Lectures co-financed by the European Union in scope of the European Social Fund

Ionic Conductors: Characterisation of Defect Structure Lectures 9-10 Fast ion conduction in solids II amorphous materials Dr. I. Abrahams Queen Mary University of London. Lectures co-financed by the European Union in scope of the European Social Fund. Oxide Glasses.

lillian-osborne
Télécharger la présentation

Lectures co-financed by the European Union in scope of the European Social Fund

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Ionic Conductors: Characterisation of Defect Structure Lectures 9-10 Fast ion conduction in solids IIamorphous materialsDr. I. AbrahamsQueen Mary University of London Lectures co-financed by the European Union in scope of the European Social Fund

  2. Oxide Glasses Glasses are typically made up of polymeric frameworks which show no long-range order. In inorganic oxide based glasses the framework typically consists of corner sharing MO4 tetrahedra or MO3 trigonal planes . Three types of oxides are of interest in glass chemistry: (1) Network Formers Oxides that readily form glasses when quenched from high temperatures, e.g. SiO2, P2O5, B2O3 etc. (2) Network Modifiers Oxides that that can be mixed with network formers to yield glasses. They are typically ionic and act by disrupting the network., e.g. Li2O, Na2O, CaO etc. (3) Network Intermediates These oxide do not form glasses on their own, but when mixed with glass formers may either act as network formers or network modifiers, e.g. Al2O3, SnO2, TiO2 etc. Lectures co-financed by the European Union in scope of the European Social Fund

  3. Glass formation Glasses are typically formed by rapid cooling of melts and are thus governed by kinetics, through the control of the cooling rate. In theory, every inorganic material, within a certain compositional range, can be transformed into a glass, if extreme conditions of synthesis are available If the liquid cooling rate is sufficiently high, then instead of crystallisation, the undercooled liquid is transformed into a supercooled state. This state of the liquid is thermodynamically metastable, as it possess a higher internal energy than the corresponding crystalline state. Lectures co-financed by the European Union in scope of the European Social Fund

  4. A plot of entropy vs temperature leads to the conclusion that a glass, at 0K, would have a finite amount of entropy known as the zero-point entropy. This is regarded as frozen-in configurational entropy. The described behaviour would be changed if the supercooled liquid were cooled extremely slowly. In this case, the entropy of the supercooled liquid would follow the dashed line and would be zero at a positive temperature, T0. Lectures co-financed by the European Union in scope of the European Social Fund

  5. As a consequence, further cooling would result in a negative entropy of the glass at 0 K. Obviously, according to the third law of thermodynamics this hypothetical behaviour is impossible and is known as the Kauzmann paradox. This has been explained by considering that below T0 vibrational entropy would still remain and this would be reduced to zero at 0 K in accordance with the third law. The major consequence of this is that glasses cannot be formed below T0 (the Kauzmann temperature) and hence this temperature can be identified as the ideal glass transition temperature. Lectures co-financed by the European Union in scope of the European Social Fund

  6. Thus glasses have a higher free energy than the corresponding crystal and are considered metastable. Lectures co-financed by the European Union in scope of the European Social Fund

  7. Thermal Analysis of Glasses When a glass is heated it exhibits characteristic thermal events, Tg the glass transition temperature, Tc the crystallisation temperature and Tm the melting temperature. Lectures co-financed by the European Union in scope of the European Social Fund

  8. DTA trace of 56Li2O:2ZrO2:40 P2O5 Lectures co-financed by the European Union in scope of the European Social Fund

  9. Cation Conducting Glass Electrolytes • When oxides such as Li2O or Ag2O are used as a network modifiers, the M+ ions are potentially mobile and can hop between available sites in the glass. • Advantages over crystalline electrolytes: • While crystalline conductors show anisotropic conduction properties, in glasses conduction is isotropic. • When used as real materials, crystalline electrolytes suffer from grain boundary resistances which reduce their overall conductivity. In monolithic glasses there are no grain boundaries. • Crystalline solid electrolytes generally have well defined composition ranges. In glasses it is possible synthesize glasses with wide ranging compositions and hence tailor specific properties such as conductivity, air sensitivity and thermal stability. Lectures co-financed by the European Union in scope of the European Social Fund

  10. Monolithic Glass Batteries Glass Electrodes Substitution of the network forming oxide by suitable transition metal oxides allows for the introduction of electronic conduction into the system. This means that glasses can be synthesized which show conductivities varying from pure ionic to pure electronic. This could allow for the construction of a monolithic glass battery with anode, cathode and electrolyte regions. Lectures co-financed by the European Union in scope of the European Social Fund

  11. In such a system is that the network extends throughout the glass monolith and components are air stable. • Advantages: • Problems associated with electrode/electrolyte interface are diminished, while grain boundary resistances are removed altogether. • Cheap construction • Potentially miniaturisable therefore suitable for miniature power supplies e.g. on board and on chip power sources. Lectures co-financed by the European Union in scope of the European Social Fund

