1 / 13

Výročná celoústavná konferencia ÚEF SAV, 10. decembra 2008

Laboratórium materiálovej fyziky. Ing. Pavel Diko, DrSc. Mgr. Mária Kaňuchová, PhD. Ing. Martina Šefčiková, PhD. , matersk á dovolenka Ing. Katarína Zmorayová, PhD., matersk á dovolenka Mgr. Vitalij Antal, doktorand EÚ, projekt NESPA Ing. Dušan Šuster, doktorand LPP APVV

winona
Télécharger la présentation

Výročná celoústavná konferencia ÚEF SAV, 10. decembra 2008

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Laboratórium materiálovej fyziky Ing. Pavel Diko, DrSc. Mgr. Mária Kaňuchová, PhD. Ing. Martina Šefčiková, PhD., materská dovolenka Ing. Katarína Zmorayová, PhD., materská dovolenka Mgr. Vitalij Antal, doktorand EÚ, projekt NESPA Ing. Dušan Šuster, doktorand LPP APVV Mgr. Daniela Volochová, doktorand SAV, materská dovolenka Mgr. Peter Kulík (zdielaný s LNAM) Solupráca: RNDr. J. Kováč, CSc. (LNAM), RNDR. V. Kavečanský, CSc. (OFK) Výročná celoústavná konferencia ÚEF SAV, 10. decembra 2008

  2. Vedecký program LMF REBCO monokryštalických masívne supravodiče Rast YBCO kryštálov Kryštálové defekty Tvorba piningových centier - nesupravodivé častice - chemické piningové centrá Nové supravodiče iron-based oxyarsenides (oxypnictides) Gd0.8Th0.2FeAsO, Tc =56K

  3. Riešené projekty Medzinárodné NESPA., NanoEngineeredSuperconductorsforPowerAplications 6-th Framework Program, MarieCurrieTrainingNetwork, 2006/2010, Domáce APVV, Dizajn mikroštruktúry YBCO masívnych supravodičov 2006/2009. APVV LPP, Monokryštalické kompozitné YBCO supravodiče 2006/2010. VEGA 2/7052/27, YBCO supravodiče pre silnoprúdové aplikácie, 2007/2009. Centrum excelentnosti SAV NANOSMART, Centrum nanoštruktúrovaných materiálov, 2007/2009.

  4. Publikácie v 2008 CC P. Diko, X. Chaud, V. Antal, M. Kaňuchová, M. Šefčiková and J. Kováč, Eliminationofoxygenationcracks in top-seededmelt-growth YBCO superconductors by highpressureoxygenation, Supercond. Sci. Technol. 21 (2008) 11508 (3pp). P. Diko, M. Šefčıková, M. Kaňuchová, K. Zmorayová, Microstructureof YBCO bulksuperconductorswith CeO2 addition, MaterialsScience and Engineering B 151 (2008) 7–10. M. Šefciková, P. Diko, B. Bozzo, X. Granados , X. Obradors, Influenceofcrystalplane on theweldingqualityof YBCO bulksuperconductor, MaterialsScience and Engineering B 151 (2008) 107–110. X. Chaud, T. Prikhna, Y. Savchuk, A. Joulain, E. Haanappel, P. Diko, L. Porcar, M. Soliman, Improvedmagnetictrappedfield in thin-wall YBCO single-domainsamples by high-pressureoxygenannealing, MaterialsScience and Engineering B 151 (2008) 53–59. WOS, SCOPUS X Chaud, Y Savchuk, N Sergienko, T Prikhna and P Diko, High-pressureoxygenationofthin-wall YBCO single-domainsamples, JournalofPhysics: ConferenceSeries97 (2008) 012043. P. Diko, M. Kaňuchová, X. Chaud, P. Odier, X GranadosX. Obradors, Oxygenationmechanismof TSMG YBCO BulkSuperconductor, JournalofPhysics: ConferenceSeries97 (2008) 012160. O. Staller, D. Holzmann, G. Gritzner, P.l Diko, D.lMikolaj, F. Kováč, Texturednickeltapespreparedfromcommerciallyavailablematerial, Cent. Eur. J. Chem. • 6(2) • 2008 • 135–139.

  5. Prednáškynamedzinárodných podujatiach P. Diko, V. Antal, M. Kaňuchová, V. Kavečanský, Gritzner, J. Kováč„PinningbehaviourofCusubstitutions in YBCO TSMG bulksuperconductors, prednáška na “InternationalConference on Superconductivity and Magnetism(ICSM 2008) 25-29 August 2008, Side-Antalya/TURKEY, P. DIKO, X. CHAUD, V. ANTAL, M. KAŇUCHOVÁ, M. ŠEFČÍKOVÁ, J. KOVÁČEliminationofOxygenationCracking in YBCO BulkSuperconductors, prednáška na 3rdInternationalConferenceFractographyofAdvancedCeramics, September 7 – 10, 2008, Stará Lesná. M. Jirsa, M. Rames, M. Muralidhar, and P. Diko, EffectofOxygenation on MagneticPerformanceof (Nd,Eu,Gd)Ba2Cu3Oy Bulkwith a lamellarNanostructure, prednáška na “InternationalConference on Superconductivity and Magnetism(ICSM 2008) 25-29 August 2008, Side-Antalya/TURKEY, V. Antal, M. Eisterer, H. Weber, P. Diko, X. Chaud, M. Kaňuchová, M. Šefčiková„Criticalcurrentdensity in Al-doped YBCO bulksuperconductors“, NESPA Workshop, 2-4.10.2008 Rust, Austria. Posterové príspevky M. Šefčiková, V. Antal, M. Kaňuchová, J. Kováč, P. Diko Microstructure and critical current density of YBCO bulk superconductors with CeO2 addition, 16-th Conference of Czech and Slovak Physicists, September 8-11, 2008, Hradec Králové. Kaňuchová M., Antal V., Šefčíková M., Kováč J., Diko P., Pinning behavior of Ag substitution in YBCO TSMG bulk superconductor, 16-th Conference of Czech and Slovak Physicists, September 8-11, 2008, Hradec Králové.

