CD4MCu PUMP PROGRAM APPLICATIONS

. 2. . CD4MCu. DUPLEX SS (TWO PHASE METALLURGY WHERE 316 IS ONLY ONE)300 SERIES FOR CORROSION RESISTANCE 400 SERIES FOR STRENGTH AND HARDNESSCORROSION RESISTANCE EQUAL TO OR BETTER THAN 316SSDOUBLE THE YIELD STRENGTH OF 316SSEXCELLENT RESISTANCE TO ABRASION AND EROSION. . . 3. . CD4MCu. EXCELLE

elom
Télécharger la présentation

CD4MCu PUMP PROGRAM APPLICATIONS

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

    1. CD4MCu PUMP PROGRAM APPLICATIONS

    2. CD4MCu DUPLEX SS (TWO PHASE METALLURGY WHERE 316 IS ONLY ONE) 300 SERIES FOR CORROSION RESISTANCE 400 SERIES FOR STRENGTH AND HARDNESS CORROSION RESISTANCE EQUAL TO OR BETTER THAN 316SS DOUBLE THE YIELD STRENGTH OF 316SS EXCELLENT RESISTANCE TO ABRASION AND EROSION

    3. CD4MCu EXCELLENT RESISTANCE TO: PITTING AND CREVICE CORROSION STRESS CORROSION CRACKING IN CHLORIDE CONTAINING SOLUTIONS OR VAPORS SODIUM CHLORIDE - BRINE CALCIUM CHLORIDE METHYLENE CHLORIDE SEA WATER

    4. CD4 APPLICATIONS BLACK LIQUOR IN PAPER MILLS WOOD DIGESTION SATURATED SOLN. SODIUM SULFATE AND SODIUM CARBONATE CORROSIVE BLEACHES AND DYES FERTILIZER PRODUCTION PHOSPHATE AND PHOSPHORIC ACID

    5. CD4 APPLICATIONS..cont. FATTY ACIDS WITH SOLIDS LIME SLURRIES NITRIC ACID LESS THAN 1 MM/YR CORROSION FOR ALL CONCENTRATIONS: UNDER 200 OF LESS THAN 60% CONCENTRATION

    6. CD4 APPLICATIONS SULFURIC ACID 0-20 % CONCENTRATION AT 140-160 OF 0-10 % CONCENTRATION AT 185 OF TITANIUM DIOXIDE PLUS SULFURIC ACID TITANIUM SULFATE

    7. CD4 IN SYSTEM ONE PUMPS CAVITATION CORROSION OCCURS WHEN LOW NPSH ALLOWS THE FORMATION OF VAPOR BUBBLES ON THE IMPELLER EXPLOSIVE FORCE OF BUBBLES RUPTURING: REMOVE PROTECTIVE FILM OF SS LEADING TO CORROSION CAN REMOVE SMALL AMOUNTS OF METAL SYSTEM ONE PUMPS USE CD4 IMPELLERS TO WITHSTAND THE FORCES OF CAVITATION CORROSION AND EROSION GREATER HARDNESS, STRENGTH AND CORROSION RESISTANCE

    8. CD4 IN SYSTEM ONE PUMPS..cont. CD4 BACKCOVERS AND CASINGS ARE AVAILABLE FOR EROSION AND ABRASION APPLICATIONS THE FACTORY WILL STOCK THE FRAME A 10 AND 13 IMPELLER SIZE WET ENDS PRICE IS GREATER DUE TO HIGHER CASTING COST AND SMALLER MACHINING QUANTITIES