1 / 12

Commercially available Tungsten Plates

Commercially available Tungsten Plates. Cime Bocuze (St Pierre-en Faucigny, France) Plansee (Reutte, Austria). W HCAL Prototype meeting in Annecy 24/9/2009. W. Klempt CERN/PH. W Composite Material (Cime Bocuze). Consist of W ( ≥ 90%) rest mixture of (Fe), Ni, Cu …  = 17 – 18 g/cm 3

wfierro
Télécharger la présentation

Commercially available Tungsten Plates

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Commercially available Tungsten Plates Cime Bocuze (St Pierre-en Faucigny, France) Plansee (Reutte, Austria) W HCAL Prototype meeting in Annecy 24/9/2009 W. Klempt CERN/PH

  2. W Composite Material (Cime Bocuze) • Consist of W (≥ 90%) rest mixture of (Fe), Ni, Cu … •  = 17 – 18 g/cm3 • Λ ≈ 10 cm, X0 ≈ 0.4 cm • Well established production procedure • Easy to machine (i.e. sawing/cuting of plates) 1500 °C

  3. Product Range and Material Properties

  4. Mechanical Properties

  5. Pure Tungsten Plate Production (Plansee) Produce ingots (weight ≤ 500kg) Sintering temp. 2000-2500 °C Roll to final thickness 2000-2500 °C

  6. Mechanical Properties of Pure Tungsten • Sintered Tungsten exhibits low ductility (is rather brittle) atroom temperature. • Its mechanical properties are situated somewhere between metals and ceramics and are very dependent on small (~ 1%) admixtures (Re, La2O3 etc. ) • It’s Young’s modulus is known (≈2 x ESS) • But it is not easy to get other engineering values like:stress- strain diagram, tensile strength, fracture elongationetc.. • A single load test will not give enough information, other series of measurements are needed; • Plansee is willing to help us with these values

  7. Comparison of Mechanical Properties *Alloys used must be paramagnetic, **Tests required

  8. Plate size and tolerances • Currently available plate sizes • Thickness of 12 mm is feasible for both • Flatness tolerance ca. 1.5 mm • ≤ 1 mm possible • Thickness tolerance ± 0.5 mm • With machining ± 0.1 mm (cost ↑)

  9. Machinability • Abrasive water jet cutting is suitable • Holes, slots & various cut-outs are possible • Precision of ± 0.1 mm is possible (but very expensive)

  10. Magnetic properties of Densimet 180

  11. Magnetic properties of Densimet 180 μ