  12. Ionic Conduction in Glasses There is no single theory of ion transport in glasses to explain high ionic conductivity. The three most important models are: (1) The strong electrolyte model (Anderson-Stuart) This is based on the assumption that effective carrier density Ni is independent of ion concentration and temperature and thus ithe mobility, of these species is a quantity that depends on both parameters, (ion concentration and temperature). (2) The weak-electrolyte model According to this model iis independent of ion concentration and is weakly dependent on temperature, while Ni depends on both parameters. (3) The defect model This is based on the same principles as those identified in crystalline ion conductors. Lectures co-financed by the European Union in scope of the European Social Fund

  13. According to the strong electrolyte model a cation hops from an occupied site near a non-bridging oxygen (NBO) to a vacant site which is close to another NBO. In doing this, the conducting ion has to overcome the energy barrier generated by the bridging oxygen (BO). At first the mobile ion needs to remove itself from association with NBO (binding energy, Eb,). The energy that is associated with long range motion, is strain energy, ES. Thus, the total activation energy for this process is given as a sum of these energies. (a) strong-electrolyte model and (b) weak- electrolyte model Lectures co-financed by the European Union in scope of the European Social Fund

  14. After necessary approximations this equation can be written as Where, zo and ro are the charge and radius of the O2- ion, respectively,  is a non-periodic lattice parameter determined by the distance between neighbouring sites, r is the cation radius rD is the bottleneck radius in the glass, G is the elastic modulus and  is a covalency parameter. The weak electrolyte model assumes the existence of two sites and that the conduction process is dominated by the ions, which are thermally brought to higher energy sites. Lectures co-financed by the European Union in scope of the European Social Fund

  15. Structural Characterisation of Glasses Because there is no long range order, the structure of glasses are not easily accessible using standard characterisation techniques such as X-ray diffraction. Other techniques such as NMR, IR, EXAFS and neutron scattering, can be employed to probe the local structure. Most of these techniques are also suitable for crystalline materials where diffraction methods can give a clear picture of the structure. Therefore it is possible to compare results from the glasses with crystalline compounds of similar composition in order to yield the structure of the glass. The preferred coordination environments of ions in oxides will be the same whether in glass or crystalline forms. Lectures co-financed by the European Union in scope of the European Social Fund

  16. Glass Structure Glass forming oxides typically adopt tetrahedral or trigonal planar coordination environments. These can be classified according to the Qn nomenclature. Where n represents the number of bridging oxygens. Lectures co-financed by the European Union in scope of the European Social Fund

  17. Solid State NMR NMR is a nucleus specific technique that can yield important information on local structure. Atomic nuclei are made up of protons and neutrons (except 1H). The nuclear spin results from the coupling of these nucleons and is characterised by the spin quantum number I Ican have integral, half integral or zero values. Nuclei with an odd mass number have half-integral spins e.g.1H I = 1/2, 7Li I= 3/2 Nuclei with an even mass number and even charge number have zero spin e.g. 12C and 16O I = 0 Nuclei with an even mass number, but with an odd charge number have integral spins, e.g. 14N and 6Li I =1 Lectures co-financed by the European Union in scope of the European Social Fund

  18. The motion of charged particles has an associated magnetic field. If a nucleus possesses angular momentum then there is an associated magnetic moment . Let us represent the magnetic moment by a vector Applied field Parallel or antiparallel to applied field direction No Applied field Random orientation Lectures co-financed by the European Union in scope of the European Social Fund

  19. In an applied field the energy of the nucleus is dependent on the magnetic quantum numbermI mI = -1/2 mI = 1/2 Energy This interaction of the magnetic moment with the applied static magnetic field is known as the Zeeman interaction. Lectures co-financed by the European Union in scope of the European Social Fund

  20. In order to obtain an NMR spectrum we need to excite nuclei. This is achieved using a radio frequency pulse. rf Energy The resulting NMR spectrum shows an absorption of the rf frequency. The resonance frequency is proportional to the strength of the applied field. Lectures co-financed by the European Union in scope of the European Social Fund

  21. Chemical shift One of the most important features of NMR is the chemical shift. This is caused by nuclei with differing degrees of shielding. This means that they absorb at different applied field strengths. Electrons surrounding each nucleus interact with the magnetic field causing a circulation of the electronic charge around the nucleus. This results in a secondary magnetic field at the nucleus that is opposed to the applied field. Thus the circulating electrons shield the nucleus from the full extent of the applied field. Lectures co-financed by the European Union in scope of the European Social Fund

