1 / 11

Cold work, recovery, recrystallization

Cold work, recovery, recrystallization. Example:Single crystal. State I:Annealed metal. Fairly strong and ductile. r  = 10 6 /cm 2. Low internal energy: stable. Cold worked. State II:Cold worked metal. r  = 10 10-12 /cm 2. Very strong and brittle. High internal energy: not very stable.

kerry
Télécharger la présentation

Cold work, recovery, recrystallization

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Cold work, recovery, recrystallization

  2. Example:Single crystal State I:Annealed metal Fairly strong and ductile r= 106/cm2 Low internal energy: stable

  3. Cold worked State II:Cold worked metal r= 1010-12/cm2 Very strong and brittle High internal energy: not very stable

  4. Heated at ~0.5 Tm State III:Recovered metal r= 108/cm2 Dislocation alignment: Polygonization (one recovery process) Strong and less brittle Compared to state II Internal energy is lowered

  5. Recall what a grain boundary is

  6. Heated at ~0.5 Tm State IV:Recrystallization begins r= 106/cm2 New strain free grains are formed by nucleation Stronger than state I and ductile Internal energy is further lowered

  7. Heated at ~0.5 Tm State V:Recrystallization complete r= 106/cm2 Recrystallized Stronger than state I and ductile

  8. In summary • We started with a single crystal and ended with a polycrystal : grain refinement • The driving force for this process is decrease in internal energy

  9. For a polycrystals ( in real life) Cold worked Initial recrystallization

  10. Recrystallized Grain growth

  11. Some facts • Without a minimum amount of cold work (5-15%), there is no recrystallization • After the metal is completely recrystallized, grain growth occurs • Grain growth law at a constant temperature Di2 - D02 = Kt Di = final grain size D0 = initial grain size t = time