% in PP – Mass Fractal, df = 1.5 (DLA) Dpp = 0.13 mm

  16. C. I. PV 19 Monoazo Pigment Violet 19 TEM – Dpp = 0.05 mm LS – Dagg = 0.4 mm Powder – Mass Fractal, df = 2.32 (RLA) Dpp = 0.03 mm, Dagg = 1.2 mm 1% in PP – Mass Fractal, df = 1.55 (DLA) Dpp = 0.16 mm, Dagg = 1.0 mm 5% in PP – Mass Fractal, df = 1 (DLA) Dpp = 0.26 mm

  17. C. I. PY 13 Disazo Pigment Yellow 13 TEM – Dpp = 0.1 mm LS – Dagg = 0.5 mm Powder – Mass Fractal, df = 2.34 (RLA) Dpp = 0.035 mm, Dagg = 0.32 mm 5% in PP – Mass Fractal, df = 2.7 (RLA) Dpp = 0.052 mm, Dagg = 0.49 mm

  18. C. I. PY 14 Disazo Pigment Yellow 14 TEM – Dpp = 0.1 mm LS – Dagg = 0.5 mm Powder – Mass Fractal, df = 2.63 (RLA) Dpp = 0.125 mm, Dagg = 0.52 mm 5% in PP – Mass Fractal, df = 2.77 (RLA) Dpp = 0.08 mm, Dagg = 0.43 mm

  19. C. I. PY 83 Pigment Yellow 83 TEM – Dpp = 0.1 mm (length) LS – Dagg = 1.2 mm Powder – Non Mass Fractal Dpp = 0.14 mm 1% in PP – Mass Fractal, df = 1.4 (DLA) Dpp = 0.14 mm, Dagg = 1.1 mm 5% in PP – Mass Fractal, df = 1.62 (DLA) Dpp = 0.12 mm, Dagg = 4.5 mm

  20. X=Cl Phthalocyanine Pigment Green 7 TEM – Dpp = 0.05 mm LS – Dagg = 0.1 mm Powder – Non Mass Fractal Dpp = 0.018 mm 50% in PE – Mass Fractal, df = 1.4 (DLA) Dpp = 0.036 mm, Dagg = 0.767 mm

  21. Effect of Pigments on the lamellar thickness of PP The Long Period decreased from 233Å to 131Å on addition of pigments

  22. Conclusions • Organic pigments field has ignored the importance of aggregates to optical properties. Mass fractal aggregates were observed for all the pigments when milled into polymers. • The size of a crystal is too small to scatter visible light. Aggregation is critical to have good optical properties, and this issue has been dealt with for the first time. • There is an incredible range of behavior in terms of aggregation, based on the polarity of the compound and the particle size. • Some contradictions in the behavior can be seen. • There is a potential to control and design the aggregate size and structure of organic pigments if we had a bit more understanding.

  23. Future Work • Carry out mass fractal analysis using different pigments from different classes and different polymers. • Study of processing effects on the nature of aggregates. • Study of effect of additives on the behavior of aggregates. • Mass fractal analysis of digital electron micrographs of organic pigment powders and polymer samples. • Simulations of the process of formation of aggregates starting from primary particles. • Simulate growth processes for different systems like asymmetric particles, polydispersity and roughness of surfaces.

  24. Acknowledgements • Dr Gregory Beaucage. • Dr George Skillas. • Sun Chemical Corporation. • Advanced Photon Source, ANL. • Research Group and the Department. • My friends and my family.