  22. Electron withdrawal causes a de-shielding effect, while electron donation causes a shielding effect. The degree of shielding is dictated by the chemical environment, i.e. the neighbouring atoms/ions and the nature of the bonding. The resulting chemical shift of the resonance is therefore characteristic of particular chemical environments. Chemical shifts are recorded with respect to a standard reference Chemical shift ( ppm) = (observed resonance frequency – resonance frequency of standard) ____________________________________________________ operating frequency Lectures co-financed by the European Union in scope of the European Social Fund

  23. Dipolar interactions between spins can occur. In the case of interaction between like spins, for a single nucleus the spectrum would consist of two lines with peak separation given by: Where  is the gyromagnetic ratio for a particular nucleus  is the angle between the internuclear vector and the magnetic field r is the distance between nuclei. A similar equation can be written for interactions between unlike spins. Lectures co-financed by the European Union in scope of the European Social Fund

  24. This interaction occurs between a nucleus and all of its neighbours. In addition in a randomly orientated polycrystalline solid this interaction is averaged over all values of . This leads to severe broadening of spectra compared to solution state NMR. The peculiar line shape of solid state spectra is due to directionally dependent differences in shielding. This is known as chemical shift anisotropy. Lectures co-financed by the European Union in scope of the European Social Fund

  25. The solid state line shape can be described by the chemical shift tensor which has three principal components which are ordered according to the Haeberlen convention |d33-diso| > |d11-diso| > |d22-diso| Isotropic Chemical Shift diso = (d11 + d22 + d33)/3 Chemical Shift Anisotropy Dd = d33 - (d11 + d22)/2 Asymmetry h = (d22 - d11)/(d33 - diso) Lectures co-financed by the European Union in scope of the European Social Fund

  26. In order to narrow the line width and minimise the effects of chemical shift anisotropy, the sample can be spun in the magnet. If the spinning sample is orientated at the so called magic angle of 54 44’ to the applied field then the term (1- 3cos2) = 0 and the spectrum simplifies. In order to reduce the spectrum to a single line, the sample must be spun at frequency greater than or equal to the spread of frequency corresponding to the anisotropy. At lower spinning speeds the spectrum appears as a central isotropic peak flanked by spinning sidebands. Lectures co-financed by the European Union in scope of the European Social Fund

  27. 31P NMR spectra of lithium aluminium titanium phosphate (LATP) glasses Q1Li Q1Ti/Al Q2 Lectures co-financed by the European Union in scope of the European Social Fund

  28. Derived NMR parameters for 31P spectrum of LTP glass. Lectures co-financed by the European Union in scope of the European Social Fund

  29. The area of each peak (and its associated spinning sidebands) is proportional to the number of phosphate atoms in a particular environment. This means that the spectrum contains quantitative information. By taking the ratios of the different phosphate species present and with a knowledge of the composition of the glass it is possible to calculate how much oxygen is not associated with the phosphate network and therefore bonded exclusively to Ti. Since the number of Q1Ti species is known we can also calculate the number of phosphate groups that are linked to Ti (i.e. coordination number). Hence it is possible from this simple 1-dimensional spectrum to derive a structural formula for LTP glass. Lectures co-financed by the European Union in scope of the European Social Fund

  30. Structure of LTP glass Ions Network Li+10Ti4+0.17(TiOO4/2)2-0.83 (PO2O2/2)-6.98(PO3O1/2)2-1.03 5-CN Ti Q2 P Q1 P Lectures co-financed by the European Union in scope of the European Social Fund

  31. 27Al NMR spectra of LATP glasses [Al(OP)6] [Al(OP)5] [Al(OP)4] Lectures co-financed by the European Union in scope of the European Social Fund

  32. Compositional Variation of Al species in LATP glasses Lectures co-financed by the European Union in scope of the European Social Fund

  33. Electrode Glasses Electrode glasses, show mixed ionic/electronic conduction. e.g. in lithium manganese phosphate the Mn2+ ion is strongly paramagnetic causing severe line broadening in NMR. However at low concentrations it is possible to obtain spectra. LMnP (60-x)Li2O : (10-x)MnO: 40P2O5 Lectures co-financed by the European Union in scope of the European Social Fund

  34. At x = 5, both Q1 and Q2 groups are visible in the 31P spectrum At x = 10, both sites are still visible. However the relative intensity of the Q1 resonance is greatly reduced. This suggests that Mn2+ is preferentially located near Q1 sites. Lectures co-financed by the European Union in scope of the European Social Fund

  35. Trends in isotropic chemical shift (iso) Trends in (iso) with composition can yield important structural information. For example in the glass system (0.55-x)Na2O: xSrO:0.45P2O5 (0 x 0.55) The glass network is a mixture of Q1 and Q2 phosphate groups R. Pires, I. Abrahams, T.G. Nunes and G.E. Hawkes, J. Non-Cryst. Solids. 337, 2004, 1. Lectures co-financed by the European Union in scope of the European Social Fund

