An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 1st anual MEETING STFI Chemnitz 12-14/15-2010 GEORG BÖRNER Chemisches Werk fürDach- und BautenschutzGmbH & Co. KG D-36251 Bad HersfeldHeinrich-Börner-Str. 31Tel. 06621 / 175-0Info@GeorgBoerner.de Verkaufsbüro Rhein-MainD-63452 HanauChemnitzer Straße 20Tel. 06181 / 96916-0Hanau@GeorgBoerner.de D-90475 NürnbergSaganer Straße 37Tel. 0911 / 94469-0Nuernberg@GeorgBoerner.de www.GeorgBoerner.de Dr. Gerhard Faßbender Laboratory Director Gerhard.Fassbender@GeorgBoerner.de YourLecturer

  2. Traditional approach, hot process, bitumen based + Light-coloured, highly NIR and visible light reflective top coat, prefabricated rolls (88-100 cm width) + Top coat surface should be smooth, non-porous and not sticky at elevated temperature to ensure easy (self) cleaning + Replacing bitumen and polymer content by sustainable/recycled materials up to 30% + Demo material can be easily produced using traditional production equipment - PCM cannot be included due to sensitivity to heat and high shear Conceptual design, revised

  3. Product for new roofs NIR-reflective topcoat withreinforcement 0.5 mm Renewable/bitumen/polymer waterproofing layer 1.4 mm Impreg. performance compo- site reinforcement 1 .6 mm Renewable/bitumen/polymerself adhesive 1.0 mm Release foil Total thickness approx.4.5 mm Specifications acc. to -European Standards for bituminous roofing felts- for new roofs NU-Roof modified polymer bitumen membrane

  4. Product for old roofs to be renovated NIR-relective topcoat withreinforcement 0.5 mm Renewable/bitumen/polymer waterproofing layer 1.4 mm Impreg. performance compo- site reinforcement 1 .6 mm Renewable/bitumen/polymeradhesive to be welded 1.0 mm PE film, 10µm Total thickness approx.4.5 mm Specifications acc. to -European Standards for bituminous roofing felts- for new roofs NU-Roof modified polymer bitumen membrane

  5. More futuristic approach, cold process, dispersion based + Light-coloured, highly NIR and visible light reflective top coat + Top coat surface should be smooth, non-porous and not sticky at elevated temperature to ensure easy (self) cleaning + Polyester fleece reinforced base coat, impregnated with acrylate or rubber modified bitumen dispersion including PCM - As no suitable production line is available within NU-Roof, only small, hand made samples can be produced for demonstration purposes Conceptual design, revised

  6. Product for new roofs NIR-reflective topcoat withreinforcement 0.5 mm Dispersion based waterproo-fing layer incl. PCM 1.4 mm PES-fleece reinforcement, im-pregnated, incl. PCM 1 .6 mm Dispersion based self adhesive layer incl. PCM 1.0 mm Release foil Total thickness approx.4.5 mm NU-Roof cold processed self adhesive membrane