An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ECE 480 – Introduction to Nanotechnology + Lab. Emre Yengel Department of Electrical and Communication Engineering Fall 2013

  2. Silicon; Basics

  3. Silicon; Basics

  4. Silicon; Basics

  5. Silicon; Basics

  6. Silicon; Basics

  7. Silicon; Basics

  8. Silicon; Basics

  9. Silicon Wafer

  10. Silicon Wafer

  11. Silicon Wafer • Czochralskisi crystalgrowth;

  12. Silicon Wafer • 1-inch (25 mm) • 2-inch (51 mm). Thickness 275 µm. • 3-inch (76 mm). Thickness 375 µm. • 4-inch (100 mm). Thickness 525 µm. • 5-inch (130 mm) or 125 mm (4.9 inch). Thickness 625 µm. • 150 mm (5.9 inch, usuallyreferredto as "6 inch"). Thickness 675 µm. • 200 mm (7.9 inch, usuallyreferredto as "8 inch"). Thickness 725 µm. • 300 mm (11.8 inch, usuallyreferredto as "12 inch"). Thickness 775 µm. • 450 mm (17.7 inch, usuallyreferredto as "18 inch"). Thickness 925 µm (expected)

  13. Silicon; Defects

  14. Silicon; Defects

  15. Semiconductors • Low resistivity => “conductor” • High resistivity => “insulator” • Intermediate resistivity => “semiconductor” • conductivity lies between that of conductors and insulators • generally crystalline in structure for IC devices • In recent years, however, non-crystalline semiconductors have become commercially very important polycrystalline amorphous crystalline

  16. Semiconductor Materials

  17. Band Theory of Solids • The conduction band is the range of electron energies enough to free an electron from binding with its atom to move freely within the atomic lattice of the material as a 'delocalized electron'. • In solids, the valence band is the highest range of electron energies in which electrons are normally present at absolute zero temperature.

  18. Silicon; Defects • Atomic density: 5 x 1022 atoms/cm3 • Si has four valence electrons. Therefore, it can form covalent bonds with four of its nearest neighbors. • When temperature goes up, electrons can become free to move about the Si lattice.

  19. Electrical Properties of Silicon  Silicon is a semiconductor material. • Pure Si has a relatively high electrical resistivity at room temperature.  There are 2 types of mobile charge-carriers in Si: • Conduction electrons are negatively charged; • Holes are positively charged.  The concentration (#/cm3) of conduction electrons & holes in a semiconductor can be modulated in several ways: • by adding special impurity atoms ( dopants ) • by applying an electric field • by changing the temperature • by irradiation

  20. Silicon; Electron-Hole Pair Generation • When a conduction electron is thermally generated, a “hole” is also generated. • A hole is associated with a positive charge, and is free to move about the Si lattice as well.

  21. Carrier Concentration in Intrinsic Silicon • The “band-gap energy” Eg is the amount of energy needed to remove an electron from a covalent bond. • The concentration of conduction electrons in intrinsic silicon, ni, depends exponentially on Egand the absolute temperature (T):

  22. Silicon; Defects

  23. Silicon; Doping (N type) • Si can be “doped” with other elements to change its electrical properties. • For example, if Si is doped with phosphorus (P) (or arsenic (As)), each P atom can contribute a conduction electron, so that the Si lattice has more electrons than holes, i.e. it becomes “N type”: Notation: n = conduction electron concentration

  24. Silicon; Doping (P type) • If Si is doped with Boron (B), each B atom can contribute a hole, so that the Si lattice has more holes than electrons, i.e. it becomes “P type”: Notation: p = hole concentration

  25. Summary of Doping

  26. Silicon; Electron-Hole Concentrations • Under thermal equilibrium conditions, the product of the conduction-electron density and the hole density is ALWAYS equal to the square of ni: N-type material P-type material

  27. Terminology donor: impurity atom that increases n acceptor: impurity atom that increases p N-type material: contains more electrons than holes P-type material: contains more holes than electrons majority carrier: the most abundant carrier minority carrier: the least abundant carrier intrinsic semiconductor: n = p = ni extrinsic semiconductor: doped semiconductor