Ti TA NIUM + Ni CKEL (1 + 1 mm)

X EPNM – Bechichi 2010. Ti TA NIUM + Ni CKEL (1 + 1 mm). Ti. Ni. +. EXPOSED TO THERMAL PROCESS LOADS. TASKS. According to ISO 9001 standard WORK IN WAY TO SATISFY THE CUSTOMER. Base tasks :. Additonally can be:. Assure high quality of product.

lane
Télécharger la présentation

Ti TA NIUM + Ni CKEL (1 + 1 mm)

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. X EPNM – Bechichi 2010 TiTANIUM+ NiCKEL(1 + 1 mm) Ti Ni + EXPOSED TO THERMAL PROCESS LOADS Authors: Mariusz Prażmowski, Robert Bański, Zygmunt Szulc, Aleksander Gałka, Sebastian Kokot.

  2. TASKS According to ISO 9001 standard WORK IN WAY TO SATISFYTHECUSTOMER Basetasks: Additonallycan be: • Assure high quality of product • Recognize conditions of element exploitation • Check its influence for element’s durability • Offer acceptable price • Eventually correct technologicalparameters of manufacturing • Informthecustomeraboutresults of tests and examinations • Works and deliveries make in agreed time X EPNM – Bechichi 2010

  3. Application of Ti+Ni (1+1) mm Chlorineelectrolysis Membaraneelectrolyser Separate modul Bimetallic disc Ti + Ni Elektrolizer Bimetallic disc Ti + Ni Cathode(Ni) Detail of using X EPNM – Bechichi 2010 Anode (Ti)

  4. Identification of tasks Choose of parameters of cladding set • In high simply set – efect – bad bond Ni 201 Ti Gr.1 • Important changes in cladding set – getting improvement of bond Ni 201 Ti Gr.1 X EPNM – Bechichi 2010

  5. Identification of tasks Choose of optimal format of set • Preliminary set had sizes:1220 x 2000 mm. • Basis on costs analysis / problems such as: • Assembly in conditions of open area • Flatness of elements – Ti and Ni plates in delivery to cladding • Costs of straightening after cladding • In agreement with customer finally agreed sizes: 490 to 500 x 1250 mm X EPNM – Bechichi 2010

  6. Identification of tasks Choose of thermal loading to testing • (A) Simulation of loading connected with heating of element in process of jointing of cathode part – Nickiel with anode part – Titanium; possible methods • Resistance welding or microplasma welding or laser welding or electron beam welding Adoptedthatproper to modelling of loading will be heattreatment 610C / 1 h • (B) Simmulation of cladding process and regeneration active layers on anode (titanium). Adoptedthatproper to modelling of loading will be cycledheattreatment: 12 cycles – as on graph • Sample was heating during 5 minutes to temperature 480C, holding through 10 minutes, and next cooling through 20 minutes to room temperature (20C), in which was holding during 10 minutes. For each samples cycle of loading was repeated 12 times. X EPNM – Bechichi 2010

  7. Initiation point Identification of tasks Choose of thermal loading to testing - continuation • (C) Made heat treatment basis on heating of samples in temperature 500C in time 13 h • (D) Additionally – made heat treatment basis on joints (A) + (C), {610/1h} + 500C / 13h} • Samples to heat treatment were taking from productive element as below • Heat treatments were done in LAC furnace, model LMH 04/12 X EPNM – Bechichi 2010

  8. Tests and examinations MICROSTRUCTURALEXAMINATIONS • Conditions at the begining – without HT – test piece no. 1; a) x 200, b) x 500 • After HT 610C / 1 h – test piece no. 2; a) x 200, b) x 500, c) x 750 X EPNM – Bechichi 2010

  9. Tests and examinations MICROSTRUCTURALEXAMINATIONS • After HT 500C / 13 h; test piece no. 3; a) x 200, b) x 500, c) x 750 • After HT 610C / 1 h + 500C / 13 h; test piece no. 3; a) x 200, b) x 500, X EPNM – Bechichi 2010

  10. Tests and examinations HARDNESSEXAMINATIONS HV0,1 • TABLE OF RESULTS • Test piece no. 1 • Test piece no. 2 X EPNM – Bechichi 2010

  11. Tests and examinations HARDNESSEXAMINATIONS HV0,1 • GRAPH Ti Gr.1 Nickel Gr. 201 X EPNM – Bechichi 2010

  12. Tests and examinations TECHNOLOGICAL TEST • Shear test • For production are making 4 tests for batch of 50 pcs. X EPNM – Bechichi 2010

  13. Tests and examinations TECHNOLOGICALTESTS • Examples of results X EPNM – Bechichi 2010

  14. xplomet xplomet xplomet CONCLUSIONS • Examinations had strictly applicable character. • Any of heat treatment refer to conditions of manufacturing and exploitation of Ti + Ni has no negative influence for durability of bond. • Good made bond Ti+Ni cannot be broken by thermal loading on level of manufacturing techniques. • In aim to avoid any questions to speaker of this presentation, he let himself to make a question, for patienced and for sure borred audience – WHO WROTE THESE WORDS ? For 'tis the sport to have the enginerHoist with his own petard, an't shall go hardBut I will delve one yard below their minesAnd blow them at the moon. • THANKYOU FOR ATTENTION X EPNM – Bechichi 2010

  15. THANKYOU FOR ATTENTION In presentationhavebeenused materials of INEOS Chlor Ltd. and MScworks of students: K. Niezgoda & P. Szymlak