EBSD analysis of dislocations on DC-Spark sample after heat treatment (1.040 C in H 2 , 2h)

EBSD analysis of dislocations on DC-Spark sample after heat treatment (1.040 C in H 2 , 2h). Anité Pérez Fontenla 28.01.2014. Aim of the study:.

xanthe
Télécharger la présentation

EBSD analysis of dislocations on DC-Spark sample after heat treatment (1.040 C in H 2 , 2h)

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. EBSD analysis of dislocationson DC-Spark sample after heat treatment (1.040 C in H2, 2h) Anité Pérez Fontenla 28.01.2014

  2. Aim of the study: • A deeper understanding of the dislocations role in the material response to the BKD’s could help us to understand why areas with same surface status are highly affected by the phenomena. • A crucial aspect is to find a diagnostic technique which determines their presence and/or density; • Dislocation presence (like a group concept) in the microstructure of the material can be studied using Electron Backscatter Diffraction (EBSD). This technique fulfills our following requirements: • Non destructive • Appropriate for 3D specimens • Provides a good combination of spatial and angular resolution • Relatively reduced time of data collection How?

  3. How? • If we focus an electron beam on a crystalline sample e- disperse beneath the surface, diffracting among the crystallographic planes. • The diffracted beam produces a pattern (EBSP) that can be imaged by placing a phosphor screen close to the specimen. EBSP are composed of intersecting bands (Kikuchi bands) that are directly related to the crystal lattice structure in the sampled region. Bands & dislocations? To accommodate plastic deformation, the material generates dislocations which disturbs the structure of the lattice and that leads in a reduction of bands quality 

  4. How? • That can be directly related with the residual strain and represented in a • local misorientation map. As BKD phenomena are complex and not well known, the density of dislocations will be studied with a simpler case: a hardness indentation.

  5. The average misorientation between every pixel and its surrounding pixels is calculated, and assigns the mean value to that pixel; Before micro-hardness test After micro-hardness test

  6. What’s next? Hardness indent nr2…successful! Check the reproducibility of the technique and obtaining statistics about the affected zone; Which part of the green area is due to dislocations and which one due to surface deformation? • interferometry? • AFM?

  7. Sub-grains or faceting?