Silicon Nanowire based Solar Cells. ICORE - 2010, Pragya Singh, Pratul K Singh. Outline:Light Trapping in CellsSolar CellEnergy Conversion in Solar CellSolar Cells EverywherePlanar Silicon Solar CellNanowires- PropertiesSilicon Nanowires- PropertiesFabricationTechniques for SiNW DepositionExperiment at the SSN Research Centre.

albert
Télécharger la présentation

silicon nanowire based solar cells

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

    1. Silicon Nanowire based Solar Cells International Congress On Renewable Energy ICORE 2010 2nd December, 2010. Pragya Singh Pratul K Singh

    2. ICORE - 2010, Pragya Singh, Pratul K Singh

    3. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    4. ICORE - 2010, Pragya Singh, Pratul K Singh

    5. ICORE - 2010, Pragya Singh, Pratul K Singh

    6. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    7. Solar Cell Cell is thin Si wafer Size 10x10 cm : size of a CD Thickness is in fractions of mm Metal pattern is to make electrical contacts. ICORE - 2010, Pragya Singh, Pratul K Singh

    8. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    9. Energy Conversion in Solar Cell Light is shone Electrons are knocked out Electrons and holes move in opposite directions Electrical output is generated between the contacts. ICORE - 2010, Pragya Singh, Pratul K Singh

    10. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    11. Solar Cells Everywhere Solar cells : Safe Clean Quiet Durable Reliable Installable anywhere ICORE - 2010, Pragya Singh, Pratul K Singh

    12. The Main Catch ICORE - 2010, Pragya Singh, Pratul K Singh

    13. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    14. ICORE - 2010, Pragya Singh, Pratul K Singh

    15. Sliced into Nano-scale ICORE - 2010, Pragya Singh, Pratul K Singh

    16. ICORE - 2010, Pragya Singh, Pratul K Singh

    17. ICORE - 2010, Pragya Singh, Pratul K Singh

    18. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    19. No Lattice Mismatch. Flexibility to create heterostructures. Broad range of materials. Integration of compound semiconductor based optoelectronic devices with silicon based microelectronics. ICORE - 2010, Pragya Singh, Pratul K Singh Nanowires- Properties

    20. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    21. Recombination: Poor efficiency may be due to recombination within the bulk silicon element. Photon strikes the p-n junction in bulk silicon, Produces an electron-hole pair. Electron and hole must travel along the wire to produce current. ICORE - 2010, Pragya Singh, Pratul K Singh Silicon Nanowires- Properties

    22. Recombination: Tendency to recombine with other oppositely charged charge carrier Resulting in heat generation rather than electrical energy ICORE - 2010, Pragya Singh, Pratul K Singh

    23. Reduced Recombination in SiNW: Small diameters. SiNWs grown vertical, perpendicular to the surface of the substrate. Electrons strikes on the surface. Distance of hole/electron travel is minimized. Distance is of the order of nanometers. ICORE - 2010, Pragya Singh, Pratul K Singh

    24. Light Trapping: Light falling on the substrate gets reflected and once again gets absorbed by silicon nanowires. ICORE - 2010, Pragya Singh, Pratul K Singh

    25. Increased Surface Area: Very narrow pointed structures. Diameter in nanometers. Length in micrometers. Greater area made of p-n junctions is exposed to sunlight. Increases absorptivity. ICORE - 2010, Pragya Singh, Pratul K Singh

    26. ICORE - 2010, Pragya Singh, Pratul K Singh Silicon Nanowires- Properties

    27. Tiny PV Cells: Composed of 3 layers: Inner P region Intrinsic or pure silicon Outer N region ICORE - 2010, Pragya Singh, Pratul K Singh

    28. Photon strikes the outer shell Electron-hole pair is created Travels in the radial direction towards the P layer (core) before recombination. ICORE - 2010, Pragya Singh, Pratul K Singh

    29. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    30. Fabrication Catalyst Particles : The catalyst must be inert to the reaction products (during CVD nanowire growth). Gold Aluminum Tin Indium Gallium ICORE - 2010, Pragya Singh, Pratul K Singh

    31. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    32. Techniques for SiNW Deposition Techniques: Supercritical-Fluid-Based and Solution-Based Growth Techniques Molecular Beam Epitaxy Laser Ablation Silicon Monoxide Evaporation PECVD ICORE - 2010, Pragya Singh, Pratul K Singh

    33. Silicon Nanowire based Solar Cells ICORE - 2010, Pragya Singh, Pratul K Singh

    34. Experiment at the SSN Research Centre ICORE - 2010, Pragya Singh, Pratul K Singh

    35. Si-NW Growth Principle ICORE - 2010, Pragya Singh, Pratul K Singh

    36. Si-NW Deposition Process Steps ICORE - 2010, Pragya Singh, Pratul K Singh Silicon (4 inch) n-type Substrate Cleaned Chromium layer of 10.7nm deposited by EBE Method Gold Layer of 2.6nm deposited by EBE Method

    37. SiNW Deposition Experiment Catalyst Nano Particles: Gold Film Layer (2.6nm) Deposited on Silicon Substrate by EBE Heated at 580 degrees to form Nano Particles Figure1 SEM image of Nano particles of Gold ICORE - 2010, Pragya Singh, Pratul K Singh

    38. SiNW Deposition Experiment PECVD system. Temperature : 380 degrees Pressure in mTorr : 500mT Time of Deposition : 30 minutes Gases Used : Silane, Hydrogen and Argon ICORE - 2010, Pragya Singh, Pratul K Singh

    39. Si NW Comparison ICORE - 2010, Pragya Singh, Pratul K Singh

    40. Thank You ICORE - 2010, Pragya Singh, Pratul K Singh