Electroanalytical Chemistry

Electroanalytical Chemistry. Lecture #4 Why Electrons Transfer?. The Metal Electrode. E f = Fermi level; highest occupied electronic energy level in a metal. E F. E. E F. E redox. Why Electrons Transfer. Reduction. Oxidation. E redox. E. E. E F.

axel
Télécharger la présentation

Electroanalytical Chemistry

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Electroanalytical Chemistry Lecture #4 Why Electrons Transfer?

  2. The Metal Electrode • Ef = Fermi level; highest occupied electronic energy level in a metal EF E

  3. EF Eredox Why Electrons Transfer Reduction Oxidation Eredox E E EF • Net flow of electrons from M to solute • Ef more negative than Eredox • more cathodic • more reducing • Net flow of electrons from solute to M • Ef more positive than Eredox • more anodic • more oxidizing

  4. The Kinetics of Electron Transfer • Consider:O + ne- = R • Assume: • O and R are stable, soluble • Electrode of 3rd kind (i.e., inert) • no competing chemical reactions occur kR ko

  5. Equilibrium for this Reaction is Characterised by... • The Nernst equation:Ecell = E0 - (RT/nF) ln (cR*/co*) • where: cR*= [R] in bulk solution co*= [O] in bulk solution • So, Ecell is related directly to [O] and [R]

  6. Equilibrium (cont’d) • At equilibrium,no net current flows, i.e.,E = 0  i = 0 • However, there will be a dynamic equilibrium at electrode surface:O + ne- = RR - ne- = Oboth processes will occur at equal ratesso no net change in solution composition

  7. Current Density, I • Since i is dependent on area of electrode, we “normalize currents and examineI = i/A we call this current density • So at equilibrium, I = 0 = iA + iC ia/A = -ic/A = IA = -Ic = Iowhich we call the exchange current density • Note: by convention iA produces positive current

  8. Exchange Current Density • Significance? • Quantitative measure of amount of electron transfer activity at equilibrium • Io large  much simultaneous ox/red electron transfer (ET)  inherently fast ET (kinetics) • Io small  little simultaneous ox/red electron transfer (ET)  sluggish ET reaction (kinetics)

  9. Summary: Equilibrium • Position of equilibrium characterized electrochemically by 2 parameters: • Eeqbm - equilibrium potential, Eo • Io - exchange current density

  10. How Does I vary with E? • Let’s consider: • case 1: at equilibrium • case 2: at E more negative than Eeqbm • case 3: at E more positive than Eeqbm

  11. Case 1: At Equilibrium E = Eo - (RT/nF)ln(CR*/CO*)E - E0 = - (RT/nF)ln(CR*/CO*) E = Eo so, CR* = Co*I = IA + IC = 0 no net current flows IA O G R IC Reaction Coordinate

  12. Case 2: At E < Eeqbm • E - Eeqbm = negative number = - (RT/nF)ln(CR*/CO*)  ln(CR*/CO*) is positive CR* > CO* some O converted to R net reduction passage of net reduction current IA O G R IC I = IA + IC < 0 Reaction Coordinate

  13. Case 2: At E > Eeqbm • E - Eeqbm = positive number = - (RT/nF)ln(CR*/CO*)  ln(CR*/CO*) is negative CR* < CO* some R converted to O net oxidation passage of net oxidation current IA R G IC O I = IA + IC > 0 Reaction Coordinate

  14. Overpotential,  fast slow • Fast ET = current rises almost vertically • Slow ET = need to go to very positive/negative potentials to produce significant current • Cost is measured in overpotential,  = E - Eeqbm Cathodic Current, A  Eeqbm Edecomp Cathodic Potential, V

  15. Can We Eliminate ?What are the Sources of  •  = A + R + C • A, activationan inherently slow ET = rate determining step • R, resistancedue to finite conductivity in electrolyte solution or formation of insulating layer on electrode surface; use Luggin capillary • C, concentrationpolarization of electrode (short times, stirring)

  16. Reference Working Electrode Luggin Capillary Luggin Capillary • Reference electrode placed in glass capillary containing test solution • Narrow end placed close to working electrode • Exact position determined experimentally

  17. The Kinetics of ET • Let’s make 2 assumptions: • both ox/red reactions are first order • well-stirred solution (mass transport plays no role) • Then rate of reduction of O is: - kR co*where kR is electron transfer rate constant

  18. The Kinetics of ET (cont’d) • Then the cathodic current density is: • IC = -nF (kRCO*) • Experimentally, kR is found to have an exponential (Arrhenius) potential dependence:kR = kOC exp (- CnF E/RT) • where C = cathodic transfer coefficient (symmetry) • kOC = rate constant for ET at E=0 (eqbm)

  19. O G R Reaction Coordinate , Transfer Coefficient  - measure of symmetry of activation energy barrier  = 0.5  activated complex halfway between reagents/ products on reaction coordinate; typical case for ET at type III M electrode

