Electron poor materials research group

Electron poor materials research group. Group meeting Sept. 30, 2010 Theory-FCC Zinc-Blende Equations of State. Procedure. 20 Volume cycles each volume cycle contains 3 VASP runs 2 relaxation runs (back to back) and then a static run to get accurate energy values

jackie
Télécharger la présentation

Electron poor materials research group

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Electron poor materials research group Group meeting Sept. 30, 2010 Theory-FCC Zinc-Blende Equations of State

  2. Procedure • 20 Volume cycles • each volume cycle contains 3 VASP runs • 2 relaxation runs (back to back) and then a static run to get accurate energy values • all 20 cycles take from 3-6 minutes • Values for the minimum volume V0, bulk modulus K0, minimum energy E0, and derivative of the bulk modulus K0p are then calculated from a 3rd order Birch-Murnaghan fit to the 20 volume and free energy points obtained from the 20 Volume cycles.

  3. INCAR_relax System = InSb NSW = 5 | number of ionic steps ISIF = 4 | ISIF=4 relax cellshape and ions. NOT volume IBRION = 1 | ionic relaxation algorithm EDIFF = 1E-4 | break condition for elec. SCF loop EDIFFG = -1E-3 | break condition for ionic relaxation loop MAXMIX = 80 | keep dielectric function between ionic movements NELMIN = 8 | minimum number of electronic steps NFREE = 15 | number of degrees of freedom (don't go above 20) #RECOMMENDED MINIMUM SETUP GGA=CA #xchange-correlation VOSKOWN=0 #=1 if GGA=91; else = 0 PREC = NORMAL #PRECISION, sets fft grid ENCUT = 150 #energy cutoff, commented to use enmax in potcar LREAL = .FALSE. #.FALSE. MEANS USE RECIPROCAL LATTICE ISMEAR = 0 #0 means use gaussian smearing

  4. INCAR_static System = InSb #ISTART = 0 # startjob: no WAVECAR file #ICHARGE = 2 # charge: from atoms #INIWAV = 1 # random initialization for wf. NELM = 40 # maximum of 40 electronic steps NELMIN = 2 # minimum of 2 steps NELMDL = -5 # no update of charge for 3 steps EDIFF = 1E-4 # accuracy for electronic minimization #RECOMMENDED MINIMUM SETUP GGA=CA #xchange-correlation VOSKOWN=0 #=1 if GGA=91; else = 0 PREC = NORMAL #PRECISION, sets fft grid ENCUT = 150 #energy cutoff, commented to use enmax in potcar LREAL = .FALSE. #.FALSE. MEANS USE RECIPROCAL LATTICE ISMEAR = -5 #-5 means use tetrahedral with blochl

  5. InSb Experimental Volume: 67.97

  6. GaSb Experimental Volume: 56.63

  7. ZnTe Experimental Volume: 56.83

  8. ZnSe Experimental Volume: 45.98