1 / 41

Recent Development of Light-weighting Steels

Recent Development of Light-weighting Steels. Graduate Institute of Ferrous Technology Dong-Woo Suh. Contents. What is light-weighting steels? Brief review on related research activities Some results on prototype alloys Concluding remarks. Why light-weighting?. 0.2. 0.14.

ecrosby
Télécharger la présentation

Recent Development of Light-weighting Steels

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Recent Development of Light-weighting Steels Graduate Institute of Ferrous Technology Dong-Woo Suh

  2. Contents • What is light-weighting steels? • Brief review on related research activities • Some results on prototype alloys • Concluding remarks

  3. Why light-weighting? 0.2 0.14 CO2 emission (kg/km) 0.02 1,088 ~1,360 kg (over 75% of car weight)

  4. Evolution of automobile • Light-weighting materials • w/o loss of crashworthiness • More efficient combustion • engine Improvement of fuel efficiency • Hybrid vehicle • Fuel cell vehicle Development of alternative vehicles

  5. Needs for light-weighting in alternative vehicles battery system / motor / fuel cell / gas storage battery system / motor + 90~100kg + 250kg

  6. One way – Higher strength steels 1500

  7. Needs for another approach Double strength Half thickness? • Front structure • 500 ~ 800MPa  1500MPa • : 30% reduction in thickness considering • the structural stiffness (Toyota)

  8. lattice expansion lower atomic mass of substitutional atom ● Specific weight of Fe-Al alloy ■ Specific weight of Fe-14~28Mn-Al-C [Frommeyer] Basic concept of light-weighting steels (M. Shiga et al. J. Phy. Soc. J.) • Al : 26.98 g/mol • Fe: 55.85 g/mol

  9. Alloy developments • 3 main research activities • Steels with ferrite as major phase • Based on Fe-Al binary system with microalloying elements • TS 400~600MPa, T.EL 30~35% • Automotive application, corrosion resistance • Multiphase steels • Based on Fe-Mn-Al-C system with microalloying elements • TS 800~1200MPa, T.EL 30~60% • Automotive structural components, reinforcements • Steels with austenite as major phase • Based on Fe-Mn-Al-C system with larger amount of austenite stabilizer • TS 600~1500MPa, T.El < 60% • Automotive structural component, military armor plate

  10. Issues of Fe-Al ferritic alloys • Alloy design - Fe-Al binary phase diagram - Role of carbon and -carbide - Effect of microalloying elements • Phase transformation and properties - Process related microstructure evolutions - Formability and texture

  11. Binary Fe-Al equilibrium •  phase: - Limited domain due to Al ( stabilizer) - Disappear with addition of ~3 atomic % Al •  (A2) phase • - Solid solution of Fe and Al (disordered) • - Two transitions: k-state and magnetic • k-state • - Short range ordering • - Decreases the uniform and total elongation

  12. Workability and Al content Fe-13at.% Al Fe-17at.% Al (D.W. Suh, unpublished work)

  13. Ferritic light-weight steels

  14. Mechanical properties (low carbon) • Increase of strength • - solid solution hardening • Ductility loss • - short range ordering • - decrease of dislocation mobility • : absence of cell formation during • straining Fe-8.5%Al (G. Frommeyer et al., La Revue de Metall.)

  15. Mechanical properties (high carbon) B C D A (R.G. Baligidad et al., La Revue de Metall.) • Tensile strength ~1000MPa is achieved by hard 2nd phase • Effect of -carbide on ductility does not seems to be fully understood

  16. Development of Fe-Mn-Al-C steels • Fe-Mn-Al-C alloys ( in 60~80’s) • - replacement of Cr, Ni containing stainless steel • - Fe-34.4Mn-10.2Al-0.76C (corrosion / oxidation) • - TS ~730MPa, El ~70% • TWIP steel (from 90’s) • - Fe-18Mn-1.5Al-0.6C • Age hardenable Fe-Mn-Al-C alloys • - light-weighting steels • - TRIPLEX steel (18-28Mn, 9-12Al, 0.7-1.2C) • - austenite / -carbide / ferrite

