Silicon Quantum Dots: Grown by Ion Implantation and annealing

Silicon Quantum Dots: Grown by Ion Implantation and annealing. By Mary Coan. Outline. History of Silicon quantum dots How they were made Properties of Silicon Quantum Dots grown by ion implantation and annealing Advantages/Disadvantages Different methods to grow Silicon Quantum Dots

adamdaniel
Télécharger la présentation

Silicon Quantum Dots: Grown by Ion Implantation and annealing

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Silicon Quantum Dots: Grown by Ion Implantation and annealing By Mary Coan

  2. Outline • History of Silicon quantum dots • How they were made • Properties of Silicon Quantum Dots grown by ion implantation and annealing • Advantages/Disadvantages • Different methods to grow Silicon Quantum Dots • Which method is the best? • Summary

  3. History of Si QDs • 1960’s: First quantum size effects were seen in semiconductor nanocrystals • 1970’s: Louis Brus was working in Bell Labs researching colloidal synthesizes • 1980’s: First semiconductor quantum dots were grown • 1990: First visible-photoluminescence seen from Si QDs

  4. History of Si QDs • 1993: Silicon optoelectronic integrated circuit is suggested • 1993 to present: Si Quantum dots have been extensively researched • Different fabrication methods • microwave plasma decomposition of SiH4 • laser breakdown of SiH4 • plasma-enhanced chemical vapor deposition • high frequency discharge • high dose ion implantation

  5. Formation of Si QDs: Ion implantation and annealing T.S. Iwayama, T. Hama, D.E. Hole, I.W. Boyd, Vacuum 81, 179 (2006).

  6. Properties of Si QDs • Photoluminescence • Peak energy and intensity • Size ranges from 1 nm to over 10 nm in diameter • Size distribution within host material

  7. Photoluminescence C.W. White, J.D. Budai, S.P. Withrow, J.G. Zhu and S.J. Pennycock, IEEE Conference Proceeding 824 (1996).

  8. Photoluminescence T.S. Iwayama, T. Hama, D.E. Hole, I.W. Boyd, Vacuum 81, 179 (2006).

  9. Photoluminescence T.S. Iwayama, T. Hama, D.E. Hole, I.W. Boyd, Vacuum 81, 179 (2006).

  10. Suggested Mechanisms T.S. Iwayama, T. Hama, D.E. Hole, I.W. Boyd, Solid-State Electronics 45, 1487 (2001).

  11. Suggested Mechanisms R. Krishnan, UR, (2005).

  12. Range of Sizes • Longer anneals = Larger Si QDs • Ostwald Ripening T.S. Iwayama, T. Hama, D.E. Hole, I.W. Boyd, Vacuum 81, 179 (2006).

  13. Size distribution within Host Material M.L. Brongersma, A. Polman, K.S. Min, H.A. Atwater, “J. Appl. Phys. 86, 759 (1999).

  14. Defects within Host C. J. Nicklaw, M. P. Pagey, S. T. Pantelides, D. M. Fleetwood, R. D. Schrimpf, K. F. Galloway, J. E. Wittig, B. M. Howard, E. Taw, W. H. McNeil, J. F. Conley, Jr., IEEE Trans. Nucl. Science 47, 2269 (2000).

  15. Defects within Host C. J. Nicklaw, M. P. Pagey, S. T. Pantelides, D. M. Fleetwood, R. D. Schrimpf, K. F. Galloway, J. E. Wittig, B. M. Howard, E. Taw, W. H. McNeil, J. F. Conley, Jr., IEEE Trans. Nucl. Science 47, 2269 (2000).

  16. Defects within Host C. J. Nicklaw, M. P. Pagey, S. T. Pantelides, D. M. Fleetwood, R. D. Schrimpf, K. F. Galloway, J. E. Wittig, B. M. Howard, E. Taw, W. H. McNeil, J. F. Conley, Jr., IEEE Trans. Nucl. Science 47, 2269 (2000).

  17. Advantages/Disadvantages • Advantages: • Ease of integration into silicon based microelectronics (Dots and Process) • Ability to control the PL intensity and peak energy • Disadvantages: • Large size distribution within host material • Defects within host material • Surface damage (QDs)

  18. Other Fabrication Techniques • Microwave Plasma Decomposition of Silane Gas • Laser breakdown of Silane Gas • Plasma Enhanced Chemical Vapor Deposition • High Frequency Spark Discharge • Colloidal

  19. Which Method is Best? • It depends on what you want to use the Silicon QDs for. • If you want to make an optoelectical integrated circuit: • Plasma Enhanced CVD • Ion Implantation • If you want some cool flourishing Si QDs: • Colloidal

  20. Summary • Properties of Si QDs were discussed • PL dependent on: • Anneal time, temperature and process • Ion dose • Defects caused by Ion Implantation • Quantum dot surface\host material • Causing lower luminescence intensity • A Large size distribution throughout the Host • In the past this was a good technique now it is outdated by PCVD

  21. Questions ??