Fiber Boards Production from Cynara cardunculus Without Using Synthetic Resins

Fiber Boards Production from Cynara cardunculus Without Using Synthetic Resins. Camilo Mancera Arias Supervisor: Dr. Francesc Ferrando Piera Co- Supervisor: Dr. Joan Salvadó i Rovira. Introduction. Objectives. Work Plan. Discussion Topics. Discussion Topics. Outline Steam Explosion

yardley-hanson
Télécharger la présentation

Fiber Boards Production from Cynara cardunculus Without Using Synthetic Resins

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Fiber Boards Production from Cynara cardunculus Without Using Synthetic Resins Camilo Mancera Arias Supervisor: Dr. Francesc Ferrando Piera Co- Supervisor: Dr. Joan Salvadó i Rovira

  2. Introduction Objectives Work Plan Discussion Topics Discussion Topics Outline Steam Explosion Pressing Characterization Summary

  3. Importance of the project • Userenewable resources vs fossil resources • Increase aggregated value of agricultural residues • Construction materials Fiber boards. Introduction 1

  4. Cynara cardunculus • Wild Artichoke • Native from Mediterranean regions. • Potentially High energetic properties. • Source of Lignocellulosic biomass. • Research group projects association 2

  5. Fiber Boards • Definition • Agglomeration of fibers • Adhesives • Pressure and Temperature • Classification • Hard Fiber Boards (800-1000 kg/m3) • Medium Density Fiber Boards (600-800 kg/m3) • Semi-hard or light fiber boards (350-600 kg/m3) 3

  6. Lignin 4

  7. Objectives Production of fiber boards of commercial quality from Cynara cardunculus with better ecological properties. • Particular • Chemical characterization • Steam explosion • Identification and optimization of relevant factors • Study of other variables, soft grinding, exogenous lignin, etc. • Comparisons 5

  8. Work Plan 6

  9. Steam Explosion • Operation conditions • Water Vapor at 30-40 bars and 160-260 ºC. • Residence times of few min. Steam Explosion Reactor Pneumatic Valve • How it works… • Impregnation • Flash Expansion • Extractives and Hemicelluloses Dissolution. • Fibers Partial Rupture Tank Lay Out Laboratory Scheme 7

  10. Lignin flow and redistribution • Lignin – Fiber chemical bond formation • Operation conditions Board properties Pressing 8

  11. Characterization of Fiber Boards • Mechanical Characterization • Modulus of Rupture • Modulus of Elasticity • Internal Bond • Physical Characterization • Density • Water Absorption • Thickness Swelling • Chemical Characterization • Ashes • Lignin • Cellulose • Hemicelluloses 9

  12. Target Properties • Mechanical Properties M. sinensis • Modulus of Rupture = 61,2 MPa • Modulus of Elasticity = 7500 MPa • Internal Bond = 1,8 MPa • Mechanical Properties EU Std • Modulus of Rupture ≥ 40 MPa • Modulus of Elasticity ≥ 3000 MPa • Internal Bond ≥ 0,7 MPa • Physical Characterization M. sinensis • Density = 1100 kg/m3 • Water Absorption = 15,3% • Thickness Swelling = 5% • Physical Characterization EU Std • Density > 800 kg/m3 • Water Absorption ≤ 30% • Thickness Swelling ≤ 20% 10

  13. Summary 11

  14. Ph. D. Student Camilo Mancera Arias Universitat Rovira i Virgili Tarragona, Spain – January 2005 email: camilo.mancera@urv.net 12