  17. Deformation and work-hardening • Fe-(0~1)C-(10~30)Mn-(3~9)Al alloys 100mJ/m2 20mJ/m2 40mJ/m2 SFE TRIP TWIP S(M)BIP Mn Al C

  18. Effect of Mn content (G. Fromeyer et al., ISIJ Int.)

  19. Austenitic light-weighting steels • Alloys with 20-30%Mn, 8-10%Al, 0.8-1.2%C • - Above 850oC, supersaturated austenitic structure • - During isothermal aging in 350-700oC, -carbide • precipitation occurs to raise strength Aged at 823K for 180min. (Choo. et al., Acta Mater.)

  20. Light-weighting TRIPLEX steel • Fe-26Mn-11Al-1.2C • - austenite, ferrite and -carbide (G. Frommeyer et al., Steel Research)

  21. -carbide and cracking • (0.3~0.5)C-(5~6)Mn-(6.5~7.5)Al (S.Y. Shin et al., Met. & Mater. Trans.)

  22. Recent results on prototype alloys • 1st year results from project supported by government • Target properties • - 780MPa / 980MPa grade steels • - 10% density reduction • Fe-Mn-Al-C multi-phase steel • - to make the alloy with lean system • compared with reported alloys • - utilizing metastable austenite • - suppression of -carbide • in ferrite phase Underbody of battery-electric vehicle

  23. Fe-Mn-Al-C thermodynamic database 0.2C-7Mn-4Al (fM=0.73) 0.25C-7Mn-4Al (f M =0.82) large discrepancy

  24. Fe-Mn-Al-C thermodynamic database • Update thermodynamic database to improve reliability • (collaboration with B.J Lee, POSTECH)

  25. Austenite fraction control 0.12C-15Mn-7Al 0.2C-8Mn-7Al

  26. Fe-0.08C-6Mn-3Al TRIP steel 3.1Al (720oC))   3Al f=26.0% (D.W Suh et al., Met. & Mater. Trans.)

  27. Prototype alloys and processing soaking annealing for 2min. at 740oC, 780oC, 820oC hot-rolling 10oC/s 10oC/s cold-rolling (~75%)

  28. Density of the alloys

  29. Microstructure after cold-rolling 0.2C-8Mn-7Al 0.12C-15Mn-7Al

  30. Microstructure after annealing (820oC) 0.12C-15Mn-7Al 0.2C-8Mn-7Al

  31. Austenite fraction after annealing

  32. Properties of annealed sheets 0.2C-8Mn-7Al 0.12C-15Mn-7Al

  33. TRIP effect from metastable austenite?

  34. Change of austenite fraction • Austenite is too stable to expect strain-induced martensite formation • Alloy design considering partitioning of alloying elements are required

  35. Concluding remarks • Light-weighting steels • - alternatives for mass reduction • - potent material for future vehicles application • Three main research activities • - Fe-Al based ferritic alloys • - Fe-Mn-Al-C based multiphase alloys • - Fe-Mn-Al-C based austenitic alloys • Challenges • - Thermodynamic approaches • - Understandings on microstructure-property control • - Difficulties on production (casting and rolling)

  36. Properties of annealed sheets

  37. Fe-Al binary phase diagram

  38. Mechanical properties (low carbon) (G.Frommeyer et al., La Revue de Metall.) • Lower carbon(~0.03%) content because C decreases ductility owing to • carbide precipitates Fe3AlC, -carbide • Utilizing microalloying elements to avoid -carbide formation

  39. Microstructure constituents in light-weighting steel Matrix Ferrite+Aus. Austenite +Fer. (+) Ferrite Stable  Metastable  TRIP type TRIPLEX type Duplex type ELC type

  40. Precipitation of (Fe,Mn)3AlC (Fe,Mn) Al perovskite E21 metastable L12 Chemical modulation : austenite <100> (C and Al) spinodal decomposition