  36. The trend observed iso, appears to indicate a preferential substitution of Na+ ions by Sr2+ associated with the Q1 phosphate species and subsequent substitution of the Q2 associated cations. This suggests that the distribution of cations is non-random. At the critical composition (x  0.20) Sr2+ is predominantly associated with Q1 phosphate groups, while Na+ is predominantly associated with Q2. Lectures co-financed by the European Union in scope of the European Social Fund

  37. EXAFS Extended X-ray Absorption Fine Structure (EXAFS) is a useful technique for examining the local environment around an atom. It is element specific and so is useful for distinguishing different species in mixed systems. It is useful in both crystalline and amorphous solids. The EXAFS phenomenon is weak and requires a high intensity X-ray beam as obtained at a synchrotron source. If a sample is irradiated with X-rays of a small range of energies then when the energy of an X-ray matches the binding energy of a core electron in a specific element, absorption occurs and the electron is either promoted to a higher energy level or ejected. By measuring the X-ray absorption coefficient  as a function of photon energy an X-ray absorption spectrum is obtained.resulting transmitted (or reflected) intensity an X-ray absorption spectrum is obtained. where Im is the measured intensity (transmitted) and I0 is the incident intensity. Lectures co-financed by the European Union in scope of the European Social Fund

  38. The region just before and after the edge is known as the X-ray Absorption Near Edge Structure. While the EXAFS is present as small post edge oscillations. Lectures co-financed by the European Union in scope of the European Social Fund

  39. The XANES region can be analysed for information on the oxidation state of metals. Structural information is obtained from the EXAFS part of the spectrum which is typically in the rage 400 to 1000 eV above the absorption edge. The energy in this range is much higher than the binding energy of the electron and so the excited electron has a high kinetic energy and is ejected. On leaving the atom the electron wave undergoes interference with electrons in neighbouring atoms. The resulting constructive and destructive interference gives rise to oscillations in the absorption cross section  seen in the EXFAS region of the XAS spectrum. The outgoing electron wave will be backscattered by its neighbours. Therefore the pattern is a complex mixture of scattered and backscattered waves. Lectures co-financed by the European Union in scope of the European Social Fund

  40. The energy data (E) in eV are usually transformed to wave vector to wave vector k for analysis. where E0 is the absorption edge energy, me is the mass of an electron and  is h/2. The amplitude of each EXAFS wave depends on the number of surrounding atoms and their backscattering power (i.e. their atomic number) and the distance between the excited atom and the backscattering atom. One can define the total EXAFS spectrum (k) as the sum of individual EXAFS contributions in a multi-component system. Lectures co-financed by the European Union in scope of the European Social Fund

  41. i(k) can be defined as: Where Ns is the number of backscattering atoms at distance Ras from the absorbing atom, As is the backscattering strength of the backscattering atom, S0 is a passive electron reduction factor in the interaction,  2 is the Debye-Waller factor, is the mean free path of the electron and as is the phase shift of the wave. Analysis of the EXAFS spectrum yields Ns, Ras and 2as There are a number of theoretical approaches to modelling EXAFS data. We will not discuss these here. Lectures co-financed by the European Union in scope of the European Social Fund

  42. NaCaP3O9 glass Na spectrum R1 = 2.317(7) Å 22 = 0.034(2) Å2 N1 = 6 R2 = 3.16(8) Å 22 = 0.07(2) Å2 N2 = 6 Lectures co-financed by the European Union in scope of the European Social Fund

  43. Diffraction by glasses In diffraction experiments amorphous materials show no Bragg peaks, but they do exhibit scattering that can be analysed. For analysis of glass diffraction data we transform the data to Q space where:  = Bragg angle,  = wavelength and d = d-spacing. Lectures co-financed by the European Union in scope of the European Social Fund

  44. In order to get good radial distribution function data. the range of Q should be large. Typically neutron data allows Q ranges up to ca. 50 Å-1 while in X-ray data the maximum useable Q value is close to 20 Å-1 For laboratory X-ray data, Cu tubes have maximum Q value around 8 Å-1. Ag tubes increase the Q-max to ca. 20 Å-1 Synchrotron radiation is commonly used for X-ray experiments. The total interference function F(Q) is given by Where c represents the fraction of a chemical species, is the mean scattering length and S is the partial structure factor. The total pair correlation function G(r) is obtained by Fourier transfor of F(Q), while individual pair correlations gi,j(r) are obtained by Fourier transform of the partial structure factors. Lectures co-financed by the European Union in scope of the European Social Fund

  45. Neutron diffraction correlation functions for lithium borate glasses Swenson et al. Phys Rev. B. 52 (1995) 9310 For more detail see Lecture 15 January lectures. Lectures co-financed by the European Union in scope of the European Social Fund