  6. Citácie v roku 2008 26 SCI citácií Recenzie v roku 2008 Supercond. Sci. Technology, JournalofPhysics: ConferenceSeries, Key Engn. Mat. , VEGA Pobytynazahraničnýchpracoviskách: V. ANTAL, 4 mesiace v ATI Viedeň (NESPA) Krátkodobé tréningy v rámci NESPA: V. Antal, D. Volochová, IFW Dresden, ICAB Barcelona, Iné pozitíva P. Diko, Vedeniesekcie VII na3rdInternationalConferenceFractographyofAdvancedCeramics September 7 – 10, 2008 Hotel Academia, Stará Lesná, Poprad, SLOVAK REPUBLIC. P. Diko, člen kolégia SAV člen komisie č.7 VEGA Popularizačné aktivity P. Diko, Tri prednášky v rámci Centra rozvoja vzdelávania „Progresívne materiály a technológie“ P. Diko, kapitola vo vydanom zborníku „MASÍVNE MONOKRYŠTALICKÉ YBCO SUPRAVODIČE PRE SILNOPRÚDOVÉ APLIKÁCIE “ M. Kaňuchová, prednáška v rámco DOD, Supravodiče pre praktické aplikácie.

  7. Kryštálové defekty Najlepší výsledok v roku 2007 • Rekordné 2,5-né zvýšenie kritickej prúdovej hustoty v YBCO masívnom • supravodiči elimináciou oxidačných trhlín vysokotlakou oxidáciou. • Spolupráca s CRETA CNRS Grenoble • Výsledok publikovaný: • Diko, X. Chaud, V. Antal, M. Kaňuchová, M. Šefčíková and J. Kováč, • Eliminationofoxygenationcracks in top-seededmelt-growth YBCO • superconductors by highpressureoxygenation, Supercond. Sci. Technol. • 21 (2008) 11508 (3pp). Impactfactor 2,56

  8. Kryštálové defekty Vyššie Jc pre TSMG vzorky bez trhlín v a/c-rovine YBa2(Cu1-xAgx)O7 (x=0.005) Oxidácia: A/ 400 ºC , kyslík (1bar) B/ 760 °C pri 160bar, postupne zvyšovaný parciálny tlak kyslíka (CRETA Grenoble) a/b c A B

  9. d2 d1 a l Line 1 Line 2 Kryštálové defekty Redukcia prierezu a/c- trhlinami Typické l/d ≈0.5 Prierez ≈33% M. Eisterer at al. SUST 2006, ATI Vienna Zmena Jc nie je spôsobená rozdielnym piningom

  10. 10 mm 10 mm Kryštálové defekty Vplyv kryštálovej roviny zvaru Spolupráca s ICMAB Barcelona M. Šefciková, P. Diko, B. Bozzo, X. Granados , X. Obradors, Mat. Sci. Eng B 151 (2008) 107–110. c c {100} weld {110} weld a,b a,b 211FZ a,b 211FZ a,b

  11. Tvorba piningových centier Vplyv Ce na velkosť Y211 častíc P. Diko, M. Šefčıková, M. Kaňuchová, K. Zmorayová, Mat. Sci. Eng.B 151 (2008) 7–10. 3 wt % CeO2 CeO2 free Ce difúzna zóna pôvodné rozhranie d211 d211 = 1.5 mm d211 = 0.4 mm 30 mm 10 mm 10 mm Y2BaCuO5 BaCeO3 Y2BaCuO5

  12. Tvorba piningových centier Mechanizmus potlačenia rastu 211 častíc Častice rastú Ostwald-ovým mechanizmom – vyššia koncentrácia Y pri povrchu častice s menším polomerom r C(r) = C(∞)e (α/r) Kelvin efekt Lifshitz I, Slyozov V. J Phys Chem Solids 1961;19:35. r3t – r30≈ D. C .s . t D – difúzny koeficient Y; C – koncentrácia Y v tavenine; s = energia 211/L rozhrania t – čas Ce sa rozpúšťa v peritektickej tavenine(0.1wt. %) – príliš malá koncentrácia na ovplyvnenie D resp. C. Proces Ostwald-ovho rastu je spomalený znížením energie 211/Lmrozhrania 211 Y 211 211 Segregácia Ce na povrch 211 211

  13. Tvorba chemických piningových centier Tvorba piningových centier • Substitúcie v CuO2 rovinách a CuOreťazcochv YBa2(Cu1-xMx)3O7 • M = Fe,Co,Ni,Zn,Ag,Al,Mn,Li,Ga, Mg • Tvorba klastrov žíhaním v atmosfére s nízkym parciálnym tlakom • kyslíka(PO) • Kombinácie Cu substitúcií s Ba a Y substitúciami • Precipitáciananočastíc z presýteného tuhého roztoku