  20. The Kinetics of ET (cont/d) Substituting: • IC = - nF (kR co*) = = - nF c0*kOC exp(- CnF E/RT) Since oxidation also occurring simultaneously: • rate of oxidation = kA cR* • IA = (nF)kACR*

  21. The Kinetics of ET (cont’d) • kA = kOA exp(+ AnF E/RT) • So, substitutingIA= nF CR*kOA exp(+AnF E/RT) • And, since I = IC + IA then: • I = -nF cO*kOC exp(- CnF E/RT) +nF cR*kOA exp(+ AnF E/RT)I = nF (-cO*kOC exp(- CnF E/RT) +cR*kOA exp(+ AnF E/RT))

  22. The Kinetics of ET (cont’d) • At equilibrium (E=Eeqbm), recallIo = IA = - IC • So, the exchange current density is given by:nF cO*kOC exp(- CnF Eeqbm/RT) =nF cR*kOA exp(+ AnF Eeqbm/RT) = I0

  23. The Kinetics of ET (cont’d) • We can further simplify this expression by introducing  (= E + Eeqbm): • I = nF [-cO*kOC exp(- CnF ( + Eeqbm)/RT) + cR*kOA exp(+ AnF ( + Eeqbm)/ RT)] • Recall that ea+b = eaeb • So,I = nF [-cO*kOC exp(- CnF /RT) exp(- CnF Eeqbm/RT) + cR*kOA exp(+ AnF / RT) exp(+ AnF Eeqbm/ RT)]

  24. The Kinetics of ET (cont’d) • So,I = nF [-cO*kOC exp(- CnF /RT) exp(- CnF Eeqbm/RT) + cR*kOA exp(+ AnF / RT) exp(+ AnF Eeqbm/ RT)] • And recall that IA = -IC = I0So,I = Io [-exp(- CnF /RT) + exp(+ AnF / RT)]This is the Butler-Volmer equation

  25. The Butler-Volmer Equation • I = Io [- exp(- CnF /RT) + exp(+ AnF / RT)] • This equation says that I is a function of: •  • I0 • C and A

  26. The Butler-Volmer Equation (cont’d) • For simple ET, C + A = 1 ie., C =1 - A • Substituting:I = Io [exp((A - 1)nF /RT) + exp(AnF / RT)]

  27. Let’s Consider 2 Limiting Cases of B-V Equation • 1. low overpotentials, < 10 mV • 2. high overpotentials,  > 52 mV

  28. Case 1: Low Overpotential • Here we can use a Taylor expansion to represent ex:ex = 1 + x + ... • Ignoring higher order terms:I = Io [1+ (A nF /RT)- 1 - (A- 1)nF / RT)] = Io nF/RT • I = Io nF/RT so total current density varies linearly with  near Eeqbm

  29. Case 1: Low Overpotential (cont’d) • I = (Io nF/RT)  intercept = 0slope = Io nF/RT • Note: F/RT = 38.92 V-1 at 25oC

  30. Case 2: High Overpotential • Let’s look at what happens as  becomes more negative then if IC >> IA • We can neglect IA term as rate of oxidation becomes negligible thenI = -IC = Io exp (-CnF /RT) • So, current density varies exponentially with 

  31. Case 2: High Overpotential (cont’d) • I = Io exp (-CnF /RT) • Taking ln of both sides:ln I = ln (-IC) = lnIo + (-CnF/RT) which has the form of equation of a line • We call this the cathodic Tafel equation • Note: same if  more positive thenln I = ln Io + A nF/RT  we call this the anodic Tafel equation

  32. Tafel Equations • Taken together the equations form the basis for experimental determination of • Io • c • A • We call plots of ln i vs.  are called Tafel plots • can calculate  from slope and Io from y-intercept

  33. Tafel Equations (cont’d) • Cathodic: ln I = lnIo + (-CnF/RT)  y = b + m x • If C = A = 0.5 (normal), for n= 1 at RT slope = (120 mV)-1

  34. Tafel Plots ln |i| High overpotential:ln I = lnIo + (AnF/RT)  Anodic Cathodic Low overpotential:I = (Io nF/RT)  ln Io Mass transport limited current _ Eeqbm + , V In real systems often see large negative deviations from linearity at high  due to mass transfer limitations

  35. EXAMPLE: • Can distinguish simultaneous vs. sequential ET using Tafel Plots • EX: Cu(II)/Cu in Na2SO4 • If Cu2+ + 2e- = Cu0 then slope = 1/60 mV • If Cu2+ + e- = Cu+ slow ?Cu+ + e- = Cu0 then slope = 1/120 mV • Reality: slope = 1/40 mVviewed as n = 1 + 0.5 = 1.5 • Interpreted as pre-equilibrium for 1st ETfollowed by 2nd ET

  36. Effect of  on Current Density • A = 0.75 oxidation is favored • C = 0.75 reduction is favored

  37. Homework: • Consider what how a Tafel plot changes as the value of the transfer coefficient changes.