YBCO: CC in Pancake Coils (Am. Superconductor. ASC'04 ( J e 200 A/mm² at 24 T, 0.1 µm/cm). YBCO: /Ni/YSZ ~1 µm thick µ-bridge, H||c 4 K,. 100,000. Foltyn et al. (LANL) '96. YBCO microbridge H. ||. c. 4. 2. K. YBCO CC H. ||. c. 4. 2. K.
E N D
YBCO: CC in Pancake Coils (Am. Superconductor ASC'04 (Je 200 A/mm² at 24 T, 0.1 µm/cm) YBCO: /Ni/YSZ ~1 µm thick µ-bridge, H||c 4 K, 100,000 Foltyn et al. (LANL) '96 YBCO microbridge H || c 4 . 2 K YBCO CC H || c 4 . 2 K YBCO: /Ni/YSZ ~1 µm thick µ-bridge, H||ab 75 K, Foltyn et al. (LANL) '96 Nb-Ti: Example of Best Industrial Scale Heat Treated Composites ~1990 (compilation) Nb-Ti: Nb-47wt%Ti, 1.8 K, Lee, Naus and Larbalestier NbTi YBCO microbridge H || ab 75 K 10,000 Nb Al: ITER 3 UW-ASC'96 ² Nb3Sn: Bronze route int. stab. -VAC-HP, non-(Cu+Ta) mm Jc, Thoener et al., Erice '96. / A 2212 round wire , Nb3Sn: Non-Cu Jc Internal Sn OI-ST RRP #6555-A, 0.8 mm, LTSW 2002 Nb Sn Internal Sn Nb3Sn: Non-Cu Jc Internal Sn OI-ST RRP 1.3 mm, 3 1,000 ASC'02/ICMC'03 2223 Nb3Sn: 1.8 K Non-Cu Jc Internal Sn OI-ST RRP Critical Current Density tape B|_ 1.8 K 1.3 mm, ASC'02/ICMC'03 Nb3Al: JAERI strand for ITER TF coil 2223 tape B|| Bi-2212: non-Ag Jc, 427 fil. round wire, Ag/SC=3 Nb Sn 100 (Hasegawa ASC-2000/MT17-2001) 3 ITER Bi 2223: Rolled 85 Fil. Tape (AmSC) B||, UW'6/96 1.8 K Bronze MgB 2 Nb-Ti Bi 2223: Rolled 85 Fil. Tape (AmSC) B|_, UW'6/96 10 0 5 10 15 20 25 30 Applied Field, T MgB2: 10%-wt SiC doped (Dou et al APL 2002, UW measurements)